RESUMEN

Borosilicate glass was developed to enhance the mechanical behavior and smoothness of dental zirconia as an alternative to conventional glaze. This study assessed the mechanical and optical properties of 3 mol% yttria-stabilized tetragonal zirconia polycrystal (3Y-TZP) coated with borosilicate glass or a commercial glaze fired for an extended period of time. Disc-shaped 3Y-TZP zirconia specimens (Zpex, Tosoh) were sintered at 1550°C for 2 hours. The specimens were divided into three groups: as-sintered (control, C); commercial glaze (G); and borosilicate glass (SL). The glaze and borosilicate glass were applied over the zirconia and fired for 20 minutes at 950°C and 1200°C, respectively. Biaxial flexural strength, fractography, X-ray diffraction (XRD), roughness (Ra and Rz), fracture toughness (Vickers indentation method), color difference (∆E00), and translucency (TP00) analyses were conducted. The t-test or the one-way ANOVA and Tukey's tests were used to analyze the data (α = 0.05). Flexural strength data were subjected to the Weibull analysis. The SL group exhibited the highest flexural strength (1025.8 MPa), whereas the C (859.41 MPa) and G (816.0 MPa) groups exhibited similar values. The SL group also had the highest characteristic strength. The fracture origin in all groups was on the zirconia surface. XRD analysis revealed that the specimens from the SL group contained tetragonal, cubic, and monoclinic phases. The SL group presented the lowest surface roughness. Fracture toughness in the SL group was lower than in the C group, but similar to that observed in the G group. The translucency and color differences observed in the G and SL groups were similar. Borosilicate glass enhanced the flexural strength of 3Y-TZP, promoted the smoothest surface, and exhibited optical properties similar to those of the glaze.

Asunto(s)

Vidrio , Ensayo de Materiales , Propiedades de Superficie , Difracción de Rayos X , Itrio , Circonio , Circonio/química , Itrio/química , Vidrio/química , Análisis de Varianza , Factores de Tiempo , Resistencia Flexional , Silicatos/química , Reproducibilidad de los Resultados , Valores de Referencia , Estadísticas no Paramétricas , Color , Fenómenos Ópticos , Pruebas de Dureza , Materiales Dentales/química

RESUMEN

OBJECTIVE: this study sought to evaluate the effect of isobornyl methacrylate (IBOMA) as a diluent monomer on the physicochemical properties of experimental flowable resin composites. METHODOLOGY: the organic resin matrix of a modal flowable resin composite was formulated with 50 wt.% of bisphenol-A-glycidyl methacrylate (Bis-GMA) and 50 wt.% of a diluent monomer, in which IBOMA was used as a combining or substituent diluent monomer to triethylene glycol dimethacrylate (TEGDMA). The resin matrices were filled with 55 wt.% particles, of which 10 wt.% was 0.05-µm fumed silica, and 45 wt.% was 0.7-µm BaBSiO2 glass. Polymerization shrinkage stress (PSS; n=10), degree of conversion (DC; n=3), maximum rate of polymerization (Rpmax; n=3), film thickness (FT; n=10), sorption (Wsp; n=10), solubility (Wsl; n=10), flexural strength (FS; n=10), flexural modulus (FM; n=10), Knoop microhardness (KH; n=10), and microhardness reduction after chemical softening (HR; n=10) were evaluated. Data were analyzed using one-way ANOVA, followed by Tukey's test (α=0.05; ß=0.2). RESULTS: the results showed that the substitution or addition of IBOMA reduced FT (p=0.001), PSS (p=0.013), Rpmax (p=0.001), DC (p=0.001), FM (p=0.006) Wsp (p=0.032), and Wsl (p=0.021). However, when used as a complete substituent, IBOMA demonstrated significantly lower FS (p=0.017) and KH (p=0.008), while TEGDMA demonstrated significantly lower HR (p=0.022). CONCLUSION: the flowable composite containing IBOMA combined with TEGDMA showed no effect in KH and FS and effectively reduced the PSS, RP, FT, Wsp, and Wsl. However, it showed a reduction in DC, FS, and an increase in HR.

Asunto(s)

Bisfenol A Glicidil Metacrilato , Resinas Compuestas , Resistencia Flexional , Ensayo de Materiales , Metacrilatos , Polietilenglicoles , Polimerizacion , Ácidos Polimetacrílicos , Solubilidad , Propiedades de Superficie , Resinas Compuestas/química , Metacrilatos/química , Ácidos Polimetacrílicos/química , Polietilenglicoles/química , Bisfenol A Glicidil Metacrilato/química , Análisis de Varianza , Reproducibilidad de los Resultados , Valores de Referencia , Factores de Tiempo , Pruebas de Dureza , Dióxido de Silicio/química

RESUMEN

This study evaluated the effect of fluoride varnishes containing micrometric or nanosized sodium trimetaphosphate (TMP) on dentin erosive wear in vitro. Bovine root dentin blocks were selected by surface hardness and randomly divided into five experimental groups/varnishes (n = 20/group): placebo, 5% sodium fluoride (NaF); 5% NaF+5% micrometric TMP; 5% NaF+2.5% nanosized TMP; and 5% NaF+5% nanosized TMP. Half of the surface of all blocks received a single application of the assigned varnish, with subsequent immersion in artificial saliva for 6 h. Varnishes were then removed and the blocks were immersed in citric acid (90 s, 4×/day, 5 days). After each erosive cycle, ten blocks of each group were immersed in a placebo dentifrice for 15 s (ERO), while the other ten blocks were subjected to abrasion by brushing (ERO+ABR). Dentin erosive wear was assessed by profilometry. Data were submitted to 2-way ANOVA and to the Holm-Sidak test (p<0.05). Dentin erosive wear was significantly higher for ERO+ABR than for ERO for all varnishes. TMP-containing varnishes promoted superior effects against dentin erosive wear compared with 5% NaF alone; and 5% nanosized TMP led to the lowest wear among all varnishes. In conclusion, the addition of TMP to conventional fluoride varnish (i.e., varnish containing only NaF) enhanced its protective effects against bovine root dentin erosion and erosion+abrasion. Additionally, the use of 5% nanosized TMP led to superior effects in comparison to 5% micrometric TMP, both for erosion and erosion+abrasion in vitro.

