This paper reports on the synthesis and characterization of La2O3:Eu3+ luminescent aerogels fabricated by the sol-gel method and the supercritical drying technique. The % mol concentration of the Eu3+ ion was varied to study the effects on the luminescent properties of the aerogels. XRD and TEM analysis showed that the La2O3:Eu3+ aerogels exhibited a semi-crystalline behavior regardless of whether the concentration of europium was increased. SEM micrographs revealed a porous structure in the aerogels, which were composed of quasi-spherical nanoparticles that were interconnected and formed coral-shaped agglomerates. Photoluminescence spectroscopy characterization showed that the aerogels had an infrared emission located at λ = 793 nm, and the maximum photoluminescence emission intensity was observed for the aerogel with 50% Eu3+. The results demonstrate that, without heat treatment, it is possible to manufacture luminescent aerogels of rare-earth oxides that can be used in opto-electronic devices.
RESUMO
Transparent BaTiO(3):Eu(3+) films were prepared via a sol-gel method and dip-coating technique, using barium acetate, titanium butoxide, and polyvinylpyrrolidone (PVP) as modifier viscosity. BaTiO(3):Eu(3+) films ~500 nm thick, crystallized after thermal treatment at 700 masculineC. The powders revealed spherical and rod shape morphology. The optical quality of films showed a predominant band at 615 nm under 250 nm excitation. A preliminary luminescent test provided the properties of the Eu(3+) doped BaTiO(3).