RESUMO
Petroleum-based food packaging causes environmental problems such as waste accumulation and microplastic generation. In this work, biobased films from stable polyelectrolyte complex suspensions (PECs) of xylan and chitosan (70 Xyl/30 Ch wt% mass ratio), at different concentrations of citric acid (CA) (0, 2.5, 5, 7.5 wt%), were prepared and characterized. Films were treated at two temperatures (135 °C, 155 °C) and times (30 min, 60 min) to promote covalent crosslinking. Esterification and amidation reactions were confirmed by Fourier Transform Infrared Spectroscopy and Confocal Raman Microscopy. Water resistance and dry and wet stress-strain results were markedly increased by thermal treatment, mainly at 155 °C. The presence of 5 wt% CA tended to increase dry and wet stress-strain values further, up to 88 MPa-10% (155 °C for 60 min), and 5.6 MPa-40% (155 °C for 30 min), respectively. The UV-blocking performance of the films was improved by all treatments, as was thermal stability (up to Tonset: 230 °C). Contact angle values were between 73 and 84°, indicating partly wettable surfaces. Thus, thermal treatment at low CA concentrations represents a good alternative for improving the performance of Xyl/Ch films.
RESUMO
The present work analyzes the effect of process variables and the method of characterization of cellulose micro/nanofibers (CMNFs) obtained by different treatments. A chemical pre-treatment was performed using oxalic acid at 25 wt.% and 50 wt.%. Moreover, for mechanical pre-treatments, a rotary homogenizer or a PFI mill refiner were considered. For the mechanical fibrillation to obtain CMNFs, 5 and 15 passes through a pressurized homogenization were considered. The best results of nanofibrillation yield (76.5%), transmittance (72.1%) and surface charges (71.0 µeq/g CMNF) were obtained using the PFI mill refiner, 50 wt.% oxalic acid and 15 passes. Nevertheless, the highest aspect ratio (length/diameter) determined by Transmission Electron Microscopy (TEM) was found using the PFI mill refiner and 25 wt.% oxalic acid treatment. The aspect ratio was related to the gel point and intrinsic viscosity of CMNF suspensions. The values estimated for gel point agree with those determined by TEM. Moreover, a strong relationship between the intrinsic viscosity [η] of the CMNF dispersions and the corresponding aspect ratio (p) was found (ρ[η] = 0.014 p2.3, R2 = 0.99). Finally, the tensile strength of films obtained from CMNF suspensions was more influenced by the nanofibrillation yield than their aspect ratio.
RESUMO
The removal of native acetyl groups from hardwood O-acetyl-glucuronoxylan has a strong effect on physical characteristics, accessibility and structure of this polymer. The removal also has effects on the swelling and ion transport capacity of the cell wall of hardwoods. In this work, a kinetic expression for Eucalyptus wood deacetylation is determined. Two liquid mediums are considered: a simple alkaline one and another with a higher sodium concentration. The kinetic expression is a power law for the acetyl content and the concentrations in the liquid medium dependence, and is an Arrhenius type expression for temperature dependence. The kinetic expression can be useful to predict the physical properties of wood since the analysis of deacetylation effects on effective capillarity (ECCSA) shows that the acetyl content is a determining factor of wood ionic transport capacity.