RESUMEN

The aim of this study was to compare the cyclic fatigue resistance of nickel-titanium instruments inside single and double-curved canals at different temperatures. 160 HyFlex EDM #20.05 (HEDM), VDW.ROTATE #20.05 and #25.06, Mtwo #25.06 were randomised (n = 10) for the dynamic cyclic fatigue tests according to the curvature (i.e. single and double) at 20° ± 1°C and 35° ± 1°C. The number of cycles to fracture (NCF) was analysed by two-way ANOVA with p < 0.05. Fatigue resistance of all instruments significantly decreased at body temperature in single and double curvatures, except for HEDM in double curvature. The NCF was significantly lower in double curvature than single at both temperatures for all files, except for VDW.ROTATE #20.05 at 35° ± 1°C. Within the study limitations, temperature significantly impaired cyclic fatigue resistance of all files except HEDM #20.05 in double curvature. Similarly, double curvature had a detrimental effect on cyclic fatigue resistance of all files except for VDW.ROTATE #20.05 at body temperature.

Asunto(s)

RESUMEN

Introduction: This study aimed to evaluate the shaping ability of TruNatomy (Dentsply Maillefer, Ballaigues, Switzerland), VDW.ROTATE (VDW GmbH, Munich, Germany) and ProTaper Gold (Dentsply Maillefer, Ballaigues, Switzerland) during the preparation of resin-printed mandibular molar mesial root canals. Materials and Methods: Thirty-three printed resin-based mandibular mesial roots with two canals were obtained from extract tooth cone-beam computed tomography (CBCT) image. The printed teeth were divided into three groups (n = 11) according to the system used for root canal preparation: TruNatomy, VDW.ROTATE, and ProTaper Gold. The specimens were scanned using CBCT imaging before and after root canal preparation. Then images were registered using a dedicated software and changes in the canal area, volume, untouched canal surface, and the maximum and minimum dentin wall wear were calculated. Statistical Analysis Used: Data were statistically analyzed using Shapiro-Wilk for normality, one-way ANOVA, and Tukey or Kruskal-Wallis H tests with alpha set at 5%. Results: No differences were observed for changes in the canal area, volume, untouched canal surface area, and minimum dentine wall wear parameters for the whole canal length (P > 0.05). The mean of untouched canal surface area for the TruNatomy, VDW.ROTATE, and ProTaper Gold was 40%, 44%, and 44%, respectively. The maximum dentine wall wear was significantly lower in the ProTaper Gold group than in the TruNatomy and VDW.ROTATE groups (P < 0.05). Conclusions: TruNatomy, VDW.ROTATE, and ProTaper Gold systems showed similar shaping ability in printed resin-based mandibular mesial roots without clinically significant errors. A large amount of untouched canal surface area was observed for all systems.

RESUMEN

The apically extruded debris caused by TruNatomy System (TRN), RACE EVO system (RE) and VDW Rotate (VR) systems in mandibular anterior teeth with ribbon-shaped root canals were compared. The root canals (n = 20 in each group) were irrigated with NaOCl 2.5%, and the extruded debris was collected at pre-weighted Eppendorf tubes. The amount of apically extruded debris (mg) and the treatment time (s) were recorded. Tukey pairwise comparisons were performed to compare groups with a 95% confidence level. VR had significantly less debris extrusion values and treatment time than RE and TRN (P < 0.05). Although no difference was observed between RE and TRN in terms of apically extruded debris (P > 0.05), a significant difference in favour of RE was observed in terms of treatment time (P < 0.05). All the instruments extruded debris at varying weights.

Asunto(s)

RESUMEN

Background. This study aimed to compare the VDW.ROTATE instruments with the Reciproc Blue instruments in different kinematics in terms of the cyclic fatigue resistance. Methods. Sixty instruments, 40 VDW.ROTATE and 20 Reciproc Blue instruments, were divided into three groups (n=20): VDW.ROTATE was used in both continuous rotation and reciprocation, and Reciproc Blue was used in reciprocation only. The cyclic fatigue resistance test was carried out in an artificial canal (60°, r=3 mm) at an intracanal temperature of 35±2°C until fracture, and the time to fracture was recorded in seconds. The data were analyzed statistically using Kruskal-Wallis and Tamhane's T2 tests (P<0.05). Results. DAll the reciprocating motion groups resulted in a longer mean duration to failure than the continuous rotation motion group (P<0.05). Conclusion. It was observed that the Reciproc Blue instruments had higher cyclic fatigue resistance than VDW.ROTATE instruments (P<0.05). Recent studies have shown that reciprocal movement increases cyclic fatigue resistance compared to rotational movement. The VDW.ROTATE instrument, which has a similar size, design, and alloy as the Reciproc Blue instrument, can also be used by clinicians in reciprocating motion with endo motors capable of reciprocating in different directions. However, even if the cyclic fatigue resistance increases by using VDW.ROTATE instruments in reciprocation, the cyclic fatigue resistance is lower than Reciproc Blue instruments.