This work aimed to evaluate the use of colorimetry in the characterization of biodeterioration marupá, jequitibá and cumaru wood, submitted to white and brown rot. For this purpose, specimens of each Amazonian species were submitted to accelerated decay tests, according to American Society for Testing and Materials - ASTM D2017, during 20 weeks. With a colorimeter, the colorimetric parameters L* (lightness), a* (green-red coordinate), b* (blue-yellow coordinate) and total color change (ΔE) were determined weekly until the fourth week, and then every two weeks until the twentieth week. Additionally, it was determined the mass loss. The results indicated that the colorimetry was effective in monitoring of biodeterioration of wood, as well as to differentiate white and brown rot. The best predictions of natural resistance to white and brown rot were obtained with the parameters b* and L*, respectively. We also emphasizes the use of ΔE to estimate the biodeterioration of wood, because of their significant correlations with weight loss.(AU)
Objetivou-se avaliar o emprego da colorimetria na caracterização da biodeterioração das madeiras de marupá, jequitibá e cumaru submetidas ao ataque de fungos de podridão branca e parda. Para tanto, corpos de prova de cada espécie amazônica foram submetidos a ensaios de apodrecimento acelerado, de acordo com a American Society for Testing and Materials - ASTM D2017, durante 20 semanas. Os parâmetros colorimétricos L* (luminosidade), a* (coordenada verde-vermelho), b* (coordenada amarelo-azul) e a variação total da cor (ΔE) foram determinados semanalmente até a quarta semana, e posteriormente a cada duas semanas até a vigésima semana, com auxílio de um espectrofotocolorímetro. Adicionalmente, foram determinadas as perdas de massa dos corpos de prova. Os resultados permitiram destacar que a colorimetria foi eficaz no monitoramento da biodeterioração da madeira, bem como para diferenciação da podridão branca e parda. As melhores predições da resistência natural aos fungos de podridão branca e parda foram obtidas com os parâmetros b* e L*, respectivamente. Enfatiza-se também, o emprego da ΔE como parâmetro auxiliar na estimativa da biodeterioração da madeira, em razão de suas correlações significativas com a perda de massa.(AU)
RESUMO
This work aimed to evaluate the use of colorimetry in the characterization of biodeterioration marupá, jequitibá and cumaru wood, submitted to white and brown rot. For this purpose, specimens of each Amazonian species were submitted to accelerated decay tests, according to American Society for Testing and Materials - ASTM D2017, during 20 weeks. With a colorimeter, the colorimetric parameters L* (lightness), a* (green-red coordinate), b* (blue-yellow coordinate) and total color change (ΔE) were determined weekly until the fourth week, and then every two weeks until the twentieth week. Additionally, it was determined the mass loss. The results indicated that the colorimetry was effective in monitoring of biodeterioration of wood, as well as to differentiate white and brown rot. The best predictions of natural resistance to white and brown rot were obtained with the parameters b* and L*, respectively. We also emphasizes the use of ΔE to estimate the biodeterioration of wood, because of their significant correlations with weight loss.
Objetivou-se avaliar o emprego da colorimetria na caracterização da biodeterioração das madeiras de marupá, jequitibá e cumaru submetidas ao ataque de fungos de podridão branca e parda. Para tanto, corpos de prova de cada espécie amazônica foram submetidos a ensaios de apodrecimento acelerado, de acordo com a American Society for Testing and Materials - ASTM D2017, durante 20 semanas. Os parâmetros colorimétricos L* (luminosidade), a* (coordenada verde-vermelho), b* (coordenada amarelo-azul) e a variação total da cor (ΔE) foram determinados semanalmente até a quarta semana, e posteriormente a cada duas semanas até a vigésima semana, com auxílio de um espectrofotocolorímetro. Adicionalmente, foram determinadas as perdas de massa dos corpos de prova. Os resultados permitiram destacar que a colorimetria foi eficaz no monitoramento da biodeterioração da madeira, bem como para diferenciação da podridão branca e parda. As melhores predições da resistência natural aos fungos de podridão branca e parda foram obtidas com os parâmetros b* e L*, respectivamente. Enfatiza-se também, o emprego da ΔE como parâmetro auxiliar na estimativa da biodeterioração da madeira, em razão de suas correlações significativas com a perda de massa.