Asunto(s)

Dentina , Fluoruros Tópicos , Ensayo de Materiales , Polifosfatos , Fluoruro de Sodio , Propiedades de Superficie , Erosión de los Dientes , Bovinos , Animales , Polifosfatos/farmacología , Polifosfatos/química , Dentina/efectos de los fármacos , Fluoruro de Sodio/farmacología , Erosión de los Dientes/prevención & control , Fluoruros Tópicos/farmacología , Análisis de Varianza , Factores de Tiempo , Propiedades de Superficie/efectos de los fármacos , Distribución Aleatoria , Reproducibilidad de los Resultados , Nanopartículas/química , Abrasión de los Dientes/prevención & control , Saliva Artificial/química , Ácido Cítrico/farmacología , Valores de Referencia , Pruebas de Dureza

RESUMEN

This study investigated the impact of 'storage condition' and 'period of storage' on selected physico-mechanical properties and fracture reliability of a resin-based composite (RBC). Specimens, prepared from a nanofilled RBC (Filtek Z350 XT; 3M ESPE), underwent tests for degree of conversion (DC), flexural strength (σ), flexural modulus (E), and hardness. The specimens were initially grouped into dry storage at 37°C or wet storage in distilled water at 37°C. Subsequently, they were further divided into four subgroups based on the period of storage: 6, 24, 72, or 168 hours. Specimens tested immediately after preparation served as control. Data analysis employed two-way ANOVA and Weibull analysis (α = 5%). Compared to the control, an increase in DC was observed only after 72 hours of dry storage; σ showed higher values after both dry and wet storage, regardless of the storage period (except for the group wet-stored for 168 hours); E increased with dry storage for at least 24 hours or wet storage for 72 hours; and hardness increased after dry storage for at least 24 hours or wet storage for up to 72 hours. The Weibull modulus remained unchanged under any of the distinct storage conditions. Dry storage resulted in greater characteristic strength than the control, whereas wet storage contributed to higher strength values only at shorter periods (up to 24 hours). Overall, the inherent properties of RBCs with a similar composition to that tested in this study may change with varying storage conditions and periods.

Asunto(s)

Resinas Compuestas , Resistencia Flexional , Pruebas de Dureza , Dureza , Ensayo de Materiales , Resinas Compuestas/química , Factores de Tiempo , Análisis de Varianza , Reproducibilidad de los Resultados , Valores de Referencia , Propiedades de Superficie , Temperatura

RESUMEN

This study aimed to evaluate in vitro the effect protocols and anticaries agents containing casein amorphous calcium fluoride phosphopeptide-phosphate (CPP-ACPF, MI Paste Plus), sodium trimetaphosphate (TMP) and fluoride (F), in remineralization of caries lesions. Bovine enamel blocks with initial caries lesions were divided into groups (n = 12): 1) Toothpaste without F-TMP-MI Plus (Placebo); 2) Toothpaste 1100 ppm F (1100F), 3) 1100F + MI Paste Plus (1100F-MI Paste Plus), 4) Toothpaste with 1100F + Neutral gel with 4,500 ppm F + 5%TMP (1100F + Gel TMP) and 5) Toothpaste with 1100F + Neutral gel with 9,000 ppm F (1100F + Gel F). For the 4 and 5 groups the gel was applied only once for 1 minute, initially to the study. For the 3 group, after treatment with 1100F, MI Paste Plus was applied 2x/day for 3 minute. After pH cycling, the percentage of surface hardness recovery (%SHR); integrated loss of subsurface hardness (ΔKHN); profile and depth of the subsuperficial lesion (PLM); concentrations of F, calcium (Ca) and phosphorus (P) in enamel was determined. The data were analyzed by ANOVA (1-criterion) and Student-Newman-Keuls test (p < 0.001). Treatment with 1100F alone led to ~ 28% higher remineralization when compared to treatment with 1100F associated with MI Paste Plus (p < 0.001). The 1100F and 1100F + Gel F groups showed similar values for %SHR (p = 0.150). 1100F + Gel TMP treatment also remineralized the enamel surface by ~ 30% and 20% when compared to the 1100F + Gel F and 1100F groups (p < 0.001). The lower lesion depth (ΔKHN) was observed for the 1100F + Gel TMP group (p < 0.001), where it was 54% and 44% lower in comparison to the 1100F and 1100F + Gel F groups (p < 0.001). Polarized light microscopy photomicrographs showed subsurface lesions in all groups, but these lesions were present to a lower extent in the 1100F + Gel TMP group (p < 0.001). Treatment with 1100F + Gel TMP promoted an increase in the concentration of Ca in the enamel by ~ 57% and ~ 26% when compared to the 1100F and 1100F + MI Paste Plus groups (p < 0.001), respectively. There were no significant differences between the 1100F, 1100F + MI Paste Plus and 1100F + Gel F groups (p > 0.001). Similar values of P in the enamel were observed in the 1100F, 1100F + MI Paste Plus and 1100F + Gel F groups (p > 0.001), except for the 1100F + Gel TMP group, which presented a high concentration (p < 0.001). We conclude that the 1100F+TMP gel treatment/protocol led to a significant increased remineralization when compared to the other treatments/protocols and may be a promising strategy for patients with early caries lesions.

Asunto(s)

Cariostáticos , Caseínas , Esmalte Dental , Fluoruros , Remineralización Dental , Caseínas/farmacología , Caseínas/uso terapéutico , Remineralización Dental/métodos , Bovinos , Animales , Esmalte Dental/efectos de los fármacos , Cariostáticos/farmacología , Fluoruros/farmacología , Factores de Tiempo , Pastas de Dientes/química , Caries Dental/tratamiento farmacológico , Análisis de Varianza , Reproducibilidad de los Resultados , Polifosfatos/farmacología , Polifosfatos/química , Polifosfatos/uso terapéutico , Pruebas de Dureza , Concentración de Iones de Hidrógeno , Propiedades de Superficie/efectos de los fármacos , Ensayo de Materiales , Resultado del Tratamiento , Valores de Referencia , Dureza/efectos de los fármacos , Fosfatos

RESUMEN

Abstract This research evaluates the presence of the oxygen-inhibited layer (OIL) on the top surface of a photopolymerized dental composite resin protected with a glycerin layer. This evaluation was conducted using physical and mathematical methods. Polymerized discs were fabricated to evaluate Vickers microhardness (VHN), and pre-and post-polymerized samples were used for the calculation of C-O/C-H ratios through Fourier Transform Infrared Spectroscopy (FTIR) (n=10), using two types of glycerin, one for medical use (MG) and another for dental use (DG). Surface hardness decreased from MG to DG to CO, and the increase in C-O/C-H ratios decreased in the same order (p<0.05). Samples protected with medical and dental glycerin layers are harder and exhibit lower C-O/C-H bond ratios than the control group.

