RESUMO

Objective: This study aimed to evaluate the bond strength of a universal adhesive to dentin (µTBS) using different time periods of airborne particle abrasion (APA) and two types of acid etching. Methods: Seventy-two human third molars were divided into 9 groups (n=8) according to dentin pretreatment: APA duration (0, 5, or 10s) and acid etching (no acid - NA, 37% phosphoric acid - PhoA, or 1% phytic acid - PhyA). APA was performed at a 0.5 cm distance and air pressure of 60 psi using 50 µm aluminum oxide particles. Afterwards, two coats of Single Bond Universal adhesive (3M) were applied to the dentin surface. Composite blocks were built using the incremental technique, sectioned into 1×1 mm slices and subjected to microtensile bond strength (µTBS) testing. Fracture patterns and surface topography of each dentinal pretreatment were evaluated using a Scanning electron microscope (SEM). Bond strength data were analyzed using two-way ANOVA and Bonferroni post-hoc tests. Results: The group that received pretreatment with 5s APA and PhoA presented higher µTBS values among all groups, which was statistically different when compared with the PhoA, 10APA+PhoA, and 5APA+PhyA groups. PhyA did not significantly influence the bond strength of the air-abraded groups. Finally, adhesive failure was considered the predominant failure in all groups. Conclusion: Dentin pretreated by airborne particle abrasion using aluminum oxide demonstrated an increase in bond strength when abraded for 5 seconds and conditioned with phosphoric acid in a universal adhesive system.

RESUMO

To evaluate the feasibility of using a milled polyetheretherketone (PEEK) post and core in endodontically treated teeth with or without a ferrule. Sixty bovine tooth roots were endodontically treated followed by cementation of intraradicular retainers (IR), according to each experimental group: a) non-ferrule glass fiber post (f0FP); b) 2-mm-ferrule glass fiber post (f2FP); c) non-ferrule resized glass fiber post (f0PR); d) 2-mm-ferrule resized glass fiber post (f2PR); e) non-ferrule PEEK post and core (f0PPC); and f) 2-mm-ferrule PEEK post and core (f2PPC). Metal crowns were made and cemented. A periodontal ligament was simulated using polyether. A force was applied to the palatine portion of each sample at 45°, until fracture. Fracture resistance data were submitted to two-way ANOVA and Tukey's test (α = 0.05). Three-dimensional digital models were developed to calculate the tensions formed in the root using finite element analysis. Models of glass fiber posts and PEEK posts and cores were evaluated with or without a ferrule. The results were analyzed by the Mohr-Coulomb criterion. The type of IR was not influenced by fracture strength (p = 0.243). There were significant statistical differences among the remaining factors. Ferrule groups had greater fracture resistance, and the failure mode of teeth with a ferrule was more catastrophic than the non-ferrule group. A ferrule increases fracture resistance and influences failure mode; the PEEK post and core did not modify the biomechanics of endodontically treated teeth, and resembled the glass fiber post results. The crack initiation point differed between the ferrule and non-ferrule groups.

Assuntos

RESUMO

OBJETIVE: This study evaluated the influence of alveolar bone height and post type on compressive force resistance, fracture pattern, and stress distribution in endodontically treated teeth. MATERIALS AND METHODS: Bovine roots were endodontically treated and divided into eight groups (n = 10) according to alveolar bone height (normal alveolar bone and alveolar bone loss - 2 and 5 mm from the margin of the crown, respectively) and post type (prefabricated glass fiber post, anatomic glass fiber post, customized milled glass fiber post-and-core and customized milled polyetheretherketone (PEEK) post-and-core). Mechanical fatigue was simulated (300.000 cycles/50 N/1.2 Hz). Compression force resistance (N) was analyzed by two-way ANOVA and Tukey test (α = 0.05). Fracture patterns were described as percentages. Stress distribution was analyzed by finite element analysis. RESULTS: Significant diferences were found for alveolar bone height (P < 0.0001): normal alveolar bone groups showed higher mean values of compression force resistance compared to alveolar bone loss groups, while no significant differences were found for post type (P = 0.4551), and there was no double interaction between them (P = 0.5837). Reparable fractures were more predominant in normal alveolar bone groups, especially in the milled glass fiber and PEEK post-and-core groups. Stress distribution was similar in groups with prefabricated glass fiber posts and milled PEEK posts-and-cores, and the alveolar bone loss condition significantly increased stress concentration and strain values, mainly on apical dentin. CONCLUSIONS: Alveolar bone loss due to physiological aging and/or periodontal disease may lead to increased risk of restored tooth failure, although milled glass fiber and PEEK posts-and-cores provide more reparable fractures. CLINICAL SIGNIFICANCE: Custom-made glass fiber and PEEK post-and-cores are interesting options, since they enable clinicians to work with a single-body post-and-core system that avoid several materials interfaces and fits well in the root canal provided promising results to improve the failure behavior of restored roots, as they offer more reparable fractures even in situations of alveolar bone loss.

