RESUMEN
Polyesters with a high glass transition temperature above 130 °C were obtained from limonene oxide (LO) or vinylcyclohexene oxide (VCHO) and phthalic anhydride (PA) in the presence of commercial salen-type complexes with different metals-Cr, Al, and Mn-as catalysts in combination with 4-(dimethylamino) pyridine (DMAP), bis-(triphenylphosphorydine) ammonium chloride (PPNCl), and bis-(triphenylphosphoranylidene)ammonium azide (PPNN3) as cocatalysts via alternating ring-opening copolymerization (ROCOP). The effects of the time of precontact between the catalyst and cocatalyst and the polymerization time on the productivity, molar mass (Mw), and glass transition temperature (Tg) were evaluated. The polyesters were characterized by a molar mass (Mw) of up to 14.0 kg/mol, a narrow dispersity Tg of up to 136 °C, and low (<3 mol%) polyether units. For poly(LO-alt-PA) copolymers, biodegradation tests were performed according to ISO 14851 using the respirometric biochemical oxygen demand method. Moreover, the vinyl double bond present in the poly(LO-alt-PA) copolymer chain was functionalized using three different thiols, methyl-3-mercaptopropionate, isooctyl-3-mercaptopropionate, and butyl-3-mercaptopropionate, via a click chemistry reaction. The thermal properties of poly(LO-alt-PA), poly(VCHO-alt-PA) and thiol-modified poly(LO-alt-PA) copolymers were extensively studied by DSC and TGA. Some preliminary compression molding tests were also conducted.
RESUMEN
Cyclohexene oxide (CHO) and phthalic anhydride (PA) have been reacted in the presence of commercial salen-type complexes with different metals Cr (1), Al (2), and Mn (3) in combination with 4-(dimethylamino) pyridine (DMAP), bis-(triphenylphosphorydine) ammonium chloride (PPNCl) and bis-(triphenylphosphoranylidene)ammonium azide (PPNN3) as co-catalysts to obtain alternating poly(PA-alt-CHO)s by ring-opening copolymerization (ROCOP). The effect of different reaction conditions (pre-contact between catalyst and co-catalyst, polymerization time) on the productivity, molecular weight and glass transition temperature has been evaluated. By using a 24 h pre-contact, the aliphatic polyesters obtained were characterized by high molecular weight (Mn > 15 kg/mol) and glass transition temperature (Tg) up to 146 °C; the more sustainable metals Al and Mn in the presence of PPNCl give comparable results to Cr. Moreover, biodegradability data of these polyesters and the study of the microstructure reveal that the biodegradability is influenced more by the type of chain linkages rather than by the molecular weight of the polyesters.
RESUMEN
Differential scanning calorimetry of high molar mass poly(4-vinylphenylboronic acid, pinacol ester)s evidenced unusual reactive events above 120 °C, resulting in a high glass-transition temperature of 220 °C. A reversible ring-opening reactivity of pinacol boronates is proposed, involving a nucleophilic attack on the sp2 boron and subsequent bridging between boron atoms by interconnected pinacol moieties to form a densely crosslinked network with high Tg . FTIR, solid-state NMR investigations, and rheology studies on the polymer as well as double-tagging analyses on molecular model structures and theoretical calculations further support this hypothesis and indicate a ring-opening inducing crosslinking. When diluted in an apolar solvent such as toluene, the polymer network can be resolubilized via ring closing, thus recovering the entropically favored linear chains featuring cyclic boronate esters.