This work reports on the fabrication of a novel two-layer material composed of a porous tantalum core and a dense Ti6Al4V (Ti64) shell by powder metallurgy. The porous core was obtained by mixing Ta particles and salt space-holders to create large pores, the green compact was obtained by pressing. The sintering behavior of the two-layer sample was studied by dilatometry. The interface bonding between the Ti64 and Ta layers was analyzed by SEM, and the pore characteristics were analyzed by computed microtomography. Images showed that two distinct layers were obtained with a bonding achieved by the solid-state diffusion of Ta particles into Ti64 during sintering. The formation of ß-Ti and α' martensitic phases confirmed the diffusion of Ta. The pore size distribution was in the size range of 80 to 500 µm, and a permeability value of 6 × 10-10 m2 was close to the trabecular bones one. The mechanical properties of the component were dominated mainly by the porous layer, and Young's modulus of 16 GPa was in the range of bones. Additionally, the density of this material (6 g/cm3) was much lower than the one of pure Ta, which helps to reduce the weight for the desired applications. These results indicate that structurally hybridized materials, also known as composites, with specific property profiles can improve the response to osseointegration for bone implant applications.
RESUMO
The present work is focused on developing Ti-xTa porous alloys processed by the space holder method and solid-state sintering. The volume fraction of Ta ranged between 20 and 30 wt.%. The sintering kinetics was evaluated by dilatometry tests. Sintered materials were characterized by SEM, XRD and computed tomography. Porosity features and permeability were determined from 3D images, and their mechanical properties were evaluated from microhardness and compression tests. The sintering behavior and the final microstructure are driven by the Ta diffusion into the Ti, slowing down the densification and modifying the transition temperature of α-to-ß. Due to ß-stabilization, martensite α' was obtained after sintering. Mechanical properties are reduced because of the ß-stabilization and pore addition, being predominantly the pore effect. Permeability depended on the pore characteristics, finding values close to the human bones. It was concluded that powder metallurgy generates highly TixTa alloys with a combination of α, ß and α' Ti phases as well as remaining Ta particles that are beneficial to improve the biocompatibility and osseointegration of such materials. Being the Ti25Ta40salt alloy the most suitable for orthopedic implants because of its characteristics and properties.