RESUMO
Modulated self-assembly protocols are used to develop facile, HF-free syntheses of the archetypal flexible PCP, MIL-53(Cr), and novel isoreticular analogues MIL-53(Cr)-Br and MIL-53(Cr)-NO2. All three PCPs show good SO2 uptake (298 K, 1 bar) and high chemical stabilities against dry and wet SO2. Solid-state photoluminescence spectroscopy indicates all three PCPs exhibit turn-off sensing of SO2, in particular MIL-53(Cr)-Br, which shows a 2.7-fold decrease in emission on exposure to SO2 at room temperature, indicating potential sensing applications.
RESUMO
MFM-300(Sc) was explored as a catalyst for the gas-phase hydrogenation of acetone. The catalysis results support the presence of non-permanent open Sc(III) sites within the structure due to the requirement of Lewis acid sites for the reaction to proceed. The open Sc(III) sites are generated in situ due to the presence of hemilabile Sc-O bonds. MFM-300(Sc) showed high mechanical and chemical stability, and the crystalline structure was maintained after the catalytic reaction. The catalytic activity of the material was quantified by performing a gas-phase reaction using a continuous flow reactor. The acetone conversion in MFM-300(Sc) was estimated to be 27.7% with no loss of activity after catalytic cycles.
RESUMO
The SO2 adsorption-desorption capacity at room temperature and 1 bar of the metal-organic polyhedron MOP-CDC was investigated. In addition, the qualitative solid-state absorption-emission properties of this material (before and after SO2 exposure) were measured and tested, and it demonstrated remarkable capability for SO2 detection. Our results represent the first example of fluorimetric SO2 detection in a MOP.
Assuntos
Metais , AdsorçãoRESUMO
Metal-organic frameworks MIL-53(Al)-TDC and MIL-53(Al)-BDC were explored in the SO2 adsorption process. MIL-53(Al)-TDC was shown to behave as a rigid-like material upon SO2 adsorption. On the other hand, MIL-53(Al)-BDC exhibits guest-induced flexibility of the framework with the presence of multiple steps in the SO2 adsorption isotherm that was related through molecular simulations to the existence of three different pore opening phases narrow pore, intermediate pore, and large pore. Both materials proved to be exceptional candidates for SO2 capture, even under wet conditions, with excellent SO2 adsorption, good cycling, chemical stability, and easy regeneration. Further, we propose MIL-53(Al)-TDC and MIL-53(A)-BDC of potential interest for SO2 sensing and SO2 storage/transportation, respectively.
RESUMO
We report the first experimental investigation of porous organic cages (POCs) for the demanding challenge of SO2 capture. Three structurally related N-containing cage molecular materials were studied. An imine-functionalized POC (CC3) showed modest and reversible SO2 capture, while a secondary-amine POC (RCC3) exhibited high but irreversible SO2 capture. A tertiary amine POC (6FT-RCC3) demonstrated very high SO2 capture (13.78â mmol g-1 ; 16.4 SO2 molecules per cage) combined with excellent reversibility for at least 50 adsorption-desorption cycles. The adsorption behavior was investigated by FTIR spectroscopy, 13 Câ CP-MAS NMR experiments, and computational calculations.