---

Resumen La presente investigación evalúa la presencia de la capa inhibida por oxígeno OIL en la última superficie fotocurada de una resina compuesta de uso odontológica que fue protegida con una capa de glicerina. Esta evaluación se hizo a partir de métodos físicos y matemáticos. Se fabricaron discos polimerizados para evaluar la microdureza Vickers (VHN) y pre y post polimerizados para el cálculo de tasas C-O/C-H por medio de Espectroscopía Infrarroja Transformada de Fourier (FTIR) (n=10) usando dos tipos de glicerina, una de uso médico (MG) y otra de uso dental (DG). La dureza superficial disminuyó de MG a DG a CO y el aumento de tasas C-O/C-H disminuyó en ese mismo orden (p<0,05). Las muestras protegidas con capas de glicerina médica y odontológica son más duras y presentan menos cantidad tasas de enlaces C-O/C-H que el grupo control.

Asunto(s)

Resinas Compuestas/análisis , Glicerol/análisis , Polímeros , Espectroscopía Infrarroja por Transformada de Fourier , Pruebas de Dureza

RESUMEN

Abstract Objective: To evaluate the effect of different pressures of an oral irrigation device (OID) and the irrigation solution type on the surface roughness of the giomer restorative material. Material and Methods: In this in vitro study, disk-shaped giomer samples were fabricated and assigned to 5 groups (n=23): Group 1, storage in distilled water (control); Group 2, OID #7 pressure/ water; Group 3, OID #10 pressure/ water; Group 4, OID #7 pressure/ 0.05% CHX; Group 5, OID #10 pressure/ 0.05% CHX. The samples' treatment simulated a one-year application of OID. Surface roughness (Ra) and topography of the giomer were evaluated using profilometry and scanning electron microscopy. The data were analyzed with Paired t-test, Tukey, and ANOVA tests (α=0.05). Results: The Ra of the samples increased significantly after treatment with OID (p<0.001). The roughness increase in groups with a pressure of 10 was higher than those with a pressure of 7 (p<0.001). The effect of pressure on surface changes was significant (p<0.001). However, the solution type and the cumulative effect of these two factors were insignificant (p=0.08 and p=0.43, respectively). Conclusion: Oral irrigation device with both solutions significantly increased the surface roughness and topographic changes of the giomer. The severity of these changes was related to the device's pressure.

Asunto(s)

Biguanidas , Agua Destilada , Clorhexidina/efectos adversos , Resinas Compuestas , Propiedades de Superficie , Técnicas In Vitro/métodos , Análisis de Varianza , Pruebas de Dureza/métodos

RESUMEN

Aim: To determine if the artificial staining with black tea (BT) influences the enamel microhardness before in-office bleaching and if BT staining is necessary to evaluate the efficacy of bleaching with 35% hydrogen peroxide Methods: Enamel/dentin blocks were randomized into groups according to the staining protocol (n=5/group): (CO) control ­ maintained in artificial saliva solution (AS); (BT4) immersed in black tea solution for 4 h; (BT24) immersed in black tea solution for 24 h. After the staining protocols, all specimens were kept in AS for one week, followed by bleaching (three sessions of HP application for 40 min). Knoop surface microhardness (kgF/mm2) was determined at baseline (T0), after staining (T1), after 7 days of storage in AS (T2), and after bleaching (T3). The color (∆E00) and coordinate changes (∆L, ∆a, ∆b) were measured using a digital spectrophotometer at T0 and T3. Data were submitted to one-way (∆E00, ∆L, ∆a, ∆b) or two-way ANOVA repeated measures (kgF/mm2) and Tukey's test (a=5%). Results: The staining protocols (BT4 and BT24) promoted significantly lower microhardness (T1 and T2, p<0.05) than CO, whereas CO was the only group to maintain microhardness values over time. Bleaching promoted perceptible ∆E00 without a significant difference among the groups regardless of the staining protocol (p=0.122). CO and BT4 showed no differences in terms of ∆L and ∆a (p>0.05), but BT4 displayed a higher ∆b than CO. Conclusion:The artificial staining with BT negatively affected the enamel surface microhardness and was not essential to evaluate the efficacy of 35% hydrogen peroxide bleaching

Asunto(s)

Coloración y Etiquetado , Té/efectos adversos , Blanqueamiento de Dientes , Color , Esmalte Dental , Blanqueadores , Pruebas de Dureza , Peróxido de Hidrógeno

RESUMEN

Various forms of temporary resins are offered on the market; however, the properties of temporary resins obtained by milling and 3D printing have not been fully examined. This study aimed to compare the flexural strength and Vickers hardness of milled and 3D-printed resins. Methods: Three resins were tested: Evolux PMMA (milled resin), Cosmos Temp (3D-printed resin), and Structur 2 SC (bis-acrylic resin, group control). Specimens were prepared with rectangular shapes (n = 12) for flexural strength measurements and disc shapes (n = 9) for Vickers hardness tests. Flexural strength tests were performed at a crosshead speed of 0.75 mm/min, and the Vickers hardness was measured under a load of 20 N for 10 s. The obtained data were subjected to the Kruskal­Wallis test. Results: A significant difference (p < 0.05) in flexural strength was observed among the three sample groups: Evolux PMMA (111.76 MPa), Structur 2 SC (87.34 MPa), and Cosmos Temp (56.83 MPa). No significant difference (p < 0.05) was observed between the Vickers hardness values of Structur 2 SC (33.37 VHN) and Evolux PMMA (29.11 VHN); however, both materials were statistically superior to Cosmos Temp (10.90 VHN). Conclusion: While the mechanical properties of the milled resin were superior or similar to those of the bisacrylic resin, the 3D-printed resin was statistically inferior to both the milled and bis-acrylic resins

Asunto(s)