Assuntos

RESUMO

Abstract To evaluate the feasibility of using a milled polyetheretherketone (PEEK) post and core in endodontically treated teeth with or without a ferrule. Sixty bovine tooth roots were endodontically treated followed by cementation of intraradicular retainers (IR), according to each experimental group: a) non-ferrule glass fiber post (f0FP); b) 2-mm-ferrule glass fiber post (f2FP); c) non-ferrule resized glass fiber post (f0PR); d) 2-mm-ferrule resized glass fiber post (f2PR); e) non-ferrule PEEK post and core (f0PPC); and f) 2-mm-ferrule PEEK post and core (f2PPC). Metal crowns were made and cemented. A periodontal ligament was simulated using polyether. A force was applied to the palatine portion of each sample at 45°, until fracture. Fracture resistance data were submitted to two-way ANOVA and Tukey's test (α = 0.05). Three-dimensional digital models were developed to calculate the tensions formed in the root using finite element analysis. Models of glass fiber posts and PEEK posts and cores were evaluated with or without a ferrule. The results were analyzed by the Mohr-Coulomb criterion. The type of IR was not influenced by fracture strength (p = 0.243). There were significant statistical differences among the remaining factors. Ferrule groups had greater fracture resistance, and the failure mode of teeth with a ferrule was more catastrophic than the non-ferrule group. A ferrule increases fracture resistance and influences failure mode; the PEEK post and core did not modify the biomechanics of endodontically treated teeth, and resembled the glass fiber post results. The crack initiation point differed between the ferrule and non-ferrule groups.

RESUMO

ABSTRACT Tooth bleaching is one of the most conservative aesthetic techniques. At-home and in-office bleaching may be performed, as well as the combination of both techniques. As this combination may be done in different manners, distinct orders of combinations were proposed in this report. A 24 years-old man, whose upper central incisor and canine shades were A2 and A3 respectively, was initially treated by chair-side with 40-min application of 40% hydrogen peroxide (HP) for two sessions. Afterwards, an two-week overnight at-home bleaching was performed with 10% carbamide peroxide (CP). The shade of upper central incisors changed to 1M1 and canine was B1. Conversely, a 30 years-old woman was firstly conducted with at-home bleaching (overnight 4-weeks 10% CP) and, subsequently, with a single appointment of in-office bleaching for 45 minutes (35% HP). The shade of her upper central incisor changed from A1 to 0.5M1 and the upper canine from A3 to B1. The VITA classical (A1-D4) shade guide and VITA Bleached guide 3D-MASTER were used to determine the tooth color during the treatments. In both bleaching treatments, patients reported no significant tooth sensitivity and the final outcomes met their expectation.

RESUMO O clareamento dental é uma das técnicas estéticas mais conservadoras no âmbito odontológico. Técnicas de clareamento caseira ou de consultório, ou a combinação de ambas, podem ser realizadas para alcançar o prognóstico desejado. Esta combinação das técnicas pode ser realizada por meio de diferentes abordagens, como apresentado neste relato de casos. Um paciente do gênero masculino, 24 anos de idade, cujos incisivo central superior e caninos apresentaram cor A2 e A3, respectivamente, foi inicialmente submetido à técnica de clareamento de consultório de duração por sessão de 40 mim com gel de peróxido de hidrogênio (PH) 40%, em duas sessões. Posteriormente, a técnica de clareamento caseira foi realizada durante duas semanas com gel de peróxido de carbamida (PC) a uma concentração de 10%.A cor final dos incisivos centrais superiores foi alterada para 1M1, enquanto a dos caninos para B1. Por outro lado, uma paciente do gênero feminino, 30 anos de idade, foi inicialmente submetida ao clareamento caseiro (durante a noite, por 4 semanas- PC 10%), e subsequentemente, com aplicação pontual de agente clareador (PH 35%) em consultório, em sessão de 45 min. A cor do incisivo central superior da paciente, mudou de A1 para 0,5M1 e do canino superior de A3 para B1. As escalas de cor VITA Classic (A1-D4), e VITA Bleachedguided 3D-MASTER foram utilizadas nesta série de casos para determinar a coloração dos dentes durante os tratamentos. Em ambos os tratamentos, os pacientes não reportaram sensibilidade dental significante, e suas expectativas finais foram atendidas.

