RESUMO
The literature has shown that there is no consensus regarding the best resin composite photoactivation protocol. This study evaluated the efficiency of the conventional, soft-start, pulse-delay and exponential protocols for photoactivation of resin composites in reducing the shrinkage stress and temperature variation during the photopolymerisation. The photoactivation processes were performed using a photocuring unit and a smartphone app developed to control the irradiance according each photoactivation protocol. These photoactivation methods were evaluated applying photoactivation energies recommended by the resins manufactures. Three brands of resin composites were analysed: Z-250, Charisma and Ultrafill. The cure effectiveness was evaluated through depth of cure experiments. All results were statistically evaluated using one-way and multi-factor analysis of variance (ANOVA). The use of exponential and pulse-delay methods resulted in a significant reduction of the shrinkage stress for all evaluated resins; however, the pulse-delay method required too long a photoactivation time. The increases on the temperature were lower when the exponential photoactivation was applied; however, the temperature variation for all photoactivation protocols was not enough to cause damage in the restoration area. The evaluation of the depth of cure showed that all photoactivation protocols resulted in cured resins with equivalent hardness, indicating that the choice of an alternative photoactivation protocol did not harm the polymerisation. In this way, the results showed the exponential protocol as the best photoactivation technique for practical applications.
RESUMO
INTRODUCTION: High levels of shrinkage stress caused by volumetric variations during the activation process are one of the main problems in the practical application of composite resins. OBJECTIVE: The aim of this study is to reduce the shrinkage stress and minimize the effects caused by composite resin volumetric variation due to the photopolymerization. In this way, this work proposes a systematic study to determine the optimal dimming function to be applied to light curing processes. MATERIAL AND METHODS: The study was performed by applying mathematical techniques to the optimization of nonlinear objective functions. The effectiveness of the dimming function was evaluated by monitoring the polymerization shrinkage stress during the curing process of five brands/models of composites. This monitoring was performed on a universal testing machine using two steel bases coupled in the arms of the machine where the resin was inserted and polymerized. The quality of the composites cured by the proposed method was analyzed and compared with the conventional photoactivation method by experiments to determine their degree of conversion (DC). Absorbance measurements were performed using Fourier-transform infrared spectroscopy (FT-IR). A T-test was performed on DC results to compare the photoactivation techniques. We also used scanning electron microscopy (SEM) to analyze in-vitro the adhesion interface of the resin in human teeth. RESULTS: Our results showed that the use of the optimal dimming function, named as exponential, resulted in the significant reduction of the shrinkage stress (~36.88% ±6.56 when compared with the conventional method) without affecting the DC (t=0.86, p-value=0.44). The SEM analyses show that the proposed process can minimize or even eliminate adhesion failures between the tooth and the resin in dental restorations. CONCLUSION: The results from this study can promote the improvement of the composite resin light curing process by the minimization of polymerization shrinkage effects, given an operational standardization of the photoactivation process.
Assuntos
Resinas Compostas/química , Resinas Compostas/efeitos da radiação , Cura Luminosa de Adesivos Dentários/métodos , Polimerização/efeitos da radiação , Adesividade , Análise do Estresse Dentário , Teste de Materiais , Microscopia Eletrônica de Varredura , Transição de Fase/efeitos da radiação , Valores de Referência , Espectroscopia de Infravermelho com Transformada de Fourier , Estresse Mecânico , Fatores de TempoRESUMO
Abstract High levels of shrinkage stress caused by volumetric variations during the activation process are one of the main problems in the practical application of composite resins. Objective The aim of this study is to reduce the shrinkage stress and minimize the effects caused by composite resin volumetric variation due to the photopolymerization. In this way, this work proposes a systematic study to determine the optimal dimming function to be applied to light curing processes. Material and Methods The study was performed by applying mathematical techniques to the optimization of nonlinear objective functions. The effectiveness of the dimming function was evaluated by monitoring the polymerization shrinkage stress during the curing process of five brands/models of composites. This monitoring was performed on a universal testing machine using two steel bases coupled in the arms of the machine where the resin was inserted and polymerized. The quality of the composites cured by the proposed method was analyzed and compared with the conventional photoactivation method by experiments to determine their degree of conversion (DC). Absorbance measurements were performed using Fourier-transform infrared spectroscopy (FT-IR). A T-test was performed on DC results to compare the photoactivation techniques. We also used scanning electron microscopy (SEM) to analyze in-vitro the adhesion interface of the resin in human teeth. Results Our results showed that the use of the optimal dimming function, named as exponential, resulted in the significant reduction of the shrinkage stress (~36.88% ±6.56 when compared with the conventional method) without affecting the DC (t=0.86, p-value=0.44). The SEM analyses show that the proposed process can minimize or even eliminate adhesion failures between the tooth and the resin in dental restorations. Conclusion The results from this study can promote the improvement of the composite resin light curing process by the minimization of polymerization shrinkage effects, given an operational standardization of the photoactivation process.