RESUMO
The magnetism of Co-Rh nanoparticles is investigated experimentally and theoretically. The particles (approximately 2 nm) have been synthesized by decomposition of organometallic precursors in mild conditions of pressure and temperature, under hydrogen atmosphere and in the presence of a polymer matrix. The magnetic properties are determined by SQUID, Mössbauer spectroscopy, and X-ray magnetic circular dichroism (XMCD). The structural and chemical properties are characterized by wide angle X-ray scattering, transmission electronic microscopy and X-ray absorption near edge spectroscopy. All the studied Co-Rh clusters are magnetic with an average spin moment per atom mu that is larger than the one of macroscopic crystals or alloys with similar concentrations. The experimental results and comparison with theory suggest that the most likely chemical arrangement is a Rh core, with a Co-rich outer shell showing significant Co-Rh mixing at the interface. Measured and calculated magnetic anisotropy energies (MAEs) are found to be higher than in pure Co clusters. Moreover, one observes that the MAEs can be tuned to some extent by varying the Rh concentration. These trends are well accounted for by theory, which in addition reveals important spin and orbital moments induced at the Rh atoms as well as significant orbital moments at the Co atoms. These play a central role in the interpretation of experimental data as a function of Co-Rh content. A more detailed analysis from a local perspective shows that the orbital and spin moments at the Co-Rh interface are largely responsible for the enhancement of the magnetic moments and magnetic anisotropy.
RESUMO
The synthesis and characterization of molybdenum colloidal particles were evaluated using thermal and sonochemical methods and starting from different metal precursors, Mo(CO)6 and (NH4)2MoS4. The products were characterized by elemental analysis, spectroscopic (UV, FTIR), and surface analysis (XPS) techniques, as well as by transmission electron microscopy (TEM) for determining the particle sizes. Using Mo(CO)6 as metal source, particle sizes with an average diameter of 1.5 nm can be obtained using tert-amyl alcohol as solvent and tetrahydrothiophene as sulfurating ligand. The characterization of these particles showed that they are composed of molybdenum oxide MoO3. Using (NH4)2MoS4 as metal precursor, particles with average diameters of 4.7 and 2.5 nm were synthesized using thermal and sonochemical methods, respectively. The characterization of these particles showed them to be composed of molybdenum sulfide, MoS2. The sonochemical method proved to be the fastest and most convenient synthetic pathway of obtaining small colloidal particles at low temperatures and with control of the average size. Copyright 1998 Academic Press.