Diseño Asistido por Computadora , Restauración Dental Provisional , Resinas , Resistencia Flexional , Pruebas de Dureza

RESUMEN

A escassez de dados científicos que validem os benefícios da diatomita para as propriedades físicas da resina composta Zirconfill® torna imperioso a realização de novos estudos, principalmente no tocante a utilização dessa resina contendo diatomita em restaurações semidiretas. Objetivo: Avaliar in vitro a polimerização e resistência de união entre uma resina composta contendo diatomita e de uma resina composta bulk-fill após 24 horas e após 06 meses de envelhecimento em água. Materiais e métodos: Foram utilizados 28 incisivos bovinos para produzir cavidades dentinárias cônicas (4,8 mm de diâmetro maior x 2,8 mm de diâmetro menor x 4 mm de espessura) e fator C de magnitude 3,1. Esses preparos cavitários (n=28) foram restaurados com as resinas compostas Filtek™ One Bulk-fill (BF) (3M ESPE) ou Zirconfill ® (ZF) (BM4), através da técnica semidireta, utilizando o sistema adesivo Single Bond Universal (3M ESPE) e o cimento resino dual Relyx™ Ultimate (3M ESPE). A análise da polimerização foi realizada através da razão base/topo (B/T) de dureza Vickers. E a resistência de união RU foi realizada através do teste de extrusão push-out em máquina de ensaio universal. As amostras foram armazenadas em água destilada a 37 ºC por 24 horas ou 06 meses, mas apenas a RU avaliou as amostras após 06 meses de envelhecimento. Os dados da B/T e da RU foram submetidos à análise de variância (ANOVA) a um e a dois critérios, respectivamente, com pós-teste de Tukey (p <0.05). Resultados: Não houve diferença estatisticamente significativa entre as resinas compostas na B/T. Para a RU, a resina composta ZF mostrou valores maiores do que a resina BF em ambos os tempos avaliados. Não houve diferença estatisticamente significativa de nenhuma resina na avaliação ao longo do tempo. Conclusão: A resina composta contendo diatomita mostrou-se promissora quando utilizada em restaurações semidiretas, visto que obteve resultados similar e até superior a resina composta bulk-fill (AU).

---

The scarcity of data validating scientific diatomite benefits for physical properties of Zirconfill® resin composite makes essential to develop new studies, especially regarding the use of this resin composite containing diatomite in semi-direct restorations. Aim: To evaluate in vitro the cure and bond strength between a resin composite containing diatomite and a bulk-fill resin composite after 24 hours and after 06 months of water storage. Materials and methods: Twenty-eight bovine incisors (n=28) were used to produce conical dentinal cavities (4,8 mm of larger diameter x 2,8 mm of smaller diameter x 4 mm of thickness) and C-factor of magnitude 3.1. These cavities were restored with Filtek™ One Bulk-Fill (BF) (3M ESPE) or Zirconfill® (ZF) (BM4) resin composites, through the semi-direct technique, using Scotchbond™ Universal (3M ESPE) adhesive system and Relyx™ Ultimate (3M ESPE) dual resin cement. The cure analysis was performed through bottom-to-top (B/T) ratio of vickers hardness, while bond strength (RU) was performed through the push-out test in a universal testing machine. The specimens were stored in distilled water at 37 ºC for 24 hours or 06 months, but only RU analyzed the specimens after 06 months aging. B/T and RU data were, respectively, submitted to one-way and two-way analysis of variance (ANOVA) with Tukey's post-test (p <0.05). Results: There was no statistically significant difference between the composite resins in B/T. For RU, the ZF composite resin showed higher values than the BF resin at both evaluated times. However, there was no statistically significant difference in resin composites over time. Conclusion: The resin composite containing diatomite showed promise when used in semi-direct restorations since it obtained similar or even superior results to bulk-fill resin composite (AU).

Asunto(s)

Animales , Circonio , Polimerizacion , Tierra de Diatomeas , Factores de Tiempo , Técnicas In Vitro/métodos , Análisis de Varianza , Restauración Dental Permanente , Pruebas de Dureza

RESUMEN

O estudo objetivou avaliar a dureza superficial de três resinas compostas (Filtek Z350 - 3M ESPE, Zirconfil - TECHNEW, Vitra ­ FGM), após processo de clareamento dental de consultório a base de peróxido de Hidrogênio a 40%. Foram confeccionados 60 corpos de prova, com espessuras de 6,0 x 2,0 mm, sendo 20 corpos de cada material restaurador (n=20). Após processo de acabamento e polimento, os espécimes foram divididos aleatoriamente em dois grupos para cada material restaurador (n=10), onde o grupo controle G1-C, foi mantido em saliva artificial e o grupo experimental G2-E, foi submetido ao gel clareador de consultório a base de peróxido de hidrogênio a 40% de acordo com a indicação do fabricante. O teste de dureza utilizado foi o de Vickers. Para cada corpo de prova, foram realizadas quatro leituras consecutivas e equidistantes, com uma carga de 300g de força durante 15s. Os valores de dureza para resinas testadas foram estatisticamente mais elevadas no grupo controle, do que no grupo teste. Sendo que a maior diferença nos valores das médias entre os grupos ocorreu na resina Z350XT e para a margem de erro fixada (5%) se comprova diferença significativa (p < 0,05) entre os grupos teste e controle para cada resina. O uso do peróxido de hidrogênio 40% pela técnica de consultório, promoveu mudanças significativas na dureza superficial das resinas testadas. Além disso, a resina Z350XT apresentou dureza superior as demais resinas, porém foi a mais afetada pelo agente clareador (AU).

---

The study aimed to evaluate the surface hardness of three composite resins (Filtek Z350 - 3M ESPE, Zirconfil - TECHNEW, Vitra - FGM), after an in-office tooth whitening process using 40% hydrogen peroxide. Sixty specimens were made, with thicknesses of 6.0 x 2.0 mm, with 20 specimens of each restorative material (n=20). After finishing and polishing, the specimens were randomly divided into two groups for each restorative material (n=10), where the control group G1-C was maintained in artificial saliva and the experimental group G2-E was subjected to gel in-office bleaching agent based on 40% hydrogen peroxide, according to the manufacturer's instructions. The hardness test used was the Vickers hardness test and for each specimen, four consecutive and equidistant readings were performed, with a load of 300g of force for 15s. Hardness values for tested resins were statistically higher in the control group than in the test group. The greatest difference in mean values between the groups occurred in the Z350XT resin and for the fixed margin of error (5%) there is a significant difference (p < 0.05) between the test and control groups for each resin. The use of 40% hydrogen peroxide by the in-office technique promoted significant changes in the surface hardness of the tested resins. In addition, the Z350XT resin presented higher hardness than the other resins, but was the most affected by the bleaching agent (AU).

