RESUMO
OBJECTIVES: To evaluate the effect of EDC on elastic modulus (E), MMPs activity, hydroxyproline (HYP) release and thermal denaturation temperature of demineralized dentin collagen. METHODS: Dentin beams were obtained from human molars and completely demineralized in 10 wt% H3PO4 for 18 h. The initial E and MMP activity were determined with three-point bending and microcolorimetric assay, respectively. Extra demineralized beams were dehydrated and the initial dry mass (DM) was determined. All the beams were distributed into groups (n=10) and treated for 30 s or 60 s with: water, 0.5 M, 1 M or 2 M EDC or 10% glutaraldehyde (GA). After treatment, the new E and MMP activity were redetermined. The beams submitted to DM measurements were storage for 1 week in artificial saliva, after that the mass loss and HYP release were evaluated. The collagen thermal denaturation temperature (TDT) was determined by DSC analysis. Data for E, MMP activity and HYP release were submitted to Wilcoxon and Kruskal-Wallis or Mann-Whitney tests. Mass loss and TDT data were submitted to ANOVA and Tukey tests at the 5% of significance. RESULTS: EDC was able to significantly increase collagen stiffness in 60s. 10% GA groups obtained the highest E values after both 30 and 60s. All cross-linking agents decreased MMP activity and HYP release and increased TDT temperature. Significant differences were identified among EDC groups after 30 or 60 s of cross-linking, 1M or 2M EDC showed the lowest MMP activity. SIGNIFICANCE: Cross-linking agents are capable of preventing dentin collagen degradation. EDC treatment may be clinically useful to increase resin-dentin stability.
Assuntos
Reagentes de Ligações Cruzadas/química , Dentina/química , Varredura Diferencial de Calorimetria , Humanos , Técnicas In VitroRESUMO
OBJECTIVES: This study evaluated the kinetics of water uptake and percent conversion in neat versus ethanol-solvated resins that were formulated to be used as dental bonding agents. METHODS: Five methacrylate-based resins of known and increasing hydrophilicities (R1, R2, R3, R4 and R5) were used as reference materials. Resins were evaluated as neat bonding agents (100% resin) or they were solvated with absolute ethanol (95% resin/5% ethanol or 85% resin/15% ethanol). Specimens were prepared by dispensing the uncured resin into a circular mold (5.8 mm x 0.8 mm). Photo-activation was performed for 80s. The water sorption/diffusion/solubility was gravimetrically evaluated, while the degree of conversion (DC) was calculated by Fourier-transform infrared spectroscopy. RESULTS: Water sorption increased with the hydrophilicity of the resin blends. In general, the solvated resins exhibited significantly higher water sorption, solubility and water diffusion coefficients when compared to their corresponding neat versions (p<0.05). The only exception was resin R1, the least hydrophilic resin, in which neat and solvated versions exhibited similar water sorption (p>0.05). Addition of ethanol increased the DC of all resins tested, especially of the least hydrophilic, R1 and R2 (p<0.05). Despite the increased DC of ethanol-solvated methacrylate-based resins, it occurs at the expense of an increase in their water sorption/diffusion and solubility values. SIGNIFICANCE: Negative effects of residual ethanol on water sorption/solubility appeared to be greater as the hydrophilicity of the resin blends increased. That is, the use of less hydrophilic resins in dental adhesives may create more reliable and durable bonds to dentin.
Assuntos
Etanol/química , Cimentos de Resina/química , Solventes/química , Água/química , Absorção , Adsorção , Bis-Fenol A-Glicidil Metacrilato/química , Resinas Compostas/química , Difusão , Humanos , Teste de Materiais , Metacrilatos/química , Polietilenoglicóis/química , Polímeros/química , Ácidos Polimetacrílicos/química , Solubilidade , Espectroscopia de Infravermelho com Transformada de Fourier , Fatores de Tempo , MolhabilidadeRESUMO
This study evaluated the permeability properties of five experimental resin membranes that ranged from relatively hydrophobic to relatively hydrophilic to seal acid-etched dentin saturated with water or ethanol. The experimental resins (R1, R2, R3, R4, and R5) were evaluated as neat bonding agents or as solutions solvated with ethanol (70% resin/30% ethanol). The quality of dentin sealing by these experimental resins was expressed in terms of reflection coefficients calculated as the ratio of the effective osmotic pressure to the theoretical osmotic pressure of test solutions. The effective osmotic pressure produced across resin-bonded dentin was induced in hypertonic solutions (CaCl(2) or albumin) at zero hydrostatic pressure. The outward fluid flow induced by these solutions was brought to zero by applying an opposing negative hydrostatic pressure. The least hydrophilic resins blends, R1 and R2, exhibited significantly (p < 0.05) higher reflection coefficients than the most hydrophilic resins (R4 and R5) in both conditions of dentin saturation (water and ethanol). The reflection coefficients of neat resins were, in general, significantly higher when compared with their corresponding solvated versions in both conditions of dentin saturation. In dentin saturated with ethanol, bonding with neat or solvated resins, resulted in reflection coefficients that were significantly higher when compared with the results obtained in dentin saturated with water. Reflection coefficients of CaCl(2) (ca. 1 x 10(-4)) were significantly lower (p < 0.05) than for albumin (ca. 3 x 10(-2)). Application of hydrophobic resins may provide better sealing of acid-etched dentin if the substrate is saturated with ethanol, instead of water.
Assuntos
Cimentos Dentários/química , Cimentos Dentários/metabolismo , Albuminas/metabolismo , Humanos , Pressão Osmótica , SolubilidadeRESUMO
The aim of this study was to evaluate the ability of five experimental resins, which ranged from hydrophobic to hydrophilic blends, to seal acid-etched dentine saturated with water or ethanol. The experimental resins (R1, R2, R3, R4, and R5) were evaluated as neat bonding agents (100% resin) or as solutions solvated with absolute ethanol (70% resin/30% ethanol). Fluid conductance was measured at 20 cm H(2)O hydrostatic pressure after sound dentine surfaces were: (i) covered with a smear layer; (ii) acid-etched; or (iii) bonded with neat or solvated resins, which were applied to acid-etched dentine saturated with water or ethanol. In general, the fluid conductance of resin-bonded dentine was significantly higher than that of smear layer-covered dentine. However, when the most hydrophobic neat resins (R1 and R2) were applied to acid-etched dentine saturated with ethanol, the fluid conductance was as low as that produced by smear layers. The fluid conductance of resin-bonded dentine saturated with ethanol was significantly lower than for resin bonded to water-saturated dentine, except for resin R4. Application of more hydrophobic resins may provide better sealing of acid-etched dentine if the substrate is saturated with ethanol instead of with water.