RESUMO

OBJECTIVE: To evaluate the fracture behavior of human molars with extensive MOD restorations using short-fiber-reinforced resin composite of varying viscosities. MATERIALS AND METHODS: Human molars were randomly divided into seven groups (n = 12): intact teeth (control); restoration using conventional high-viscosity resin composite without (Filtek Z350XT, 3M) or with fibers (everX Posterior, GC); conventional low-viscosity resin composite without (Filtek Supreme Flowable, 3M) or with fibers (everX Flow Dentin Shade, GC); bulk-fill low-viscosity resin composite (Filtek Bulk Fill Flow, 3M) or with fibers (everX Flow Bulk Shade, GC). Restorations were performed on extensive MOD preparations, following the manufacturers' recommendations for each material. Specimens underwent fracture strength testing (N) and fracture pattern (%) categorized as repairable, possibly repairable, or non-repairable. Results were analyzed using a generalized linear model (N) and Fisher's exact test (%), with α = 0.05. RESULTS: Restorations performed with high-viscosity materials showed fracture strength values similar to the control and higher than those of restorations using low-viscosity resin composites (p < 0.0001), except for the bulk-fill low-viscosity resin composite with fibers (p > 0.05). Teeth restored using low-viscosity resin composite with fibers showed a higher % of repairable and possibly repairable fractures than the control (p = 0.0091). CONCLUSIONS: The viscosity of materials mediated the fracture strength, with restorations using high-viscosity resin composites promoting values similar to the intact tooth; however, the presence of fibers influenced the fracture pattern. CLINICAL SIGNIFICANCE: Teeth with MOD cavities restored with high-viscosity resin composites showed similar fracture strength to intact teeth. Fiber-reinforced low-viscosity resin composite for the base of restoration resulted in a more repairable/possibly repairable fracture pattern.

Assuntos

RESUMO

OBJECTIVE: Evaluate the penetration of hydrogen peroxide (HP) into the pulp chamber, bleaching efficacy (BE) and amount of gel expended during in-office bleaching using an applicator brush tip and conventional tip from different commercial brands. MATERIALS AND METHODS: 104 human premolars were randomly distributed into thirteen groups (n = 8) according to the commercial brand: DSP White Clinic 35 % Calcium (DW), Nano White 35 % (NW), Total Blanc One-Step 35 % (TS), Whiteness HP Blue 35 % (WB), Potenza Bianco Pro SS 38 % (PB), Opalescence XTra Boost 40 % (OB), no bleaching (negative control), and application method: applicator brush tip and conventional tip for all groups. Initial HP concentration (%) was determined via titration and pH was measured with digital pH meter. Concentration (µg/mL) of HP into the pulp chamber was measured using UV-Vis spectrophotometry, the BE (ΔE*ab, ΔE00 and ΔWID) was evaluated with a digital spectrophotometer, and the amount of gel expended was evaluated using a precision analytical digital balance. Statistical analysis included two-way ANOVA, Tukey's, and Dunnett's test. Comparison between HP into the pulp chamber vs BE was performed with Person's correlation (α = 0.05). RESULTS: Brush tip demonstrated a low amount of HP in the pulp chamber compared to the conventional method for all bleaching gels (p < 0.0003), as well as lower amount of gel expended (p < 0.002). The brush tip did not result in a significant difference in BE compared to the conventional (p > 0.05). No correlations were found between both factors (p > 0.05). CONCLUSION: Brush tip showed lower penetration of HP in the pulp chamber and a reduced volume of spent gel when compared to the conventional tip, for all commercial brands. CLINICAL RELEVANCE: Brush tip is recommended for bleaching gels in an attachable syringe due to its ability to reduce the penetration of HP into the pulp chamber and minimize the amount of bleaching gel used.