RESUMO
Objetivou-se avaliar o emprego de ensaios de dureza Rockwell na caracterização da biodeterioração das madeiras de Simarouba amara (marupá), Cariniana micrantha (jequitibá) e Dipteryx odorata (cumaru), submetidas ao ataque dos fungos apodrecedores Trametes versicolor (podridão branca) e Gloeophyllum trabeum (podridão parda). Para tanto, corpos de prova de cada espécie amazônica foram submetidos a ensaios de apodrecimento acelerado, de acordo com a ASTM D2017 (2005), durante 20 semanas. A caracterização da dureza Rockwell foi realizada semanalmente até a 4ª semana e, posteriormente, a cada duas semanas, até a 20ª semana. Adicionalmente, foram determinadas as perdas de massa, conforme critérios estabelecidos pela ASTM D2017 (2005). Quanto aos resultados, destaca-se que a dureza Rockwell pode ser empregada como ferramenta principal na caracterização da biodeterioração da madeira, sendo sensível na predição dos estágios iniciais. Dentre as madeiras amazônicas, o cumaru apresentou a maior resistência natural aos fungos apodrecedores. Com relação aos fungos, a podridão parda atacou mais intensamente as três madeiras amazônicas.
This study aimed to evaluate the use of Rockwell hardness in the characterization of the biodeterioration of Simarouba amara (marupá), Cariniana micrantha (jequitibá) e Dipteryx odorata (cumaru) woods, which were submitted to decay fungi Trametes versicolor (white rot) and Gloeophyllum trabeum (brown rot). For this purpose, specimens of each Amazon species were submitted to decay fungi, according to ASTM D2017 (2005). The characterization of the Rockwell hardness was performed weekly until the fourth week, and then every two weeks until the twentieth week. Additionally, it was determined the mass loss, according to criteria established by ASTM D2017 (2005). The results indicated that the Rockwell hardness can be used as a primary tool in the characterization of the biodeterioration of wood, being sensitive in predicting the early stages. Among the Amazon woods, cumaru wood showed a greater natural resistance to decay fungi. With respect to decay fungi, brown rot more intensely attacked the three Amazon woods.
RESUMO
This study aimed to evaluate the use of Rockwell hardness in the characterization of the biodeterioration of Simarouba amara (marupá), Cariniana micrantha (jequitibá) e Dipteryx odorata (cumaru) woods, which were submitted to decay fungi Trametes versicolor (white rot) and Gloeophyllum trabeum (brown rot). For this purpose, specimens of each Amazon species were submitted to decay fungi, according to ASTM D2017 (2005). The characterization of the Rockwell hardness was performed weekly until the fourth week, and then every two weeks until the twentieth week. Additionally, it was determined the mass loss, according to criteria established by ASTM D2017 (2005). The results indicated that the Rockwell hardness can be used as a primary tool in the characterization of the biodeterioration of wood, being sensitive in predicting the early stages. Among the Amazon woods, cumaru wood showed a greater natural resistance to decay fungi. With respect to decay fungi, brown rot more intensely attacked the three Amazon woods.
Objetivou-se avaliar o emprego de ensaios de dureza Rockwell na caracterização da biodeterioração das madeiras de Simarouba amara (marupá), Cariniana micrantha (jequitibá) e Dipteryx odorata (cumaru), submetidas ao ataque dos fungos apodrecedores Trametes versicolor (podridão branca) e Gloeophyllum trabeum (podridão parda). Para tanto, corpos de prova de cada espécie amazônica foram submetidos a ensaios de apodrecimento acelerado, de acordo com a ASTM D2017 (2005), durante 20 semanas. A caracterização da dureza Rockwell foi realizada semanalmente até a 4ª semana e, posteriormente, a cada duas semanas, até a 20ª semana. Adicionalmente, foram determinadas as perdas de massa, conforme critérios estabelecidos pela ASTM D2017 (2005). Quanto aos resultados, destaca-se que a dureza Rockwell pode ser empregada como ferramenta principal na caracterização da biodeterioração da madeira, sendo sensível na predição dos estágios iniciais. Dentre as madeiras amazônicas, o cumaru apresentou a maior resistência natural aos fungos apodrecedores. Com relação aos fungos, a podridão parda atacou mais intensamente as três madeiras amazônicas.