RESUMO

This in vitro study aimed to evaluate surface microhardness, roughness, color, gloss and topography of low-cost Brazilian resin composites, compared with an international one. All 120 samples (8mm ø x 2mm height) were prepared and divided into 5 groups: Ultrafill (Biodinâmica), Llis (FGM), Fill Magic (Coltene), Applic (Makira), and Filtek Z250XT (3M Oral Care). Surface microhardness (KHN) (n=10) was analyzed at two time periods: before and after simulated tooth brushing (STB). Other standardized samples of each group (n=10) were analyzed for surface roughness (Ra), color (ΔL, Δa, Δb, ΔE, ΔE00) and gloss unit (GU) at the same two periods. The topography of non-brushed and brushed samples of each group (n=4) was evaluated by scanning electron microscopy. Data were analyzed statistically by two-way repeated measures ANOVA with Bonferroni post-hoc test (KHN, Ra, GU), and one-way ANOVA with Tukey post-hoc test (ΔL, Δa, Δb, ΔE, ΔE00) (α=0.05). Topographic images were submitted to descriptive analysis. The low-cost Brazilian resin composites investigated were compared with the international one and revealed: lower KHN, regardless of before or after STB; statistically similar Ra before STB, except Ultrafill, which presented higher values; lower Ra after STB, except Ultrafill, which presented statistically similar values; statistically similar color change in ΔL, Δa, Δb parameters; statistically similar color change in ΔE, ΔE00 parameters, except Fill Magic, which presented lower values; lower gloss before STB; lower gloss after STB, except Ultrafill, which presented statistically similar values. In a situation of scarce resources, low-cost Brazilian composites might be an acceptable cost-effective restorative alternative.

Assuntos

RESUMO

Objective: This study aimed to evaluate the surface microhardness and morphology, as well as the microshear bond strength of a self-etching adhesive (Clearfil SE, Kuraray) to eroded dentin, exposed or not to cigarette smoke. Forty dental crowns were divided into 4 groups (n = 10): no treatment (control) (C); erosion (E); erosion + cigarette smoke exposure (ES); cigarette smoke exposure (S). Samples were prepared through third molars polishing until dentin exposure, followed by crown section. Erosive cycles were performed 5 times/day for 30 s at 60 min intervals. Cigarette smoke was produced with twenty cigarettes/day, during 5 days. Microhardness was evaluated initially and after the treatments. Microshear bond strength was tested after the treatments and dentin restoration with flow composite. Failure patterns and dentin morphology was evaluated by Scanning Electron Microscopy. Microshear bond strength data was submitted to two-way ANOVA, microharness test was adjusted by gamma distribution to be a non-parametric analyses (p=0.05), and surface morphology as qualitative analyses. Loss percentage of microhardness was observed only in groups submitted to erosion. Bond strength was statistically similar between all groups. The most prevalent failure pattern was of adhesive type. Morphological analysis of dentin showed obliterated tubules in groups submitted to cigarette smoke exposure. Cigarette smoke exposure did not promote any effect in the percentage of microhardness loss, as in sound dentin as in eroded dentin. Cigarette smoke, erosion, and association of both, did not alter the bond strength of self-etching adhesives to dentin. (AU)

Objetivo: Este estudo teve como objetivo avaliar a microdureza (% perda de dureza) e morfologia de superfície (MS), assim como a resistência de união (RU) de um adesivo autocondicionante (Clearfil SE, Kuraray) à uma dentina erodida, exposta ou não à fumaça de cigarro. Material e Métodos: Quarenta coroas dentais de terceiros molares foram seccionadas da raiz e polidas até a exposição dentinária, sendo aleatoriamente divididas em 4 grupos (n=10): sem tratamento (controle), erosão (E), erosão+ exposição a fumaça de cigarro (ES); exposição a fumaça de cigarro (S).O ciclo erosivo foi realizado 5 vezes/dia por 30s, com 60 minutos de intervalo entre eles. Os grupos ES e S foram exposto à fumaça de cigarro produzida por 20 cigarros/dia, durante 5 dias. A avaliação da microdureza foi realizada antes e após os tratamentos, enquanto a resistência da união por microcisalhamento foi realizada após os tratamentos Os padrões de fratura representativos e a MS dentinária foram avaliados por microscopia eletrônica de varredura (MEV). Os dados de RU foram analisados por ANOVA dois fatores, enquanto a análise de microdureza foi ajustada por distribuição gama por ser uma análise não-paramétrica (p=0.05). A MS foi analisada qualitativamente. Resultados: Os grupos expostos aos ciclos erosivos (E e ES) apresentaram % de perda de dureza significativamente menor que os grupos não expostos (Controle e S. aos ciclos erosivos (E e ES). Para RU, não houve diferença estatística significativa entre os grupos. O padrão de fratura mais observado foi do tipo adesivo, e através das imagens obtidas por MEV, observou-se a obliteração de túbulos dentinários no grupo exposto à fumaça de cigarro, enquanto os grupos submetidos aos ciclos erosivos (E e ES) apresentaram maior exposição e diâmetro de túbulos dentinários. Conclusão: A exposição à fumaça de cigarro não promove nenhum efeito quanto a perda de porcentagem de dureza dentinária, assim como em dentina erodida e saudável. A fumaça de cigarro, o processo erosivo, e a associação de ambos, não altera a resistência da união de adesivos autocondicionantes à dentina. (AU)

Assuntos