Assuntos

RESUMO

This study evaluated the stress distribution on an implant-supported zirconia crown of a mandibular first molar subjected to oblique loading by occlusal contact with the natural maxillary first molar by using the 3D finite element method. Two virtual models were made to simulate the following situations: (1) occlusion between maxillary and mandibular natural first molars; (2) occlusion between zirconia implant-supported ceramic crown on a mandibular first molar and maxillary natural first molar. The models were designed virtually in a modeling program or CAD (Computer Aided Design) (Rhinoceros). An oblique load of 100 N was uniformly applied to the zirconia framework of the crown. The results were obtained by the Von Mises criterion of stress distribution. Replacement of the mandibular tooth by an implant caused a slight increase in stress on portions of the maxillary tooth roots. The crown of the maxillary model in occlusion with natural antagonist tooth showed 12% less stress when compared with the maxillary (model in occlusion with the) implant-supported crown. The mandibular crown of the implant show 35% more stress when compared with the mandibular antagonist crown on the natural tooth. The presence of the implant to replace the mandibular tooth increased the stresses on the maxillary tooth, especially in the region of the mesial and distal buccal roots.

Assuntos

RESUMO

Aim: The aim of this study was to investigate the impact of pretreatment with ethanolic solutions of caffeic acid phenethyl ester (CAPE) at varying concentrations on the dentin collagen matrix, specifically focusing on its biomodification potential. This was assessed through evaluations of the modulus of elasticity and changes in mass. Methods: Seventy dentin collagen matrices (demineralized sticks) were prepared to receive treatments with ethanolic solutions of CAPE at concentrations of 0.05%, 0.1%, 0.5%, or 2.5%, or with control treatment solutions (distilled water or ethanol) for one hour. The dentin matrices were evaluated for modulus of elasticity and mass before (baseline), immediately after treatment (immediately), and after storage in Simulated Body Fluid (SBF) for time intervals of 1 and 3 months. Results: Generalized linear models for repeated measures over time indicated no significant differences between groups (p=0.7530) or between different time points (p=0.4780) in terms of the modulus of elasticity. Regarding mass variation, no differences were observed in the time interval between 1 month and the immediate time (p=0.0935). However, at the 3-month mark compared to the immediate time, the 0.1% CAPE group exhibited less mass loss compared to the water group (p=0.0134). Conclusion: This study concludes that various concentrations of CAPE in an ethanolic solution did not affect the modulus of elasticity of dentin, suggesting that CAPE lacks biomodifying potential in this context. However, it was observed that 0.1% CAPE positively influenced the variation in mass over different evaluation time intervals

Assuntos

RESUMO

BACKGROUND: The effectiveness of in-office bleaching protocols performed with violet LED light either combined with a bleaching agent containing 37% carbamide peroxide, or not, was determined by comparing teeth with different degrees of darkening. METHODOLOGY: Eighty bovine incisors were separated into groups of "light" teeth (luminosity greater than or equal to B3) and "dark" teeth (less than or equal to A3.5) to receive the protocols: HP - 35% hydrogen peroxide (Whiteness HP), CP - 37% carbamide peroxide (Whiteness SuperEndo), LED - violet LED light (Bright Max Whitening), CPLED - CP associated with the LED. For color analysis the CIEL*a*b* e WID, ΔEab, ΔE00 e ΔWID parameters were used. Data were analyzed using Mann-Whitney, Kruskal-Wallis, Dunn, Friedman or Nemenyi tests (α = 5%). RESULTS: HP and CP resulted in similar color change values (ΔEab, ΔE00 e ΔWID) for light and dark teeth (p > 0.05). Dark teeth showed better bleaching effectiveness (ΔEab, ΔE00 e ΔWID) than light teeth when CPLED was used (p < 0.05). LED showed color change that were below the limits of acceptability and perceptibility for ΔWID. CONCLUSION: light teeth are effectively bleached with the use of HP or CP, whereas dark teeth respond better to treatment with the CPLED protocol. Violet LED used alone did not show a satisfactory result.