RESUMO
This study aimed to evaluate the use of Rockwell hardness in the characterization of the biodeterioration of Simarouba amara (marupá), Cariniana micrantha (jequitibá) e Dipteryx odorata (cumaru) woods, which were submitted to decay fungi Trametes versicolor (white rot) and Gloeophyllum trabeum (brown rot). For this purpose, specimens of each Amazon species were submitted to decay fungi, according to ASTM D2017 (2005). The characterization of the Rockwell hardness was performed weekly until the fourth week, and then every two weeks until the twentieth week. Additionally, it was determined the mass loss, according to criteria established by ASTM D2017 (2005). The results indicated that the Rockwell hardness can be used as a primary tool in the characterization of the biodeterioration of wood, being sensitive in predicting the early stages. Among the Amazon woods, cumaru wood showed a greater natural resistance to decay fungi. With respect to decay fungi, brown rot more intensely attacked the three Amazon woods.
Objetivou-se avaliar o emprego de ensaios de dureza Rockwell na caracterização da biodeterioração das madeiras de Simarouba amara (marupá), Cariniana micrantha (jequitibá) e Dipteryx odorata (cumaru), submetidas ao ataque dos fungos apodrecedores Trametes versicolor (podridão branca) e Gloeophyllum trabeum (podridão parda). Para tanto, corpos de prova de cada espécie amazônica foram submetidos a ensaios de apodrecimento acelerado, de acordo com a ASTM D2017 (2005), durante 20 semanas. A caracterização da dureza Rockwell foi realizada semanalmente até a 4ª semana e, posteriormente, a cada duas semanas, até a 20ª semana. Adicionalmente, foram determinadas as perdas de massa, conforme critérios estabelecidos pela ASTM D2017 (2005). Quanto aos resultados, destaca-se que a dureza Rockwell pode ser empregada como ferramenta principal na caracterização da biodeterioração da madeira, sendo sensível na predição dos estágios iniciais. Dentre as madeiras amazônicas, o cumaru apresentou a maior resistência natural aos fungos apodrecedores. Com relação aos fungos, a podridão parda atacou mais intensamente as três madeiras amazônicas.
RESUMO
This study aimed to evaluate the use of Rockwell hardness in the characterization of the biodeterioration of Simarouba amara (marupá), Cariniana micrantha (jequitibá) e Dipteryx odorata (cumaru) woods, which were submitted to decay fungi Trametes versicolor (white rot) and Gloeophyllum trabeum (brown rot). For this purpose, specimens of each Amazon species were submitted to decay fungi, according to ASTM D2017 (2005). The characterization of the Rockwell hardness was performed weekly until the fourth week, and then every two weeks until the twentieth week. Additionally, it was determined the mass loss, according to criteria established by ASTM D2017 (2005). The results indicated that the Rockwell hardness can be used as a primary tool in the characterization of the biodeterioration of wood, being sensitive in predicting the early stages. Among the Amazon woods, cumaru wood showed a greater natural resistance to decay fungi. With respect to decay fungi, brown rot more intensely attacked the three Amazon woods.
Objetivou-se avaliar o emprego de ensaios de dureza Rockwell na caracterização da biodeterioração das madeiras de Simarouba amara (marupá), Cariniana micrantha (jequitibá) e Dipteryx odorata (cumaru), submetidas ao ataque dos fungos apodrecedores Trametes versicolor (podridão branca) e Gloeophyllum trabeum (podridão parda). Para tanto, corpos de prova de cada espécie amazônica foram submetidos a ensaios de apodrecimento acelerado, de acordo com a ASTM D2017 (2005), durante 20 semanas. A caracterização da dureza Rockwell foi realizada semanalmente até a 4ª semana e, posteriormente, a cada duas semanas, até a 20ª semana. Adicionalmente, foram determinadas as perdas de massa, conforme critérios estabelecidos pela ASTM D2017 (2005). Quanto aos resultados, destaca-se que a dureza Rockwell pode ser empregada como ferramenta principal na caracterização da biodeterioração da madeira, sendo sensível na predição dos estágios iniciais. Dentre as madeiras amazônicas, o cumaru apresentou a maior resistência natural aos fungos apodrecedores. Com relação aos fungos, a podridão parda atacou mais intensamente as três madeiras amazônicas.
