In the present work, multiple-wall carbon nanotubes (MWCNTs) were surface modified in an environmentally friendly way, using low-frequency ultrasonic energy. This type of modification was carried-out using two different types of organic acids, citric acid (CA) and oxalic acid (OA). The modification of the MWCNTs was confirmed by Fourier-transform infrared spectroscopy (FTIR), where functional groups such as OH, C=O, O-C=O and COOH were detected. By means of Raman spectroscopy, an increase in carbon surface defects was found. On the other hand, using X-ray photoelectron spectroscopy (XPS), oxidation was evidenced on the surface of the modified MWCNT. In both Raman spectroscopy and XPS, the results indicate a greater modification when CA is used, possibly due to the fact that CA has a larger number of functional groups. MWCNT-CA showed good dispersion in methanol, while MWCNT-OA showed good stability in methanol and ethanol. Finally, a 20% removal of creatinine efficiency improvement was found with respect to the unmodified MWCNTs, while no improvement was found in the case of urea and uric acid.
RESUMO
Automotive and industrial design companies have profusely used commodity materials like glass fiber-reinforced polypropylene. These materials show advantageous ratios between cost and mechanical properties, but poor environmental yields. Natural fibers have been tested as replacements of glass fibers, obtaining noticeable tensile strengths, but being unable to reach the strength of glass fiber-reinforced composites. In this paper, polyamide 6 is proposed as a matrix for cellulosic fiber-based composites. A variety of fibers were tensile tested, in order to evaluate the creation of a strong interphase. The results show that, with a bleached hardwood fiber-reinforced polyamide 6 composite, it is possible to obtain tensile strengths higher than glass-fiber-reinforced polyolefin. The obtained composites show the existence of a strong interphase, allowing us to take advantage of the strengthening capabilities of such cellulosic reinforcements. These materials show advantageous mechanical properties, while being recyclable and partially renewable.