Assuntos

RESUMO

BACKGROUND: The effectiveness of dental color change was assessed by incorporating titanium dioxide (TiO2) into 37% carbamide peroxide bleaching agent associated with hybrid light. METHODOLOGY: Fifty bovine incisors were selected to receive the bleaching treatment, and separated into five groups (n = 10): 35% hydrogen peroxide (HP) (Whiteness HP, FGM/HP); 37% carbamide peroxide (CP) (Whiteness SuperEndo, FGM/CP); CP + hybrid light (HL) (CP HL); CP + 1% TiO2 (CP TiO2); CP TiO2 + hybrid light (CP TiO2 HL). The bleaching gels were applied to the dental surface for 30 min. Hybrid light (Whitening Plus, DMC/infrared laser diodes + blue LEDs +violet LEDs) was applied with 1 min of active light, alternating with 1 min of pause. A spectrophotometer (VITA Easyshade® Advance, Vita) was used to determine the color of the dental elements at baseline and time points after the 1st, 2nd and 3rd bleaching sessions. Color change effectiveness was evaluated using Vita Classical, CIEL*a*b*, WID and ΔEab, ΔE00 and ΔWID parameters. RESULTS: Generalized mixed linear models for repeated measures (α = 5%) showed significant decrease in Vita Classical scores and a* and b* values, as well as an increase in L* and ∆WID values for all the groups. Higher color change values for ΔEab were observed for CP HL and CP TiO2 HL, while those of ΔE00 and ΔWID were higher for CP TiO2 HL at the end of the bleaching treatment. CONCLUSION: Hybrid light applied with TiO2 incorporated into CP potentiated the effectiveness of the color change in the tooth structure.

Assuntos

RESUMO

BACKGROUND: Dental color change and the temperature of the pulp chamber and of the buccal surface were evaluated during bleaching with 37% carbamide peroxide (CP) with continuous vs fractionated violet LED light protocols. METHODOLOGY: Bovine incisors received in-office bleaching for 30 min using different light protocols (Bright Max Whitening, MMOptics). Teeth were separated into groups (n = 10): HP) 35% hydrogen peroxide (Whiteness HP, FGM)/no light; CP) 37% carbamide peroxide (Whiteness SuperEndo, FGM)/no light; CP10) CP+10 min of continuous light; CP20) CP+20 min of continuous light; CP30) CP+30 min of continuous light; CPF) CP+20 cycles of 60 s light / 30 s no light (fractionated). Color evaluations were performed at different times. Evaluations of pulp and buccal surface temperatures were performed before and throughout the 30 min of bleaching. RESULTS: Generalized linear models for repeated measures over time were applied to the data (α=5%). After the 1st session, CP20 and CP30 had significantly lower b* values ​​than CP and CP10 (p = 0.0071). For ΔEab and ΔE00, CPF, CP20 and CP30 showed the highest color change among the treatments after the third bleaching (p<0.05). For temperature evaluations, CP30 showed higher pulp and buccal surface temperatures than the other protocols (p<0.0001) after 20 min. CONCLUSION: Fractionated or continuous application of violet LED for 20 or 30 min leads to greater effectiveness of color change. All protocols with the application of LED led to an increase in pulp and buccal surface temperatures during bleaching, although the fractionated application appeared to be safer than the use of continuous light.

Assuntos

RESUMO

This study aimed to evaluate the effect of endodontic sealer (ES) on bond strength (BS) of prefabricated or milled-CAD-CAM (computer-aided design and computer-aided manufacturing) glass-fiber-posts (GFP). Canals of 90 single-rooted teeth were prepared for filling by the single-cone technique with gutta-percha and one of the following ES: AH Plus (epoxy resin), Endofill (zinc-oxide and eugenol), and Bio-C Sealer (calcium-silicate). After post-space preparation, tooth-specimens were equally divided in half according to type of GFP to be used. In the half to receive milled-CAD-CAM posts, tooth specimens were molded with acrylic resin to obtain replicas. These were scanned to enable the laboratory to produce the milled-CAD-CAM GFPs (Fiber CAD Lab, Angelus) by the subtractive technique. The other half of samples received prefabricated GFPs (Exacto, Angelus) (n=15). The GFPs were cemented with dual-cure resin cement (Panavia F2.0, Kuraray). Each root was sectioned into two slices per root region (cervical, middle, apical) that were subjected to the push-out BS test, in a universal testing machine. Failure mode (FM) was classified by scores. The BS data were submitted to generalized linear model analyses, while FM was analyzed using the chi-square test (a=0.05). BS showed no significant difference among the three ES (p > 0.05). BS was significantly higher for prefabricated (mean 10.84 MPa) versus milled-CAD-CAM GFPs (mean 6.94 MPa) (p <0.0001), irrespective of ES. The majority showed mixed failures. It could be concluded that type of ES did not affect BS of GFPs to dentin, and prefabricated-GFPs had higher bond-strength than customized-milled-CAD-CAM GFPs.