RESUMO
O conhecimento acerca da resistência dos compostos ligno-celulósicos ao ataque de microrganismos é primordial para servir de base à prevenção da deterioração e a correta destinação de emprego do material. Nesse sentido, avaliou-se a resistência natural a fungos apodrecedores de painéis aglomerados confeccionados com partículas de madeira (Eucalyptus grandis) e/ou bambu (Bambusa vulgaris). Foram produzidas, em laboratório, chapas aglomeradas nas dimensões 50x50x0,95cm e massa específica pré-estabelecida em 0,70g cm-3, nas proporções de 100:0, 75:25, 50:50, 25:75 e 0:100 de madeira e bambu, respectivamente. A massa de partículas representou 91 por cento da massa seca de cada painel, sendo, o restante, formado pelo adesivo ureia-formaldeído (8 por cento) e parafina (1 por cento). Para determinação da resistência natural ao ataque de fungos xilófagos, os painéis foram testados em laboratório e utilizados os fungos Gloeophyllum trabeum (podridão parda) e Trametes versicolor (podridão branca), de acordo com a ASTM D 2017 (2005). Quanto aos resultados, foi observado que os painéis confeccionados com mistura de partículas de madeira e bambu apresentaram menor resistência ao ataque dos fungos apodrecedores. Painéis que utilizaram apenas bambu ou madeira apresentaram resistência biológica semelhante. Dentre os fungos, T. versicolor atacou mais severamente os painéis.
The knowledge about lignocellulosic compounds strength to the attack of microorganisms is essential for preventing deterioration and also for knowing the correct usage of the material. Accordingly it was evaluated the natural resistance of wood panels made of particles of wood (Eucalyptus grandis) and/or bamboo (Bambusa vulgaris) to decay fungi. Particleboards were produced in laboratory, each of them with dimensions 50x50x0.95cm and density pre-set at 0.70g cm-3, in proportions of 100:0, 75:25, 50:50, 25:75 and 0:100 of wood and bamboo, respectively. The particles mass represented 91 percent of the dry mass of each panel while the remainder was formed by the urea-formaldehyde adhesive (8 percent) and paraffin (1 percent). The panels were tested in the laboratory and Gloeophyllum trabeum (brown rot) and Trametes versicolor (white rot) were used to determine the natural resistance to attack by wood decay fungi. It was observed that panels which were made with a mixture of particles of wood and bamboo were less resistant to attack by decay fungi. Panels that were made from bamboo or wood only showed similar biological resistance. Among fungi, T. versicolor was the one that attacked panels more severely.
RESUMO
The knowledge about lignocellulosic compounds strength to the attack of microorganisms is essential for preventing deterioration and also for knowing the correct usage of the material. Accordingly it was evaluated the natural resistance of wood panels made of particles of wood (Eucalyptus grandis) and/or bamboo (Bambusa vulgaris) to decay fungi. Particleboards were produced in laboratory, each of them with dimensions 50x50x0.95cm and density pre-set at 0.70g cm-3, in proportions of 100:0, 75:25, 50:50, 25:75 and 0:100 of wood and bamboo, respectively. The particles mass represented 91% of the dry mass of each panel while the remainder was formed by the urea-formaldehyde adhesive (8%) and paraffin (1%). The panels were tested in the laboratory and Gloeophyllum trabeum (brown rot) and Trametes versicolor (white rot) were used to determine the natural resistance to attack by wood decay fungi. It was observed that panels which were made with a mixture of particles of wood and bamboo were less resistant to attack by decay fungi. Panels that were made from bamboo or wood only showed similar biological resistance. Among fungi, T. versicolor was the one that attacked panels more severely.
