RESUMEN
The charging of nanoporous carbon via electrodeposition of solid iodine from iodide-based electrolyte is an efficient and ecofriendly method to produce battery cathodes. Here, the interactions at the carbon/iodine interface from first contact with the aqueous electrolyte to the electrochemical polarization conditions in a hybrid cell are investigated by a combination of in situ and ex situ methods. EQCM investigations confirm the flushing out of water from the pores during iodine formation at the positive electrode. XPS of the carbon surface shows irreversible oxidation at the initial electrolyte immersion and to a larger extent during the first few charge/discharge cycles. This leads to the creation of functional groups at the surface while further reactive sites are consumed by iodine, causing a kind of passivation during a stable cycling regime. Two sources of carbon electrode structural modifications during iodine formation in the nanopores have been revealed by in situ Raman spectroscopy, (i) charge transfer and (ii) mechanical strain, both causing reversible changes and thus preventing performance deterioration during the long-term cycling of energy storage devices that use iodine-charged carbon electrodes.
RESUMEN
The uncontrolled zinc electrodeposition and side reactions severely limit the power density and lifespan of Zn metal batteries. Herein, the multi-level interface adjustment effect is realized with low-concentration redox-electrolytes (0.2 m KI) additives. The iodide ions adsorbed on the zinc surface significantly suppress water-induced side reactions and by-product formation and enhance the kinetics of zinc deposition. The distribution of relaxation times results reveal that iodide ions can reduce the desolvation energy of hydrated zinc ions and guide the deposition of zinc ions due to their strong nucleophilicity. As a consequence, the Zn||Zn symmetric cell achieves superior cycling stability (>3000 h at 1 mA cm-2 , 1 mAh cm-2 ) accompanied by a uniform deposition and a fast reaction kinetics with a low voltage hysteresis (<30 mV). Additionally, coupled with an activated carbon (AC) cathode, the assembled Zn||AC cell delivers a high-capacity retention of 81.64% after 2000 cycles at 4 A g-1 . More importantly, the operando electrochemical UV-vis spectroscopies show that a small number of I3 - can spontaneously react with the dead zinc as well as basic zinc saltsand regenerate iodide ions and zinc ions; thus, the Coulombic efficiency of each charge-discharge process is close to 100%.