Assuntos

RESUMO

Background: Greater degradation of the hybrid layer is expected when a universal adhesive system is used, especially in the conventional application strategy. Therefore, it would important to evaluate the effect of the ethanol (ETH) and a potential matrix protease inhibitor (caffeic acid phenethyl ester/ CAPE) to maximize the ability to achieve stable dentin bond strength. The aim of this study was to evaluated the effect of ETH on a wet-bonding technique, and dentin pretreatments with different concentrations of CAPE in ethanolic solution, followed by application of a universal adhesive system (Single Bond Universal) to inhibit proteolytic activity. Material and Methods: Dentin blocks were allocated to eight experimental groups according to the strategy (total-etch our self-etch) and treatments: ETH, or dentin pretreatment with CAPE (at 0.5%, 2.5%; and 5.0%). Half of each block (each hemiblock) served as the control (without dentin pretreatments) for the same group. The bonding strategy was performed (adhesive system/ restoration with composite resin). Two slices were obtained from each hemiblock and evaluated using in situ zymography. The proteolytic activity was analyzed by quantifying the green photons of the images obtained under a fluorescence microscope in three dentin locations close to the dentin-resin interface: hybrid layer (HL), underlying dentin (UD) and deep dentin (DD). Results: Wilcoxon tests (for comparison between experimental and control groups) and Friedman and Nemenyi tests (for comparisons between interface locations) showed that there was no difference between the groups with different CAPE concentrations and the respective control groups (p>0.05). ETH reduced the proteolytic activity at the HL and UD (p<0.05). Conclusions: The wet-bonding technique with ETH proved effective in reducing the proteolytic activity. The use of CAPE in different concentrations solubilized in ethanol did not have a favorable effect on proteolytic inhibition. Key words:Adhesives, Hybrid layer, Dentin, Metalloproteinases.

RESUMO

This study characterized TiO2 nanotube (TiO2-nt) ultrastructure and morphology, and the physicochemical impact on high-viscosity conventional glass-ionomer cement (GIC). TiO2-nt was synthesized by the alkaline method (n = 3), assessed by scanning (SEM) and transmission electron microscope (TEM), and was added (3%, 5%, 7%-in weight) to KM (Ketac Molar EasyMix™). Analyses included: SEM; Energy-dispersive spectroscopy (EDS); Raman spectroscopy (RAMAN); Setting time with Gillmore needles (ST); Color (Co); Radiopacity (XR); Water sorption (WS); and solubility (SO). Quantitative data were submitted to ANOVA and Tukey's tests (chr = 0.05). External and internal TiO2-nt diameters were 11 ± 2 nm and 6 ± 0 nm, respectively. Data analyses showed: (i) TiO2-nt present into KM matrix, with a concentration-dependent increase of Ti levels into KM, (ii) physical interaction between KM and TiO2-nt, (iii) longer initial ST for the 7% group compared to KM and 3% groups (p ≤ 0.01), (iv) decreased luminosity and yellowness for the 5% and 7% groups, (v) 36% greater radiopacity for the 5% group compared to enamel, dentin, and KM, and (vi) lower SO values for the 5% group, with no significant differences on WS across the groups. TiO2-nt displayed physical interaction with KM matrix, and also modified SO, XR and Co, without affecting ST. This study provides information on the potential impact of TiO2-nt on GIC performance. TiO2-nt may be proposed to boost confidence among dental surgeons in terms of GIC's handling characteristics, success rate and differential diagnostic.

