RESUMO
OBJECTIVES: To evaluate the mechanical and antimicrobial properties of boron-containing coating on translucent zirconia (5Y-PSZ). METHODS: 5Y-PSZ discs (Control) were coated with a glaze (Glaze), silver- (AgCoat), or boron-containing (BCoat) glasses. The coatings' antimicrobial potential was characterized using S. mutans biofilms after 48 h via viable colony-forming units (CFU), metabolic activity (CV) assays, and quantification of extracellular polysaccharide matrix (EPS). Biofilm architectures were imaged under scanning electron and confocal laser scanning microscopies (SEM and CLSM). The cytocompatibility was determined at 24 h via WST-1 and LIVE&DEAD assays using periodontal ligament stem cells (PDLSCs). The coatings' effects on properties were characterized by Vickers hardness, biaxial bending tests, and fractography analysis. Statistical analyses were performed via one-way ANOVA, Tukey's tests, Weibull analysis, and Pearson's correlation analysis. RESULTS: BCoat significantly decreased biofilm formation, having the lowest CFU and metabolic activity compared with the other groups. BCoat and AgCoat presented the lowest EPS, followed by Glaze and Control. SEM and CLSM images revealed that the biofilms on BCoat were thin and sparse, with lower biovolume. In contrast, the other groups yielded robust biofilms with higher biovolume. The cytocompatibility was similar in all groups. BCoat, AgCoat, and Glaze also presented similar hardness and were significantly lower than Control. BCoat had the highest flexural strength, characteristic strength and Weibull parameters (σF: 625 MPa; σ0: 620 MPa; m = 11.5), followed by AgCoat (σF: 464 MPa; σ0: 478 MPa; m = 5.3). SIGNIFICANCE: BCoat is a cytocompatible coating with promising antimicrobial properties that can improve the mechanical properties and reliability of 5Y-PSZ.
Assuntos
Anti-Infecciosos , Cerâmica , Teste de Materiais , Boro/farmacologia , Reprodutibilidade dos Testes , Zircônio/farmacologia , Propriedades de SuperfícieRESUMO
OBJECTIVE:: This study investigated the Weibull parameters and 5% fracture probability of direct, indirect composites, and CAD/CAM composites. MATERIAL AND METHODS:: Discshaped (12 mm diameter x 1 mm thick) specimens were prepared for a direct composite [Z100 (ZO), 3M-ESPE], an indirect laboratory composite [Ceramage (CM), Shofu], and two CAD/CAM composites [Lava Ultimate (LU), 3M ESPE; Vita Enamic (VE), Vita Zahnfabrik] restorations (n=30 for each group). The specimens were polished, stored in distilled water for 24 hours at 37°C. Weibull parameters (m= modulus of Weibull, σ0= characteristic strength) and flexural strength for 5% fracture probability (σ5%) were determined using a piston-on-three-balls device at 1 MPa/s in distilled water. Statistical analysis for biaxial flexural strength analysis were performed either by both one-way ANOVA and Tukey's post hoc (α=0.05) or by Pearson's correlation test. RESULTS:: Ranking of m was: VE (19.5), LU (14.5), CM (11.7), and ZO (9.6). Ranking of σ0 (MPa) was: LU (218.1), ZO (210.4), CM (209.0), and VE (126.5). σ5% (MPa) was 177.9 for LU, 163.2 for CM, 154.7 for Z0, and 108.7 for VE. There was no significant difference in the m for ZO, CM, and LU. VE presented the highest m value and significantly higher than ZO. For σ0 and σ5%, ZO, CM, and LU were similar but higher than VE. CONCLUSION:: The strength characteristics of CAD/ CAM composites vary according to their composition and microstructure. VE presented the lowest strength and highest Weibull modulus among the materials.
Assuntos
Resinas Compostas/química , Desenho Assistido por Computador , Restauração Dentária Permanente/métodos , Cimentos de Resina/química , Silicatos/química , Dióxido de Silício/química , Tocoferóis/química , Zircônio/química , Análise de Variância , Falha de Restauração Dentária , Teste de Materiais , Microscopia Eletrônica de Varredura , Maleabilidade , Probabilidade , Valores de Referência , Reprodutibilidade dos Testes , Estresse Mecânico , Propriedades de Superfície , Resistência à Tração , Fatores de Tempo , Fraturas dos DentesRESUMO
ABSTRACT Objective: This study investigated the Weibull parameters and 5% fracture probability of direct, indirect composites, and CAD/CAM composites. Material and Methods: Discshaped (12 mm diameter x 1 mm thick) specimens were prepared for a direct composite [Z100 (ZO), 3M-ESPE], an indirect laboratory composite [Ceramage (CM), Shofu], and two CAD/CAM composites [Lava Ultimate (LU), 3M ESPE; Vita Enamic (VE), Vita Zahnfabrik] restorations (n=30 for each group). The specimens were polished, stored in distilled water for 24 hours at 37°C. Weibull parameters (m= modulus of Weibull, σ0= characteristic strength) and flexural strength for 5% fracture probability (σ5%) were determined using a piston-on-three-balls device at 1 MPa/s in distilled water. Statistical analysis for biaxial flexural strength analysis were performed either by both one-way ANOVA and Tukey's post hoc (α=0.05) or by Pearson's correlation test. Results: Ranking of m was: VE (19.5), LU (14.5), CM (11.7), and ZO (9.6). Ranking of σ0 (MPa) was: LU (218.1), ZO (210.4), CM (209.0), and VE (126.5). σ5% (MPa) was 177.9 for LU, 163.2 for CM, 154.7 for Z0, and 108.7 for VE. There was no significant difference in the m for ZO, CM, and LU. VE presented the highest m value and significantly higher than ZO. For σ0 and σ5%, ZO, CM, and LU were similar but higher than VE. Conclusion: The strength characteristics of CAD/ CAM composites vary according to their composition and microstructure. VE presented the lowest strength and highest Weibull modulus among the materials.