Asunto(s)

Blanqueamiento de Dientes , Resinas Compuestas , Pruebas de Dureza , Técnicas In Vitro , Análisis de Varianza , Peróxido de Hidrógeno

RESUMEN

Objective: The aim was to evaluate the influence of fluoride-releasing restorative materials in enamel and dentin microhardness. Material and Methods: 40 blocks (5x5x3 mm) from cervical third of human molars received a cavity preparation between the enamel and dentin, and the restorations were subjected to in vitro caries model. Specimens were randomly restored with (n=10): conventional glass ionomer cement (Ketac Cem, 3M ESPE); polyacid-modified composite resin (Ionoseal, VOCO); resin-modified glass ionomer cement (Ionofast, Biodinâmica); or microhybrid composite resin (Filtek Z250, 3M ESPE). The specimens were sectioned longitudinally and enamel and dentin Knoop microhardness were determined at different distances from the restorative material (100, 200 and 300 µm) and depth of surface (20, 40 and 60 µm). The data were submitted to three-way repeated measures ANOVA and Tukey ́s test ( α =0.05). Results: For enamel, the double interactions between material x distance and material x depth were statistically significant. In all depths and distances, the highest values of enamel microhardness were observed for Ketac Cem. In dentin, the materials differed statistically from each other, and Ionoseal obtained higher microhardness values than those found in Ionofast. Conclusion: Conventional glass ionomer cement is more effective in preventing enamel demineralization around restoration followed by the polyacid-modified composite resin. In dentin, the polyacid-modified composite resin obtained better performance than resin-modified glass ionomer cement. (AU)

---

Objetivo: O objetivo foi avaliar a influência de materiais restauradores liberadores de flúor na microdureza do esmalte e da dentina. Material e Métodos: 40 blocos (5x5x3 mm) do terço cervical de molares humanos receberam preparo cavitário entre esmalte e dentina, e após a restauração foram submetidas a um modelo in vitro de cárie. As amostras foram restauradas aleatoriamente com (n=10): cimento de ionômero de vidro convencional (Ketac Cem, 3M ESPE); resina composta modificada por poliácidos (Ionoseal, VOCO); cimento de ionômero de vidro modificado por resina (Ionofast, Biodinâmica); ou resina composta microhíbrida (Filtek Z250, 3M ESPE). As amostras foram seccionadas longitudinalmente e a microdureza Knoop de esmalte e dentina foi determinada em diferentes distâncias do material restaurador (100, 200 e 300 µm) e profundidade de superfície (20, 40 e 60 µm). Os dados foram submetidos à ANOVA para medidas repetidas de três fatores e teste de Tukey (α =0,05). Resultados: Para o esmalte, as duplas interações entre material x distância e material x profundidade foram estatisticamente significativas. Em todas as profundidades e distâncias, os maiores valores de microdureza do esmalte foram observados para o Ketac Cem. Na dentina, Ionoseal obteve valores de microdureza superiores aos encontrados no Ionofast. Conclusão:O cimento de ionômero de vidro convencional é mais eficaz na prevenção da desmineralização do esmalte ao redor da restauração, seguido pela resina composta modificada por poliácidos. Na dentina, a resina composta modificada por poliácidos obteve melhor desempenho que o cimento de ionômero de vidro modificado por resina. (AU)

Asunto(s)

Resinas Compuestas , Compómeros , Caries Dental , Cementos de Ionómero Vítreo , Pruebas de Dureza

RESUMEN

Abstract Objective: To examine the cyclic fatigue resistance and surface topography of TruNatomy and ProTaper Gold nickel-titanium rotary files and evaluate the presence of alterations to surface topography following instrumentation in simulated curved canals. Material and Methods: Twenty-four nickel-titanium instruments, twelve each of TN and PTG file systems, were evaluated for cyclic fatigue resistance. The rotary files were rotated in a simulated root canal with standardized diameter, angle of curvature, and radius of curvature in a custom-made cyclic fatigue testing device until the instrument fracture occurred. The time to fracture for each instrument was recorded with a stopwatch; in seconds in each group. Fractured instruments were subjected to atomic force microscopy analysis measuring the average roughness and the root mean square values to investigate surface features of endodontic files. Mean values and standard deviation were calculated. Data were analyzed using the Mann-Whitney U test. Results: Time to fracture was marginally higher in PTG instruments than in the TN file systems. PTG files exhibited higher surface roughness when compared with TN files (p<0.05). Conclusion: TN file system had a higher cyclic fatigue resistance than PTG. Cyclic fatigue causing file breakage did affect the surface topography of the files. PTG files showed a higher surface porosity value than the TN files (AU).

Asunto(s)

Titanio/química , Microscopía de Fuerza Atómica/instrumentación , Aleaciones Dentales , Instrumentos Dentales , Endodoncia , Propiedades de Superficie , Estadísticas no Paramétricas , Cavidad Pulpar , Pruebas de Dureza , Níquel/química

RESUMEN

Abstract Introduction composite resins are indicated to the reconstruction of proximal walls and the evaluation of properties of flow bulk-fill composite resins exposed to acid challenge is necessary. Objective to evaluate the microhardness and roughness at different depths of photoactivation of bulk-fill flow composites (Filtek Bulk Fill Flow; SureFil SDR Flow; Tetric N Ceram Bulk fill) and conventional composite resin (control, Filtek Z350 XT) subjected to acid challenge. Material and method forty composites brick shaped specimens (3x3x4 mm) were made using a polyacetal matrix. To simulate pH challenges, the samples were immersed in a demineralizing solution. Each sample had Knoop microhardness (KHN) and roughness (Ra) evaluated at three depths (superficial, medium, and cervical), considering the lateral surface of the sample. Data were submitted to Kruskal-Wallis, Friedman's and Dunn's tests with a significance level of 5%. Result comparing the composites among themselves, in superficial (p=0.693), medium (p=0.053) and cervical (p=0.176) regions, there was no difference in the KHN values. There were also no differences in roughness between the composites in superficial (p=0.356), medium (p=0.734) and cervical (p=0.207) regions. Only the Filtek Z350 XT (p=0.027) showed less difference in KHN in the middle region caused by acid challenge. Changes in roughness showed that the greatest difference was at the cervical region for Bulk Fill Flow SDR (p=0.014) and Tetric N-Ceram Bulk Fill (p = 0.003) with an increase after acid challenge. Conclusion after acid challenge, bulk-fill flow composites showed alterations similar to those presented by the conventional nanoparticulate resin composite.