Assuntos

RESUMO

OBJECTIVES: To evaluate the effect of acid erosion on different physical properties of resin composite with S-PRG (surface pre-reacted glass) fillers, by conducting simulations of intrinsic and extrinsic sources. MATERIALS AND METHODS: Cylindrical samples (Ø6 vs. 2 mm) of a conventional nanohybrid resin composite (Forma, Ultradent) and of a nanohybrid resin composite with S-PRG filler (Beautifil II, Shofu) were exposed to erosive cycling (5 days), based on (n=12) remineralizing solution (control); 0.3% citric acid (pH=2.6); or 0.01 M hydrochloric acid (pH=2). Roughness (Ra), microhardness (KHN), and color (CIEL*a*b*, CIEDE2000, and Vita scale (SGU)) factors were analyzed at the initial and final time points, and the general color changes (ΔEab, ΔE00, ΔSGU) were calculated. Final images were obtained using scanning electron microscopy (SEM). The data were evaluated by generalized models, Mann-Whitney, Wilcoxon, Kruskal-Wallis, and Dunn tests (α=0.05). RESULTS: Regarding KHN, there was no difference between the groups or the time periods (p = 0.74). As for Ra, there was a significant increase in the Ra of both composites after cycling with hydrochloric acid, but only the resin composite with S-PRG filler showed a change in Ra after cycling with citric acid (p = 0.003). After cycling with citric and hydrochloric acid, the highest Ra values were found for the resin composite with S-PRG filler (p < 0.0001), corroborating the result of images (SEM) indicating loss of filler and porosities in this material. The resin composite with S-PRG filler showed higher ΔEab and ΔE00, in addition to more negative ΔSGU values and lower L* values after exposure to both acids, compared to the control (p < 0.05). CONCLUSION: The acidic conditions altered the roughness and color stability of the materials tested, pointing out that the resin composite containing S-PRG filler showed greater degradation of its physical properties than the conventional resin composite. CLINICAL RELEVANCE: Bioactive materials are relevant, considering that their properties interact with dental hard tissues; however, the S-PRG-based resin composite showed greater degradation under acidic conditions than the conventional resin composite.

Assuntos

RESUMO

BACKGROUND: The purpose of this study was: 1) to analyze the physical-chemical properties of hydrogen peroxide (HP) agents at 7.5% (HP7) and 35% (HP35), and the association with or without TiO2 nanotubes; 2) to evaluate dental bleaching effectiveness by using HP7 and HP35 together with or without TiO2 nanotubes, and applied with or without violet LED (VL). METHODOLOGY: 80 bovine incisors were treated according to groups (n = 10): HP35; HP35 + VL; HP35T (HP35 + TiO2); HP35T + VL; HP7; HP7 + VL; HP7T (HP7 + TiO2); HP7T + VL. Bleaching effectiveness was measured at 4 time points according to the Vita Classical, CIEL*a*b*, CIEDE2000, and WID parameters. HP35, HP35T, HP7, and HP7T were evaluated for mass change, pH, mean particle size (P), polydispersity (PDI), and zeta potential (ZP), over 6 months of storage. RESULTS: The pH of HP35 thickener was higher when associated to TiO2. At baseline, both of the bleaching gels containing TiO2 had lower P, PDI, and PZ (p < 0.05). All groups showed a significant decrease in Vita Classical color scores (p = 0.0037). There was a higher L* value, and lower b* values for HP7 when associated to VL after the 3rd session. (p < 0.05). HP35T showed higher color change (ΔEab, ΔE00), and lower a* value in the presence of VL (p < 0.05). ΔWID presented lower values for both gels, when TiO2 was incorporated (p ≤ 0.05). CONCLUSION: The incorporation of TiO2 to the bleaching gel showed good stability with minimal variations in physical-chemical properties. The color change in HP35 was more effective than in HP7, but the VL boosted the bleaching effectiveness of HP7, whereas TiO2 did not increase bleaching effectiveness.

