RESUMEN
Magnetic wood is a composite material that achieves harmony between both woody and magnetic functions through the active addition of magnetic characteristics to the wood itself. In addition to showing magnetic characteristics, magnetic wood offers low specific gravity, humidity control and acoustic absorption ability. It has potential for broad applications in the fields of electromagnetic wave absorption, electromagnetic interference shielding, furniture, etc. This work reports on the synthesis of Fe3O4 nanoparticles (NPs) in wood from three tropical species (Pinus oocarpa, Vochysia ferruginea and Vochysia guatemalensis) using a solution of iron (III) hexahydrate and iron (II) chloride tetrahydrate with a molar ratio of 1.6:1 at a concentration of 1.2 mol/L ferric chlorate under 700 kPa pressure for 2 h. Afterward, the wood samples were impregnated with an ammonia solution with three different immersion times. The treated wood (wood composites) was evaluated for the weight gain percentage (WPG), density, ash content and Fe3O4 content by the Fourier transform infrared spectroscopy (FTIR) spectrum, X-ray diffraction (XRD) and vibrating sample magnetometry (VSM). The results show that the species P. oocarpa had the lowest values of WPG, and its density decreased in relation to the untreated wood, with lower ash and Fe3O4 NP content. The XRD and some FTIR signals associated with changes in the wood component showed small differences from the untreated wood. Fe3O4 NPs presented nanoparticles with the smallest diameter of (approx. 7.3 to 8.5 nm), and its saturation magnetization (Ms) parameters were the lowest. On the other hand, V. guatemalensis was the species with the best Ms values, but the wood composite had the lowest density. In relation to the different immersion times, the magnetic properties were not statistically affected. Finally, the magnetization values of the studied species were lower than those of the pure Fe3O4 nanoparticles, since the species only have a certain amount of these nanoparticles (NPs), and this was reflected proportionally in the magnetization of saturation.
RESUMEN
The growing demand in the consumer market for products with sustainable technologies has motivated new applications using overmolded natural fiber composites. Therefore, studies have been conducted mainly to understand the adhesive properties of overmolded parts. In the present study, a polypropylene (PP) composite with 30% coconut fibers without additives was developed with the aid of a corotating twin screw extruder. Subsequently, a multicomponent injection mold was developed based on the geometry of the ISO 527 type I specimen, in which samples overmolded with PP and PP-coconut-fiber composite, with the overlap in the central area, were obtained to evaluate the adhesive strength of dissimilar materials. The objective of this study was to evaluate the bond between PP and PP-coconut-fiber composite under different processing conditions using an adhesive strength testing device to perform a pure shear analysis. The experimental conditions followed a statistical design considering four factors in two levels and a significance level of 5%. The results indicated that adhesive strength increased significantly as the overlap area increased. It was observed that temperature and injection flow rate were the factors that most contributed to strengthening the bonds of dissimilar materials.