RESUMO
In this work, titanium dioxide scaffolds were synthesized. Titanium isopropoxide (IV) was used as a precursor in its formation, using a polymeric network of galactopyranose as a template. The powder sample obtained was evaluated by scanning tunneling microscopy (STM), transmission electron microscopy (TEM), X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET) analysis, and thermal gravimetric analysis (TGA-DTA). According to the results, it was found that these scaffolds can be successfully synthesized in solution using the sol-gel method. The synthesized scaffolds have diameters from 50 nm with porosity of approximately 0.3-10 nm. Important parameters, such as pH and the concentration of the metallic precursors, were optimized in this solution. The values of maximum average roughness R(max) and roughness value (Ra) were 0.50 and 1.45, respectively. XRD diffraction analysis shows the formation of crystalline phases in the TiO2 scaffold at 700 °C. The use of biological polymers represents an alternative for the synthesis of new materials at low cost, manipulating the conditions in the production processes and making the proposed system more efficient.
RESUMO
The aim of this work was to evaluate the corrosion behavior of the AA6061 and AlSi10Mg alloys produced by extruded and additive manufacturing (selective laser melting, SLM). Alloys were immersed in two electrolytes in H2O and 3.5 wt. % NaCl solutions at room temperature and their corrosion behavior was studied by electrochemical noise technique (EN). Three different methods filtered EN signals, and the statistical analysis was employed to obtain Rn, the localization index (LI), Kurtosis, skew, and the potential spectral density analysis (PSD). The Energy Dispersion Plots (EDP) of wavelets method was employed to determine the type of corrosion and the Hilbert-Huang Transform (HHT), analyzing the Hilbert Spectra. The result indicated that the amplitude of the transients in the time series in potential and current is greater in the AlSi10Mg alloy manufactured by additive manufacturing. The amplitude of the transients decreases in both alloys (AA6061 and AlSi10Mg) as time increases.