Assuntos

RESUMO

OBJECTIVES: The effects of different concentrations of titanium dioxide (TiO2) into 40% hydrogen peroxide (HP) were evaluated as regards the effectiveness of dental color change either associated with activation by polywave LED light or not. MATERIALS AND METHODS: TiO2 (0, 1, 5, or 10%) was incorporated into HP to be applied during in-office bleaching (3 sessions/40 min each). Polywave LED light (Valo Corded/Ultradent) was applied or not in activation cycles of 15 s (total time of 2 min). The color of 80 third molars separated into groups according to TiO2 concentration and light activation (n = 10) was evaluated at baseline and at time intervals after the 1st, 2nd, and 3rd bleaching sessions. RESULTS: WID value was significantly higher when using HP with 5% TiO2 in the 2nd session than the values in the other groups (p < 0.05). After the 2nd and 3rd sessions, the ΔEab value was significantly higher when activated with light (p < 0.05) for all agents containing TiO2 or not. Zeta potential and pH of the agents were not modified by incorporating TiO2 at the different concentrations. CONCLUSIONS: The 5% TiO2 in the bleaching agent could enhance tooth bleaching, even without light application. Association with polywave LED light potentiated the color change, irrespective of the presence of TiO2 in the bleaching gel. CLINICAL SIGNIFICANCE: HP with 5% TiO2 could lead to a greater tooth bleaching response in the 2nd clinical session, as well as the polywave light can enhance color change.

Assuntos

RESUMO

Resumo Proposição: avaliar in vitro a rugosidade superficial de fios ortodônticos antes e após a compressão com pinças ortodônticas. Material E Métodos: 30 fios 0,014" de níckel-titânio termoativados (Neosentalloy, GAC) e 30 fios 0,019 x 0,025" de aço foram usados nos experimentos. Avaliou-se a rugosidade superficial com rugosímetro (NewViewTM 7100, Zygo), antes e após a compressão com alicate Weingart do lado esquerdo e pinça Mathieu do lado direito (Dentaurum). Foram determinados os parâmetros de rugosidade Ra (µm), Rq (µm), PV (µm), Srmax Iso (nm). Testes estat´siticos Wilcoxon foram realizados para analisar a variação dos parâmetros da rugosidade com nível de confiança de 95% e p<0,05. Resultados: Os fios redondos de NiTi apresentaram diferenças significaticas dos parâmetros Ra e Rq antes e após a compressão com pinça Mathieu. O emprego do alicate Weingart não alterou a rugosidade dos fios redondos. Os fios retangulares apresentaram diferenças significativas em todos os parâmetros com uso das duas pinças. As médias das diferenças dos parâmetros entre o alicate Weingart e a pinça Mathieu nos fios redondos, não foram estatisticamente significativos. Os fios retangulares apresentaram maior rugosidade com o emprego do alicate Weingart, com diferenças significativas. Conclusão: O uso do alicate tipo Weingart e da pinça tipo Mathieu aumentam a rugosidade dos fios de NiTi e de aço (AU)

Abstract Proposition: the surface roughness of orthodontic wires was evaluated in vitro before and after gripping with two different orthodontic pliers. Material And Methods: Units were made of 30 round heat-activated Nickel Titanium alloy wires 0,014" (Neosentalloy, GAC), and another group with 30 rectangular steel wires 0,019 x 0,025". The surface roughness was evaluated with a rugosimeter (NewViewTM 7100, Zygo), before and after gripping with Weingart plier on the left side and Mathieu plier on the right side (Dentaurum), in addition to the average difference in roughness between groups of the same types of wires with parameters Ra (µm), Rq (µm), PV (µm), Srmax Iso (nm). The variation of parameters with different clamps was evaluated (Wilcoxon test); different alloys by the same clamp, 95% confidence level and p<0.05. Results: The round wires showed significant differences (Ra and Rq) before and after being gripped with Mathieu plier. The roughness was higher after being gripped. Weingart pliers and round wires obtained the same results, with greater roughness after being clamped. Rectangular wires showed significant differences in all parameters, with both clamps. The means of the differences in the parameters between the Weingart pliers and the Mathieu forceps on the round wires were not statistically significant. In the rectangular wire, the values between the tweezers showed greater roughness with the grip of the Weingart pliers, with significant differences.Conclusion: After securing the orthodontic wires, the Weingart pliers and the Mathieu tweezers increased the roughness parameters (AU)