---

Resumo Introdução as resinas compostas são indicadas para reconstrução de paredes proximais e a avaliação das propriedades das resinas compostas bulk-fill flow expostas ao desafio ácido mostra-se necessária. Objetivo avaliar a microdureza e rugosidade em diferentes profundidades de fotoativação de resinas compostas bulk-fill flow (Filtek Bulk Fill Flow; SureFil SDR Flow; Tetric N Ceram Bulk fill) e convencional (controle, Filtek Z350 XT) submetidas ao desafio ácido. Material e método quarenta amostras retangulares (3x3x4 mm) foram confeccionadas utilizando uma matriz de poliacetal. Para simular o desafio ácido, as amostras foram imersas em uma solução desmineralizante. Cada amostra teve a microdureza Knoop (KHN) e rugosidade (Ra) avaliadas em três profundidades (superficial, média e cervical), considerando a superfície lateral da amostra. Os dados foram submetidos aos testes de Kruskal-Wallis, Friedman e Dunn com nível de significância de 5%. Resultado comparando as resinas compostas entre si, nas regiões superficial (p=0,693), média (p=0,053) e cervical (p=0,176), não houve diferença nos valores de KHN. Também não houve diferenças na rugosidade entre os materiais nas regiões superficial (p=0,356), média (p=0,734) e cervical (p=0,207). Apenas o Filtek Z350 XT (p=0,027) apresentou menor diferença de KHN na região intermediária causada pelo desafio ácido. As mudanças na rugosidade mostraram que a maior diferença foi na região cervical para Bulk Fill Flow SDR (p=0,014) e Tetric N-Ceram Bulk Fill (p=0,003), com aumento após o desafio ácido. Conclusão após desafio ácido, as resinas compostas bulk-fill flow apresentaram alterações semelhantes às apresentadas pela resina composta convencional nanoparticulada.

Asunto(s)

Estadísticas no Paramétricas , Resinas Compuestas , Caries Dental , Restauración Dental Permanente , Curación por Luz de Adhesivos Dentales , Pruebas de Dureza

RESUMEN

Introdução: a inovação dos métodos de fotopolimerização foi proposta na tentativa de diminuir o estresse de contração de polimerização das resinas compostas e proporcionar maior conforto ao paciente, reduzindo o tempo de atendimento odontológico. Objetivo: avaliar a microdureza de duas resinas compostas nanoparticuladas submetidas a diferentes técnicas de polimerização. Material e método: quarenta espécimes foram divididos em quatro grupos (n=10) da seguinte forma: Filtek Z350 XT® + técnica imediata (GI); Filtek One Bulkfill® + técnica imediata (GII); Filtek Z350 XT® + técnica de pulso tardio (GIII); Filtek One Bulkfill® + técnica de pulso tardio (GIV). Após o armazenamento em água destilada à temperatura ambiente, os corpos de prova foram direcionados para a medição de microdureza. Utilizou-se teste T para comparação de técnicas e teste Two-Way ANOVA para calcular os efeitos das resinas compostas, técnicas de polimerização e interações referentes à variável dependente (p ≤0,05). Resultado: a resina Filtek Z350 XT® apresentou maior dureza na técnica imediata (GI - 312,45 ± 64,37) e pulso tardio (GIII - 244,50 ± 75,63) comparado à resina Filtek One Bulkfill®, em ambas as técnicas. Observaram-se maiores valores de dureza referentes à técnica imediata, com diferença estatística significativa em relação à resina testada (p = 0,04 - Filtek Z350 XT®; p = 0,03 - Filtek One Bulkfill®). Ambos os fatores isolados (resina e técnicas) apresentaram efeito nos valores de microdureza (p = 0,02 e p < 0,01, respectivamente). Conclusão: a técnica convencional demonstrou atingir maiores valores de dureza quando comparada à técnica de polimerização alternativa.

---

Introduction: the innovation of photopolymerization methods was proposed in an attempt to reduce the polymerization shrinkage stress of composite resins and also provide more comfort to patient reducing the chair time. The aim of this in vitro study was to assess the microhardness of two nanofilled composite resins subject to different curing techniques. Objective: assess the microhardness of two nanofilled composite resins subject to different curing techniques. Material and method: forty specimens were divided into four groups (N=10) as follows: Filtek Z350 XT® + immediate technique (GI); Filtek One Bulkfill® + immediate technique (GII); Filtek Z350 XT® + delayed pulse technique (GIII); Filtek One Bulkfill® + delayed pulse technique (GIV). After storage in distilled water at room temperature the specimens were assessed for microhardness measurement. T-test was used for comparison of techniques and two-way ANOVA used to calculate the effects of composite resins, curing techniques and their interactions on dependent variable (p set at 0.05). Result: Filtek Z350 XT® resin presented greater hardness on immediate technique (GI - 312,45 ± 64.37) and delayed pulse (GIII - 244,50 ± 75.63) compared to Filtek One Bulkfill® under both techniques. Overall, it was observed greater hardness values under immediate technique with a significant statistical difference apart of tested resin (p = 0.04 - Filtek Z350 XT®; p = 0.03 - Filtek One Bulkfill®). Both isolated factors (resin and techniques) presented effect on microhardness values (p = 0.02 and p < 0.01, respectively). Conclusion: the conventional technique demonstrated to reach higher hardness values when compared to the alternative polymerization technique

Asunto(s)

Técnicas In Vitro , Análisis de Varianza , Resinas Compuestas , Curación por Luz de Adhesivos Dentales , Pruebas de Dureza

