3D Print Addit Manuf ; 10(4): 697-710, 2023 Aug 01.
Artigo em Inglês | MEDLINE | ID: mdl-37609577

RESUMO

The current available selective laser sintering (SLS) materials are often high in cost and limited in variety; the mechanical properties of wood-composite SLS parts are low quality, which restricts the development of SLS technology. This article aims to optimize the SLS processing parameters to enhance the mechanical properties of the Prosopis chilensis powder (PCP)/polyethersulfone (PES) composite (PCPC) part fabricated via SLS. The PCP and PES powder were proposed as the feedstock of the PCPC powder bed for SLS. First, the thermal decomposition and glass transition temperatures (Tg) of PCP and PES powder were estimated to reduce the produced PCPC parts from warping and deformation during SLS. An orthogonal experimental methodology with five factors and four levels was used to optimize the SLS parameters for the PCPC SLS test. The scanning speed, preheating temperature, and laser power are selected as the main affecting factors on this study. The influence of these factors on dimension accuracies, bending and tensile strengths, and surface roughness quality of the produced PCPC parts was studied. The PCPC particle distribution and microstructure were inspected via scanning electron microscopy. Furthermore, the synthesis weighted scoring methods were utilized to determine the optimal SLS processing parameters of the produced PCPC parts. The combined results of tests showed that the optimal SLS parameters were as follows: the scanning speed is 1.8 m/s, preheating temperature is 80°C, and the laser power is 12 W. Thus, the quality of PCPC SLS parts was significantly enhanced when the optimal parameters were utilized in the SLS process. This article provided the main reference values of SLS parameters of the PCPC. To further enhance the surface roughness quality and mechanical strengths, the postprocessing infiltration with wax was introduced; after wax infiltration, the surface roughness and mechanical strengths were significantly improved.

SELEÇÃO DE REFERÊNCIAS
DETALHE DA PESQUISA