Assuntos

RESUMO

Abstract This study aimed to evaluate the effect of endodontic sealer (ES) on bond strength (BS) of prefabricated or milled-CAD-CAM (computer-aided design and computer-aided manufacturing) glass-fiber-posts (GFP). Canals of 90 single-rooted teeth were prepared for filling by the single-cone technique with gutta-percha and one of the following ES: AH Plus (epoxy resin), Endofill (zinc-oxide and eugenol), and Bio-C Sealer (calcium-silicate). After post-space preparation, tooth-specimens were equally divided in half according to type of GFP to be used. In the half to receive milled-CAD-CAM posts, tooth specimens were molded with acrylic resin to obtain replicas. These were scanned to enable the laboratory to produce the milled-CAD-CAM GFPs (Fiber CAD Lab, Angelus) by the subtractive technique. The other half of samples received prefabricated GFPs (Exacto, Angelus) (n=15). The GFPs were cemented with dual-cure resin cement (Panavia F2.0, Kuraray). Each root was sectioned into two slices per root region (cervical, middle, apical) that were subjected to the push-out BS test, in a universal testing machine. Failure mode (FM) was classified by scores. The BS data were submitted to generalized linear model analyses, while FM was analyzed using the chi-square test (a=0.05). BS showed no significant difference among the three ES (p > 0.05). BS was significantly higher for prefabricated (mean 10.84 MPa) versus milled-CAD-CAM GFPs (mean 6.94 MPa) (p <0.0001), irrespective of ES. The majority showed mixed failures. It could be concluded that type of ES did not affect BS of GFPs to dentin, and prefabricated-GFPs had higher bond-strength than customized-milled-CAD-CAM GFPs.

RESUMO

Aim: To evaluate the occlusal and internal marginal adaptation of inlay restorations made of different materials, using CAD-CAM. Methods: Preparations were made for MOD inlays of one-third intercuspal width and 4 mm depth in 30 third human molars. The teeth were restored using CAD-CAM materials (n=10) of nanoceramic resin (Lava Ultimate), polymer-infiltrated ceramic network (VITA ENAMIC), or lithium disilicate glass-ceramic (IPS e.max CAD). The specimens were cemented with dual resin cement and sectioned at the center of the restoration, after which the two halves were evaluated, and photographed The occlusal and internal discrepancy (µm) was determined at five points: cavosurface angle of the occlusal-facial wall (CA-O); center of the facial wall (FW); faciopulpal angle (FPA); center of the pulpal wall (PW); and center of the lingual wall (LW). The data were submitted to the Kruskal-Wallis and the Dunn tests (α=0.05). Results: No difference was observed among the materials regarding the occlusal discrepancy at the CA-O, FPA, or PW internal points. The e.max CAD measurement at FW showed larger internal discrepancy than that of Lava (p=0.02). The internal discrepancy at LW was greater for e.max CAD than VITA ENAMIC (p=0.02). Conclusion: Lithium disilicate glass-ceramic presented greater internal discrepancy in relation to the surrounding walls of the inlay preparations

Assuntos

RESUMO

This study aimed to evaluate the influence of thermomechanical cycling (TMC) and type of abutment on the misfit and compressive strength of the implant−abutment interface. Forty 3.75-mm external hexagon implants with 25° angled abutments were divided into four groups (N = 10). Group A: overcast plus TMC; Group B: overcast without TMC; Group C: completely cast plus TMC; Group D: completely cast without TMC. Abutments were fixed to the implants with 32-Ncm torque, and groups A and C specimens were cyclically loaded at 80 N with 2 Hz for 1 million cycles. The misfit on the implant−abutment interface was evaluated by optical microscope (100×) and the compressive strength test was performed in a universal test machine. For statistical analysis, a two-way ANOVA and post hoc Tukey test were used. There was no difference in misfit presented by all the abutments in the absence of TMC (p > 0.05). When TMC was performed, the completely cast abutments showed greater misfit than overcast ones (p = 0.001). Regarding compressive strength, irrespective of TMC performed, the overcast abutments showed higher compressive strength values than completely cast abutments (p = 0.003). Moreover, disregarding the type of abutment used, the absence of TMC provided higher compressive strength values (p < 0.001). It was concluded that thermomechanical cyclic loading aggravated the misfit, especially in completely cast abutments, regardless of material or fabrication technique, and reduced the compressive strength of the two types of abutments tested.

