RESUMO
In this paper, we discuss the creation of a hybrid magnetorheological elastomer that combines nano- and microparticles. The mixture contained 45 wt.% fillers, with combinations of either 0% nanoparticles and 100% microparticles or 25% nanoparticles and 75% microparticles. TGA and FTIR testing confirmed the materials' thermal and chemical stability, while an SEM analysis determined the particles' size and morphology. XRD results were used to determine the crystal size of both nano- and microparticles. The addition of reinforcing particles, particularly nanoparticles, enhanced the stiffness of the composite materials studied, but their overall strength was only minimally affected. The computed interaction parameter relative to the volume fraction was consistent with the previous literature. Furthermore, the study observed a magnetic response increment in composite materials reinforced with nanoparticles above 30 Hz. The isotropic material containing only microparticles had a lower storage modulus than the isotropic sample with nanoparticles without a magnetic field. However, when a magnetic field was applied, the material with only microparticles exhibited a higher storage modulus than the samples with nanoparticles.
RESUMO
In this study, a piezoelectric harvesting device was developed using polyvinylidene fluoride (PVDF) nanofibers reinforced with either BaTiO3 nanoparticles or graphene powder. BaTiO3 nanoparticles were synthesized through the sol-gel method with an average size of approximately 32 nm. The PVDF nanofibers, along with the nanoparticle composites in an acetone-N,N-dimethylformamide mixture, were produced using a centrifugal Forcespinning™ machine, resulting in a heterogeneous arrangement of fiber meshes, with an average diameter of 1.6 µm. Experimental tests revealed that the electrical performance of the fabricated harvester reached a maximum value of 35.8 Voc, demonstrating the potential of BaTiO3/ PVDF-based piezoelectric devices for designing wearable applications such as body-sensing and energy-harvesting devices.
RESUMO
Opuntia ficus-indica (L.) Mill (OFI) is considered a natural source of bioactive phytochemicals, mainly isorhamnetin glycosides (IRGs). These compounds have demonstrated antioxidant, anti-inflammatory, and anticancer activities, among others. The development of a suitable delivery system for these compounds is needed to improve their chemical and biological stability. This study aimed to evaluate the feasibility of fabrication and characterization of IRG-loaded gelatin (GL) forcespun fibers and crosslinking with glutaraldehyde (GTA). Two different percentages (25% and 30% w/v) of GL were evaluated with 12% (w/v) OFI flour to obtain nanofibers GL/OFI1 and GL/OFI2, respectively. The morphology and physicochemical properties of the fibers were investigated. The results indicated that the diameters of the fibers were on the nanoscale. The amount of IRGs was determined using high-performance liquid chromatography (HPLC). The IRGs release and the cytocompatibility of the nanofibers were also evaluated. GL concentration significantly affected the IRG release. Among both nanofibers, the GL/OFI2 nanofiber achieved a cumulative IRGs release of 63% after 72 h. Both fibers were shown to be biocompatible with human skin/fibroblast cells. Specifically, GL/OFI1 nanofibers exhibited favorable features for their application as an extract-coupled release system. The IRGs-embedded GL nanofiber mats may become a good alternative for the delivery of phytochemicals for the health sector and biomedical applications.
RESUMO
This paper focuses on developing, fabricating, and characterizing composite polycaprolactone (PCL) membranes reinforced with titanium dioxide nanoparticles (NPs) elaborated by using two solvents; acetic acid and a mixture of chloroform and N,N-dimethylformamide (DMF). The resulting physical, chemical, and mechanical properties of the composite materials are studied by using experimental characterization techniques such as scanning electron microscopy (SEM), differential scanning calorimetry (DSC), X-Ray diffraction (XRD), Fourier-transform infrared (FTIR) analysis, contact angle (CA), uniaxial and biaxial tensile tests, and surface roughness measurements. Experimental results show that the composite material synthesized by sol-gel and chloroform-DMF has a better performance than the one obtained by using acetic acid as a solvent.