O conhecimento acerca da resistência dos compostos ligno-celulósicos ao ataque de microrganismos é primordial para servir de base à prevenção da deterioração e a correta destinação de emprego do material. Nesse sentido, avaliou-se a resistência natural a fungos apodrecedores de painéis aglomerados confeccionados com partículas de madeira (Eucalyptus grandis) e/ou bambu (Bambusa vulgaris). Foram produzidas, em laboratório, chapas aglomeradas nas dimensões 50x50x0,95cm e massa específica pré-estabelecida em 0,70g cm-3, nas proporções de 100:0, 75:25, 50:50, 25:75 e 0:100 de madeira e bambu, respectivamente. A massa de partículas representou 91% da massa seca de cada painel, sendo, o restante, formado pelo adesivo ureia-formaldeído (8%) e parafina (1%). Para determinação da resistência natural ao ataque de fungos xilófagos, os painéis foram testados em laboratório e utilizados os fungos Gloeophyllum trabeum (podridão parda) e Trametes versicolor (podridão branca), de acordo com a ASTM D 2017 (2005). Quanto aos resultados, foi observado que os painéis confeccionados com mistura de partículas de madeira e bambu apresentaram menor resistência ao ataque dos fungos apodrecedores. Painéis que utilizaram apenas bambu ou madeira apresentaram resistência biológica semelhante. Dentre os fungos, T. versicolor atacou mais severamente os painéis.
RESUMO
The knowledge about lignocellulosic compounds strength to the attack of microorganisms is essential for preventing deterioration and also for knowing the correct usage of the material. Accordingly it was evaluated the natural resistance of wood panels made of particles of wood (Eucalyptus grandis) and/or bamboo (Bambusa vulgaris) to decay fungi. Particleboards were produced in laboratory, each of them with dimensions 50x50x0.95cm and density pre-set at 0.70g cm-3, in proportions of 100:0, 75:25, 50:50, 25:75 and 0:100 of wood and bamboo, respectively. The particles mass represented 91% of the dry mass of each panel while the remainder was formed by the urea-formaldehyde adhesive (8%) and paraffin (1%). The panels were tested in the laboratory and Gloeophyllum trabeum (brown rot) and Trametes versicolor (white rot) were used to determine the natural resistance to attack by wood decay fungi. It was observed that panels which were made with a mixture of particles of wood and bamboo were less resistant to attack by decay fungi. Panels that were made from bamboo or wood only showed similar biological resistance. Among fungi, T. versicolor was the one that attacked panels more severely.
O conhecimento acerca da resistência dos compostos ligno-celulósicos ao ataque de microrganismos é primordial para servir de base à prevenção da deterioração e a correta destinação de emprego do material. Nesse sentido, avaliou-se a resistência natural a fungos apodrecedores de painéis aglomerados confeccionados com partículas de madeira (Eucalyptus grandis) e/ou bambu (Bambusa vulgaris). Foram produzidas, em laboratório, chapas aglomeradas nas dimensões 50x50x0,95cm e massa específica pré-estabelecida em 0,70g cm-3, nas proporções de 100:0, 75:25, 50:50, 25:75 e 0:100 de madeira e bambu, respectivamente. A massa de partículas representou 91% da massa seca de cada painel, sendo, o restante, formado pelo adesivo ureia-formaldeído (8%) e parafina (1%). Para determinação da resistência natural ao ataque de fungos xilófagos, os painéis foram testados em laboratório e utilizados os fungos Gloeophyllum trabeum (podridão parda) e Trametes versicolor (podridão branca), de acordo com a ASTM D 2017 (2005). Quanto aos resultados, foi observado que os painéis confeccionados com mistura de partículas de madeira e bambu apresentaram menor resistência ao ataque dos fungos apodrecedores. Painéis que utilizaram apenas bambu ou madeira apresentaram resistência biológica semelhante. Dentre os fungos, T. versicolor atacou mais severamente os painéis.