RESUMEN

Objective: This study evaluated the influence of calcium lactate and sodium fluoride mouthwashes on enamel microhardness and dentin permeability during in-office bleaching. Material and Methods: For the microhardness evaluation, enamel blocks were randomly submitted to different treatments associated with in-office bleaching agent using 40% hydrogen peroxide (Opalescence Boost PF 40%/ Ultradent; 3 sessions x 40-minute each) (n = 10): 1) Control: application of bleaching agent; 2) Calcium lactate: 1-minute immersion before bleaching treatment; 3) Sodium fluoride: immersion for 1 minute before bleaching treatment; 4) Calcium lactate + sodium fluoride: 1 minute immersion in calcium lactate solution, followed by 1 minute immersion in sodium fluoride before bleaching treatment. Dentin discs received the same treatment protocols (n = 10) to evaluate permeability. Knoop microhardness and dentin permeability assessments were performed twice (at baseline and 48 hours after the end of bleaching treatment). Results: The generalized linear model considering the design of repeated measures over time showed that there was no significant difference between treatments (p = 0.9577) and between assessments (p = 0.3267) regarding Knoop microhardness. Kruskal Wallis and Dunn tests showed that calcium lactate immersion before bleaching treatment provided higher dentin permeability than other groups (p = 0.0009). Conclusion: The use of sodium fluoride solution and calcium lactate in association with in-office bleaching treatment did not influence the microhardness of tooth enamel, although calcium lactate may increase dentin permeability. (AU)

---

Objetivo: Este estudo avaliou a influência dos enxaguatórios bucais com lactato de cálcio e fluoreto de sódio na microdureza do esmalte e na permeabilidade da dentina durante o clareamento em consultório. Material e Métodos: Para avaliação da microdureza, blocos de esmalte foram submetidos aleatoriamente a diferentes tratamentos associados a agente clareador em consultório com peróxido de hidrogênio 40% (Opalescence Boost PF 40% / Ultradent; 3 sessões x 40 minutos cada) (n = 10): 1) Controle: aplicação de agente clareador; 2) Lactato de cálcio: imersão de 1 minuto antes do tratamento clareador; 3) Fluoreto de sódio: imersão por 1 minuto antes do tratamento clareador; 4) Lactato de cálcio + fluoreto de sódio: 1 minuto de imersão em solução de lactato de cálcio, seguido de 1 minuto de imersão em fluoreto de sódio antes do tratamento clareador. Os discos de dentina receberam os mesmos protocolos de tratamento (n = 10) para avaliar a permeabilidade. As avaliações da microdureza Knoop e da permeabilidade dentinária foram realizadas duas vezes (no início do estudo e 48 horas após o término do tratamento clareador). Resultados: O modelo linear generalizado considerando o delineamento de medidas repetidas ao longo do tempo mostrou que não houve diferença significativa entre os tratamentos (p = 0,9577) e entre as avaliações (p = 0,3267) em relação à microdureza Knoop. Os testes de Kruskal Wallis e Dunn mostraram que a imersão de lactato de cálcio antes do tratamento clareador proporcionou maior permeabilidade dentinária do que os outros grupos (p = 0,0009). Conclusão: O uso de fluoreto de sódio e lactato de cálcio associado ao clareamento em consultório não influenciou a microdureza do esmalte dentário, embora o lactato de cálcio possa aumentar a permeabilidade dentinária (AU)

Asunto(s)

Fluoruro de Sodio , Blanqueamiento de Dientes , Calcarea Lactica , Dentina , Pruebas de Dureza

RESUMEN

ABSTRACT: Objective: The aim of this study was to evaluate and compare the effects of the superficial application of two different modeling resins on the surface microhardness and discoloration of composite resins. Material and Methods: The present study used two different composites and modeling resins. The composites were placed in plastic molds. Subsequently, the modeling resins were applied on the surface of the two composite groups. The microhardness and color pertaining to all the groups were evaluated. The current study used the One-Way ANOVA and Kruskal Wallis tests, in order to perform the statistical evaluation (p<0.05). Results: The present study compared the microhardness pertaining to the groups and the highest microhardness values were observed in the Estelite Asteria group (none), whereas the lowest values were observed in the GC Essentia group (Ultradent). Moreover, the current study evaluated the color stability and the greatest discoloration was observed in the control group of the GC Essentia group, whereas the least discoloration was observed in the Estelite Asteria group that included the samples prepared using Ultradent Wetting Resin. Conclusions: The results of the present study demonstrated that the use of modeling resins, which facilitate the placement of composite resins, reduced the microhardness and discoloration of composite resins. The aforementioned effect can be attributed to the variations in the structure of the filling. However, further studies are warranted to support and verify the results of the current study.

---

RESUMEN: Objetivo: El objetivo del presente estudio fue evaluar y comparar los efectos de la aplicación superficial de dos resinas humectantes sobre la microdureza superficial y la decoloración de las resinas compuestas. Material y métodos: El presente estudio utilizó dos resinas humectantes y resinas de modelado diferentes. Las resinas compuestas se colocaron en moldes de plástico. Posteriormente, se aplicaron las resinas humectantes sobre la superficie de los dos grupos. Se evaluó la microdureza y el color de todos los grupos. El presente estudio utilizó las pruebas One-Way ANOVA y Kruskal Wallis, para realizar la evaluación estadística (p<0.05). Resultados: Los valores más altos de microdureza se observaron en el grupo Estelite Asteria, mientras que los menores valores se observaron en el grupo GC Essentia (Ultradent). La mayor decoloración se observó en el grupo control o el grupo GC Essentia, mientras que la menor decoloración se observó en el grupo Estelite Asteria con Ultradent Wetting Resin. Conclusiones: Los resultados del presente estudio demostraron que el uso de resinas humectantes, que facilitan la colocación de resinas compuestas, redujo la microdureza y decoloración de las resinas compuestas. El efecto mencionado anteriormente se puede atribuir a las variaciones en la estructura del relleno. Sin embargo, se necesitan más estudios para respaldar y verificar los resultados del presente estudio.