RESUMO

PURPOSE: To evaluate the effect of polishing systems (discs or rubbers) on surface roughness (Ra) and color change (ΔE) of two bulk fill and one conventional resin composite after immersion in a dye solution. METHODS: 180 samples (10 mm x 2 mm) were separated into three groups: (1) Resin composite: Filtek One Bulk Fill (FO), Tetric N-Ceram Bulk Fill (TNC), Filtek Z350 XT (FXT) (n= 60); (2) polishing system: unpolished (control); aluminum oxide discs (Sof-Lex, AOD); cup-shaped abrasive rubber polishers (Astropol, CSA) (n= 20), and (3) immersion solutions: coffee or distilled water (n= 10). Immersion was under 5 mL of each solution for 3 hours daily, for 30 days. Measurement of Ra and ∆E was made considering two times: initial (after polishing) and final (after immersion), in addition to surface analysis by scanning electron microscopy at the end. Kruskal-Wallis, Mann-Whitney, and Dunn (α= 0.05) was used. RESULTS: For the unpolished samples after immersion in coffee, TNC (P= 0.007) showed lower ΔE than FXT and FO. For polished samples with CSA and immersed in coffee, TNC followed by FXT showed lower ΔE than in the absence of polishing. Polishing with AOD and immersed in coffee: FO had smaller ΔE than when not polished. For Ra, TNC and FO had lower values after using AOD, whereas for FXT lower Ra was noted with CSA. CLINICAL SIGNIFICANCE: The roughness and color stability of resin composites are mediated by the polished material, polishing system and dye solution. The best results were found for Tetric N-Ceram polished with aluminum oxide discs.

Assuntos

RESUMO

There is a constant search for bleaching treatments that can offer greater safety with fewer adverse effects, especially in the techniques performed in the office, which usually employ hydrogen peroxide in high concentrations (35% to 40%) that are not recommended by some international control agencies. This in vitro study evaluated the color change after tooth bleaching with the use of ozone and a 10% ozonized carbamide peroxide bleaching treatment for in-office use. Thirty molars were allocated (n = 10): three applications of ozone (1 hour every 3 days); three applications of 10% ozonized carbamide peroxide (1 hour every 3 days); 10% carbamide peroxide agent (8 hours a day for 7 days). The teeth were mounted on a plaster model to simulate the dental arch, and trays made of silicone were used for the application of the bleaching agents and to allow ozone to enter through. The ozone concentration used was 60 µg/mL, with an oxygen flow of 0.25 L/min. The values of color change showed no significant differences among treatments. The variations in the parameters over time, as well as the values of ΔEab, ΔE00, and WID, showed that there was no significant difference among the three treatments. The use of ozone and 10% ozonized carbamide peroxide for in-office use was effective for tooth bleaching with clinically perceptible and acceptable color alterations. The study was approved on September 10, 2019 by the São Leopoldo Mandic Ethics Research Committee (CAAE No. 17711719.4.0000.5374).

Assuntos

RESUMO

This study evaluated the influence of Libidibia ferrea (Lf) extract used as dentin pretreatment on the resin-dentin bond strength stability and dentin endogenous enzymatic activity. The phytochemical profile (PP) of the Lf extract was evaluated by liquid chromatography; particle size, polydispersity index (PdI), and zeta potential (ZP) were evaluated by dynamic light scattering. The tested groups were ER-Scotchbond Universal (SBU) in the etch-and-rinse (ER) mode; ERLf-SBU in the ER mode + Lf after etching; SE- SBU in the self-etch (SE) mode; and LfSE-Lf before SBU in the SE mode. Sticks were obtained for microtensile bond strength tests and failure mode (24 hr and 12 months). The hybrid layer was evaluated using scanning electron microscopy. The endogenous enzymatic activity of the underlying dentin was analyzed by in situ zymography with the same treatments. The PP showed the presence of quercetin (2.6% w/w). Lf particles were considered large after the analysis of the PdI. The ZP remained stable over time. The ER and ERLf groups had lower bond strength after 12 months, but SE and LfSE remained stable. The predominant failure mode was adhesive for both times. ER and ERLf had longer resin tags and a thicker hybrid layer. The ER and LfSE groups showed higher enzymatic activity than the ERLf and SE groups after 12 months. The Lf extract may contribute to inhibit the dentin endogenous enzymatic activity when associated with an adhesive system in the ER mode.

Assuntos