RESUMO
Grápia (Apuleia leiocarpa Vog. Macbride) is a native forest specie that has been in extinction process. The purpose of this study was to characterize the nutritional requirements of grápia in a red yellow podzolic soil by using the lacking nutrient technique. Grápia plants were cultivated in pots containing soil, under glasshouse conditions. Eighteen treatments were tested in a fatorial design (2 X 9). The factors consisted of two profiles of the same soil (A and B) and nine fertilization treatments. The fertilization treatments were: (1) natural soil, (2) complete fertilization with macro and micronutrients (complete), (3) complete less N, (4) complete less P, (5) complete less K, (6) complete less Ca, (7) complete less Mg, (8) complete less S, and (9) complete less the micronutrients Zn, Cu, Fe, Mn, B and Mo. After 165 days of cultivation the growth parameters analysed were dry weight of roots and aerial part, relationship between dry weight of root and aerial part, number of leaves, total lenght of the root system, shoot diameter, height of the plant, number of shoot nodes, and the concentration of N, P, K, Ca, Mg, Zn, Cu, Mn and Fe in the plants parts. The isolated omission of Ca, Mg, and of the micronutrients Zn, Cu, Fe and Mn from the fertilization do not affect the growth of grápia in height, shoot diameter, number of shoot nodes, number of leaves, and biomass accumulation, as well as the nutrient concentration in the plant tissues, indicating that the natural nutrient levels are adequate. The height of the plant, number of shoot nodes, number of leaves, total lenght of the root system, biomass accumulation and the nutrient concentration decrease strikingly by omitting P, S, N and K from the fertilization, for both profiles of the soil.
A grápia (Apuleia leiocarpa Vog. Macbride) é uma espécie florestal nativa que se encontra atualmente em processo de extinção. O presente trabalho foi desenvolvido com o objetivo de caracterizar as exigências nutricionais da grápia pela técnica do nutriente faltante em solo Podzólico vermelho amarelo (unidade de mapeamento São Pedro). As plantas de grápia foram cultivadas em vasos contendo solo, sob condições de casa de vegetação. Foram testados 18 tratamentos em esquema fatorial (2 X 9), onde os fatores consistiram em dois horizontes de um mesmo solo (A e B) e 9 variações de adubação. Os tratamentos de adubação foram: (1) solo natural; (2) adubação completa com macro e micronutrientes (completo); (3) completo -N; (4) completo -P; (5) completo -K; (6) completo -Ca; (7) completo -Mg; (8) completo - S e (9) completo - Zn, Cu, Fe, Mn, B e Mo. Após 165 dias de cultivo, avaliaram-se a produção de massa seca da parte aérea, do sistema radicular e total da planta, relação entre massa seca de raiz e parte aérea, número de folhas remanescentes, comprimento total do sistema radicular, diâmetro do caule, altura da planta, número de nós e os teores de N, P, K, Ca, Mg, Zn, Cu, Mn e Fe nos órgãos da planta. A omissão isolada de Ca, Mg e dos micronutrientes Zn, Cu, Fe, Mn da adubação não afeta significativamente o crescimento da grápia em altura, diâmetro do caule, número de nós, número de folhas e a produção da massa seca, bem como a concentração desses elementos nos tecidos da planta, demonstrando que os teores naturais desses nutrientes no solo são suficientes. A altura da planta, número de nós, número de folhas, comprimento do sistema radicular, produção de massa seca e a concentração de nutrientes diminuem acentuadamente pela omissão de P, S, N e K da adubação, tanto no horizonte A como no B do solo.
RESUMO
Grápia (Apuleia leiocarpa Vog. Macbride) is a native forest specie that has been in extinction process. The purpose of this study was to characterize the nutritional requirements of grápia in a red yellow podzolic soil by using the lacking nutrient technique. Grápia plants were cultivated in pots containing soil, under glasshouse conditions. Eighteen treatments were tested in a fatorial design (2 X 9). The factors consisted of two profiles of the same soil (A and B) and nine fertilization treatments. The fertilization treatments were: (1) natural soil, (2) complete fertilization with macro and micronutrients (complete), (3) complete less N, (4) complete less P, (5) complete less K, (6) complete less Ca, (7) complete less Mg, (8) complete less S, and (9) complete less the micronutrients Zn, Cu, Fe, Mn, B and Mo. After 165 days of cultivation the growth parameters analysed were dry weight of roots and aerial part, relationship between dry weight of root and aerial part, number of leaves, total lenght of the root system, shoot diameter, height of the plant, number of shoot nodes, and the concentration of N, P, K, Ca, Mg, Zn, Cu, Mn and Fe in the plants parts. The isolated omission of Ca, Mg, and of the micronutrients Zn, Cu, Fe and Mn from the fertilization do not affect the growth of grápia in height, shoot diameter, number of shoot nodes, number of leaves, and biomass accumulation, as well as the nutrient concentration in the plant tissues, indicating that the natural nutrient levels are adequate. The height of the plant, number of shoot nodes, number of leaves, total lenght of the root system, biomass accumulation and the nutrient concentration decrease strikingly by omitting P, S, N and K from the fertilization, for both profiles of the soil.