Asunto(s)

Resinas Compuestas/análisis , Dureza , Pruebas de Dureza , Decoloración de Dientes , Turquía

RESUMEN

esumen Objetivo: Comparar la microdureza de dos materiales endodónticos a base de silicato de calcio: MTA Densell Endo Sealer y TotalFill BC Sealer. Materiales y métodos: Se evaluó la microdureza de los selladores MTA Densell Endo Sealer (Grupo 1, n=5) y To- talFill BC Sealer (Grupo 2, n=5) contenidos en cilindros de dentina de vacuno a los 14 días posteriores a su fraguado. La medición se realizó a temperatura ambiente mediante la prue- ba de indentación Vickers. Se realizaron cinco indentaciones por probeta con una carga de 100 g durante 10 s cada una. Las mediciones se convirtieron a valores de dureza Vickers (HV) y los promedios de los valores HV de cada grupo se compararon por medio de la prueba t de Student con un nivel de significación de P <0,05. Resultados: A los 14 días, luego del fraguado, la mi- crodureza de MTA Densell Endo Sealer fue significativamen- te mayor (P=0,001) que la de TotalFill BC Sealer. Conclusiones: Los resultados sugieren que a causa de su dureza la remoción de MTA Densell Endo Sealer puede resultar dificultosa cuando está indicado un retratamiento (AU)

---

Aim: To compare the microhardness of two silicate-based endodontic materials: MTA Densell Endo Sealer and Total Fill BC Sealer. Materials and methods: Samples of MTA Densell Endo Sealer (Group 1, n=5) and Total Fill BC Sealer (Group 2, n=5) contained into cow dentine cylinders were subjected to the Vickers Microhardness Indentation test at room temper- ature and 14 days after setting. Five indentations per sample were performed under a load of 100 g for 10 s. The indenta- tion measurements were converted into hardness values (HV). Mean HV values of each group were compared using the Stu- dent t test at a significance level of P <0,05. Results: 14 days after setting, the microhardness of MTA Densell Endo Sealer was significantly greater (P=0,001) than that of Total Fill BC Sealer. Conclusions: The results of this study suggest that due to its hardness the removal of MTA Densell Endo Sealer could be difficult to perform when a root canal retreatment is indicated (AU)

Asunto(s)

Materiales de Obturación del Conducto Radicular , Cemento de Silicato , Pruebas de Dureza , Ensayo de Materiales

RESUMEN

El propósito de esta revisión bibliográfica es aportar información actualizada acerca de las características de los dientes bovinos en relación con su uso como sustitutos de dientes humanos en trabajos de investigación. De acuerdo con la información registrada, los dientes bovinos serían excelentes sustitutos de la dentición humana para la realización de ensayos de laboratorio con el esmalte dental como modelo experimental (AU)

---

The purpose of this bibliographic review is to provide updated information about the characteristics of bovine teeth to be used as substitutes for human teeth in dental research. According to the information recorded, bovine teeth appear to be excellent substitutes for human dentition for conducting laboratory tests, using dental enamel as an experimental model (AU)

Asunto(s)

Bovinos , Bovinos , Investigación Dental , Esmalte Dental/anatomía & histología , Erosión de los Dientes , Recubrimiento Dental Adhesivo , Esmalte Dental/ultraestructura , Pruebas de Dureza

RESUMEN

Objective: To assess the superficial microhardness of enamel-restorations margins of glass ionomer cement reinforced with silver (RS), modified with resin (RI) and composite resin (CO) after cariogenic biofilm. Materials and Methods: Thirty bovine enamel blocks with standard cavities were divided into three groups according to the materials used: RI (Riva Light Cure™, SDI), RS (Riva Silver™, SDI) and CO (Filtek™ Z350 XT, 3M). Half of each enamel block surface was covered by acid resistant varnish. After that, the blocks were exposed to Streptococcus mutans biofilm. The varnish was removed from the blocks and superficial microhardness (MDS) was measured (Knoop, 50 g, 15 s), with five indentations, 100 µm from each other in three different directions. The data were analyzed by the Shapiro Wilk, Kruskal Wallis and Mann Whitney tests (p<0.05). Results: MDS analysis indicated that in 50 µm distance from the restoration, RS group obtained hardness gain (6.31±0.01), unlike RI (-0.36±0.05) and CO (-11.43±0.02) groups that demonstrated significant loss (p<0.05). In other distances did not observe statistical difference between the groups. Regardless of the distance up to 450 µm, significant high total mineral gain was observed for RS group compared to the CO group; however, RS and RI presented similar enamel microhardness. Conclusion: All glass ionomers increased microhardness of enamel blocks even in contact with cariogenic biofilm. Although only the silver reinforced glass ionomer prevented demineralization at the margin restorations in 50 µm from the margin.

---

Objetivo: Comparar a desmineralização nas margens da interface dente/restauração utilizando cimento de ionômero de vidro modificado com resina (RI) e reforçado com prata (RS) e com resina composta (CO) após desafio cariogênico. Materiais e Métodos: 30 blocos de esmalte bovino com cavidades padronizadas foram divididos em 3 grupos de acordo com os materiais utilizados: RI (Riva Light CureTM, SDI), RS (Riva SilverTM, SDI) e CO (FiltekTM Z350 XT, 3M). Metade de cada superfície de esmalte restaurada foi protegida com verniz ácido-resistente. Os blocos foram expostos ao biofilme de Streptococcus mutans. O verniz foi removido dos espécimes com algodão e álcool para mensuração da microdureza superficial (MDS - Knoop, 50 g, 15 s), através de 3 linhas com 5 indentações em cada e 100 µm de distância entre elas. Os dados foram submetidos ao programa SPSS 20.0, teste de normalidade de Shapiro Wilk, Kruskal Wallis e Mann Whitney (p<0,05). Resultados: A análise da MDS demonstrou que na distância de 50 µm da restauração, o grupo RS apresentou ganho percentual de dureza (6,31 ± 0,01), diferentemente dos grupo RI (-0,036 ± 0,05) e CO (-11,43 ± 0,02) que apresentaram perda significativa (p<0,05). Nas demais distâncias, não foi observada diferença estatística entre os grupos. Conclusão: Todos os cimentos de ionômero de vidro aumentaram a microdureza superficial total dos blocos de esmalte mesmo após exposição ao biofilme cariogênico. No entanto, apenas o grupo RS impediu a desmineralização a 50 µm das margens de restaurações submetidas a biofilme cariogênico.

Asunto(s)

Materiales Dentales , Resinas Compuestas , Esmalte Dental , Cementos de Ionómero Vítreo , Pruebas de Dureza