RESUMO
OBJECTIVE: This study aimed to evaluate the effect of ultrasonic cleaning of the intracanal post space on the bond strength of fiber posts in oval canals filled with a premixed bioceramic (Bio-C Sealer [BIOC]) root canal sealer. MATERIALS AND METHODS: Fifty premolars were endodontically prepared and divided into 5 groups (n = 10), based on the type of root canal filling material used and the post space cleaning protocol. A1: gutta-percha + AH Plus (AHP) and post space preparation with ultrasonic cleaning, A2: gutta-percha + BIOC and post space preparation with ultrasonic cleaning, B1: gutta-percha + AHP and post space preparation, B2: gutta-percha + BIOC and post space preparation, C: control group. Fiber posts were cemented with a self-adhesive luting material, and 1 mm thick slices were sectioned from the middle and cervical third to evaluate the remaining filling material microscopically. The samples were subjected to a push-out test to analyze the bond strength of the fiber post, and the results were analyzed with the Shapiro-Wilk, Bonferroni, Kruskal-Wallis, and Mann-Whitney tests (p < 0.05). Failure modes were evaluated using optical microscopy. RESULTS: The results showed that the fiber posts cemented in canals sealed with BIOC had lower bond strength than those sealed with AHP. The ultrasonic cleaning of the post space improved the bond strength of fiber posts in canals sealed with AHP, but not with BIOC. CONCLUSIONS: BIOC decreased the bond strength of fiber posts in oval canals, regardless of ultrasonic cleaning.
RESUMO
RESUMEN: Paredes sin instrumentar y con material obturador endodóntico residual pueden elevar la posibilidad de la falla adhesiva de postes de fibroresina. Las fresas de desobturación y conformación del espacio protésico poseen una sección circular, lo que dificulta una adecuada preparación y limpieza de las paredes de los conductos ovales. El objetivo del presente estudio fue evaluar la capacidad de limpieza ultrasónica del espacio protésico y cómo ésta influyó en la resistencia a la tracción de postes de fibroresina en conductos ovales. Se utilizaron 30 premolares con conducto ovalado divididos aleatoriamente en 3 grupos de estudio (n=10), siendo: grupo A: preparación rotatoria con complemento ultrasónico, grupo B: preparación rotatoria y grupo C: grupo control. Postes de fibra de vidrio fueron cementados y luego de 7 días se realizaron cortes de un milímetro de grosor del tercio cervical y medio de cada muestra y se evaluó microscópicamente el área de gutapercha remanente y área efectiva de adhesión. Estos fueron sometidos a una prueba de push out evaluando la resistencia adhesiva de los postes. Finalmente fueron observados microscópicamente para analizar tipo de falla. Los resultados se analizaron mediante el test de ANOVA, Bonferroni, Kruskal-Wallis y Mann Whitney (p < 0.05), registrando diferencias estadísticamente significativas en la resistencia a tracción, área de gutapercha remanente y área disponible para la adhesión; además de una relación directa entre gutapercha remanente y menor resistencia a la tracción. Conclusiones: La preparación ultrasónica del espacio protésico aumenta la resistencia a la tracción de postes de fibroresinas cementados en conductos ovalados.
ABSTRACT: Untouched canal walls with residual filling materials can increase the probability of adhesive failure of fiber posts. The drills used for desobturation and conformation of the prosthetic space, has a circular cross section, which does not allow a proper preparation and cleaning of oval-shaped canal walls. The objective of the study was to evaluate the ultrasonic cleaning of the prosthetic space and how this influences the adhesive strength of fiber posts in oval-shaped canals. Thirty (30) oval-shaped canal premolars were randomly divided into 3 groups (n = 10): Group A: rotary desobturation with ultrasonic complement, group B: rotary desobturation without ultrasonic complement and group C: control group. Fiberglass posts were cemented; after 7 days, one-millimeter slices were performed, one of the cervical and another from the middle third of the root. The slices were analyzed under an optical microscope to evaluate remaining gutta percha and effective adhesion area. Samples were subjected to a push-out test to evaluate bond strength of the fiber resin posts. Finally, samples were evaluated microscopically to analyze the type of failure. The results were analyzed using ANOVA, Bonferroni, KruskalWallis and Mann Whitney test (p < 0.05), recording statistically significant differences in bond strength, remaining gutta-percha area and clean walls for adhesion; In addition, to a direct relationship between remaining gutta percha and lower adhesive strength, the ultrasonic preparation of the prosthetic space increases bond strength of fiber posts in oval canals.