A grápia (Apuleia leiocarpa Vog. Macbride) é uma espécie florestal nativa que se encontra atualmente em processo de extinção. O presente trabalho foi desenvolvido com o objetivo de caracterizar as exigências nutricionais da grápia pela técnica do nutriente faltante em solo Podzólico vermelho amarelo (unidade de mapeamento São Pedro). As plantas de grápia foram cultivadas em vasos contendo solo, sob condições de casa de vegetação. Foram testados 18 tratamentos em esquema fatorial (2 X 9), onde os fatores consistiram em dois horizontes de um mesmo solo (A e B) e 9 variações de adubação. Os tratamentos de adubação foram: (1) solo natural; (2) adubação completa com macro e micronutrientes (completo); (3) completo -N; (4) completo -P; (5) completo -K; (6) completo -Ca; (7) completo -Mg; (8) completo - S e (9) completo - Zn, Cu, Fe, Mn, B e Mo. Após 165 dias de cultivo, avaliaram-se a produção de massa seca da parte aérea, do sistema radicular e total da planta, relação entre massa seca de raiz e parte aérea, número de folhas remanescentes, comprimento total do sistema radicular, diâmetro do caule, altura da planta, número de nós e os teores de N, P, K, Ca, Mg, Zn, Cu, Mn e Fe nos órgãos da planta. A omissão isolada de Ca, Mg e dos micronutrientes Zn, Cu, Fe, Mn da adubação não afeta significativamente o crescimento da grápia em altura, diâmetro do caule, número de nós, número de folhas e a produção da massa seca, bem como a concentração desses elementos nos tecidos da planta, demonstrando que os teores naturais desses nutrientes no solo são suficientes. A altura da planta, número de nós, número de folhas, comprimento do sistema radicular, produção de massa seca e a concentração de nutrientes diminuem acentuadamente pela omissão de P, S, N e K da adubação, tanto no horizonte A como no B do solo.
RESUMO
Grápia (Apuleia leiocarpa) has dificulties to be propagated via seeds, due to the long germination period and its irregularity, caused by the tegument impermeability. The aim of this study was to develop a reliable method to facilitate the seedling production of this species, an endangered Brazilian forest tree. Thus, several experiments were carried out to test the effect of boiling water and concentrated sulfuric acid (H2SO4) with different imersion periods (15s, 30s, 1min, 2min; and 30s, 2min, 5min, 10min, 20min, respectively) on seed, collected on two regions of Brazil. Concerning the substrate effects on germination and development of seedlings, the treatments consisted of a mixture (1:1v/v) of the following substrates: sand + carbonized rice husk, sand + soil, soil + carbonized rice husk, and soil alone. The results allowed to conclude that: (i) the H2SO4 is efficient to overcome impermeability of seed coat, and the best results are gotten when the imersion period is higher than 2 min (90% of germination after 5 days of H2SO4 application); (ii) seed imersion in boiling water is not recommended (100% of death); (iii) the tradicional method, without scarification of the seed tegument, for germination induction is impracticable due to the long waiting time and by the large desuniformity; and (iv) there is no effect of the types of substrates on seed germination but, on the other hand, the combination of sand + carbonized rice husk is one of the best substrate on the seedling growth.
A grápia (Apuleia leiocarpa) apresenta dificuldades de propagação via sementes, devido a sua germinação demorada e irregular, causada pela impermeabilidade do tegumento. Com o objetivo de se desenvolver um método prático para facilitar a produção de mudas dessa espécie, foram estudados os efeitos da água em ebulição e do ácido sulfúrico (H2SO4) concentrado sobre as sementes (procedentes de duas localidades do Brasil), por diferentes períodos de exposição. As sementes tratadas com H2SO4 (30s, 2min, 5min, 10min e 20min) foram subseqüentemente lavadas em água corrente durante 5min; aquelas expostas à água em ebulição (15s, 30s, 1min e 2min), fora e junto a fonte de aquecimento, foram posteriormente imersas em água deionizada por um período igual ao tratamento testemunha (16h). Quanto ao efeito do substrato na germinação e no desenvolvimento das mudas foram testados a combinação (1:1v/v) de solo + casca de arroz carbonizada, solo + areia média, areia média + casca de arroz carbonizada e solo isoladamente; sendo o experimento executado a nível de campo. Os resultados obtidos permitem concluir que: (i) o uso do H2SO4 concentrado é eficiente na quebra da dormência tegumentar, sendo que os melhores tempos de exposição das sementes devem ser superiores a 2min (90% de germinação após 5 dias da aplicação do H2SO4); (ii) a imersão das sementes em água fervente não é recomendada (100% de morte); (iii) o método tradicional, sem escarificação do tegumento, de indução da germinação é inviável, pelo longo tempo de espera e pela sua grande irregularidade; (iv) não há efeito do tipo de substrato na germinação, porém a combinação areia + casca de arroz carbonizada é a melhor combinação quanto ao desenvolvimento das mudas.
RESUMO
Grápia (Apuleia leiocarpa) has dificulties to be propagated via seeds, due to the long germination period and its irregularity, caused by the tegument impermeability. The aim of this study was to develop a reliable method to facilitate the seedling production of this species, an endangered Brazilian forest tree. Thus, several experiments were carried out to test the effect of boiling water and concentrated sulfuric acid (H2SO4) with different imersion periods (15s, 30s, 1min, 2min; and 30s, 2min, 5min, 10min, 20min, respectively) on seed, collected on two regions of Brazil. Concerning the substrate effects on germination and development of seedlings, the treatments consisted of a mixture (1:1v/v) of the following substrates: sand + carbonized rice husk, sand + soil, soil + carbonized rice husk, and soil alone. The results allowed to conclude that: (i) the H2SO4 is efficient to overcome impermeability of seed coat, and the best results are gotten when the imersion period is higher than 2 min (90% of germination after 5 days of H2SO4 application); (ii) seed imersion in boiling water is not recommended (100% of death); (iii) the tradicional method, without scarification of the seed tegument, for germination induction is impracticable due to the long waiting time and by the large desuniformity; and (iv) there is no effect of the types of substrates on seed germination but, on the other hand, the combination of sand + carbonized rice husk is one of the best substrate on the seedling growth.
A grápia (Apuleia leiocarpa) apresenta dificuldades de propagação via sementes, devido a sua germinação demorada e irregular, causada pela impermeabilidade do tegumento. Com o objetivo de se desenvolver um método prático para facilitar a produção de mudas dessa espécie, foram estudados os efeitos da água em ebulição e do ácido sulfúrico (H2SO4) concentrado sobre as sementes (procedentes de duas localidades do Brasil), por diferentes períodos de exposição. As sementes tratadas com H2SO4 (30s, 2min, 5min, 10min e 20min) foram subseqüentemente lavadas em água corrente durante 5min; aquelas expostas à água em ebulição (15s, 30s, 1min e 2min), fora e junto a fonte de aquecimento, foram posteriormente imersas em água deionizada por um período igual ao tratamento testemunha (16h). Quanto ao efeito do substrato na germinação e no desenvolvimento das mudas foram testados a combinação (1:1v/v) de solo + casca de arroz carbonizada, solo + areia média, areia média + casca de arroz carbonizada e solo isoladamente; sendo o experimento executado a nível de campo. Os resultados obtidos permitem concluir que: (i) o uso do H2SO4 concentrado é eficiente na quebra da dormência tegumentar, sendo que os melhores tempos de exposição das sementes devem ser superiores a 2min (90% de germinação após 5 dias da aplicação do H2SO4); (ii) a imersão das sementes em água fervente não é recomendada (100% de morte); (iii) o método tradicional, sem escarificação do tegumento, de indução da germinação é inviável, pelo longo tempo de espera e pela sua grande irregularidade; (iv) não há efeito do tipo de substrato na germinação, porém a combinação areia + casca de arroz carbonizada é a melhor combinação quanto ao desenvolvimento das mudas.