RESUMEN

Objective: This work aimed to assess the bonding performance of universal adhesive and self-etch adhesives, and a comparative study was conducted using the same acid etching mode. Methods: The selective acid-etching mode was used to simulate bonded restorations to teeth defects of isolated human molars including enamel and dentin. Microtensile bond strength and microleakage of all adhesives were tested and compared after 24 h and 5000 thermocycles, respectively. The morphology of the adhesive interfaces was observed by scanning electron microscopy (SEM) and fluorescent staining. Results: The bond strength and microleakage of Single Bond Universal (SBU) adhesive are comparable to those of self-etch adhesives, although Clearfil Tri-S Bond (S3) exhibited significantly lower bond strength compared to other two self-etch groups evaluated. No significant differences were found in the microleakage resistance of these four adhesives, suggesting their similar effectiveness in sealing the margins of the restorations, although SBU showed the highest resistance of microleakage. The SEM and fluorescent staining results of the resin-dentin interfaces further revealed the formation of abundant resin tags for all adhesives. Conclusions: Self-etch adhesives evaluated in this study performed similarly to universal adhesives in selective acid-etch mode for bond strength and microleakage resistance. Both types of adhesives exhibited effective penetration capabilities into the dentinal tubules. Clinical significance: During the adhesion processes involving both dentin and enamel, self-etch adhesives can serve as alternatives to universal adhesives in selective acid-etch mode.

RESUMEN

OBJECTIVES: To evaluate the effect of proanthocyanidin-functionalized hydroxyapatite nanoparticles (nHAp_PA) used as pretreatment at different concentrations on the microtensile bond strength (µTBS) and endogenous enzymatic activity (MMPs) on pH-cycled dentin after 24 h and 6 months of artificial aging. MATERIALS AND METHODS: Fifty human sound dentin blocks were randomly assigned to 5 groups (n = 10): (i) negative control (no treatment); (ii) positive control (pH-cycling); (iii) pH-cycling + 2% nHAp_PA for 60s; (iv) pH-cycling + 6.5% nHAp_PA for 60s; (v) pH-cycling + 15% nHAp_PA for 60s. A self-etch adhesive was used for bonding procedures before resin composite build-ups. Specimens were tested with the µTBS test after 24 h and 6 months of laboratory storage. The proteolytic activity in each group was evaluated with gelatin zymography and in situ zymography. Data were statistically analyzed (p < 0.05). RESULTS: At 24 h, the µTBS of the experimental groups were significantly higher than the controls (p ≤ 0.001), and no differences were observed between different concentrations (p > 0.05). Artificial aging significantly decreased bond strength in all groups (p ≤ 0.008); however, nHAp_PA 2% still yielded higher bonding values than controls (p ≤ 0.007). The groups pretreated with nHAp_PA exhibited lower MMP-9 and MMP-2 activities compared to the positive control group and almost the same enzymatic activity as the negative control group. In situ zymography showed that after 6 months of aging, nHAp_PA 2% and nHAp_PA 6,5% decreased enzymatic activity as well as the negative control. CONCLUSIONS: Dentin pretreatment with nHAp_PA increased the bonding performance of a self-etch adhesive and decreased MMP-2 and MMP-9 activities after 6 months.

Asunto(s)

RESUMEN

OBJECTIVES: To assess and compare the microtensile dentin bond strength (µTBS) and interfacial micromorphology of three universal adhesives. METHODS: 96 human molars were assigned to three universal adhesives: Single Bond Universal (SBU), CLEARFIL Universal Bond Quick (UBQ), and RE-GEN Universal Adhesive (REGEN). Adhesives were applied in self-etch mode. SBU and REGEN were applied following the manufacturers' instructions. UBQ was divided into two subgroups: one following the manufacturer's instructions (UBQ Short) and the other with an extended application time (UBQ Extended). Teeth were restored with nanohybrid resin composite. Specimens were divided into immediate and delayed subgroups. The delayed subgroups were stored for 6 months and subjected to 5000 thermocycles. µTBS was tested, and failure mode was analyzed. Interfacial micromorphology was assessed using a scanning electron microscope. The data were statistically analyzed (p⟨ 0.05). RESULTS: The adhesive choice, aging, and their interaction significantly affected µTBS. SBU exhibited the highest immediate µTBS, comparable to UBQ (Extended) and REGEN, and significantly higher than UBQ (Short). In delayed testing, SBU outperformed the other adhesives. CONCLUSIONS: Aging negatively affected the µTBS of UBQ and REGEN, while SBU wasn't affected. The quick application concept of UBQ deteriorated its µTBS compared to the extended application time.

Asunto(s)

RESUMEN

BACKGROUND: This study aimed to evaluate the impact of photodynamic therapy (PDT) using two photosensitizers, methylene blue and indocyanine green, on the microtensile bond strength of a universal adhesive to caries-affected dentin. METHODS: The occlusal enamel of 60 third molars was cut to expose the inner one-third of the dentin. Artificial caries were induced through a pH cycling process. The samples were divided into three groups: M (Methylene blue+ diode laser), I (Indocyanine green agents+ diode laser irradiation), and control. Each group was further divided into two subgroups according to the adhesive protocol (self-etch, total-etch). After restoring with Gradia composite resin, teeth were sectioned and exposed to 5000 thermal cycles. Microtensile bond strength was measured using a universal testing machine. The data were subjected to two- and one-way ANOVA and paired comparisons were performed by the Tamhane and Tukey tests. RESULTS: The study found significant effects of the photosensitizer, etching pattern, and their interactions on the microtensile bond strength of composite resin to caries-affected dentin (P < 0.001). In the self-etching mode, PDT with indocyanine green exhibited significantly higher bond strength values compared to PDT with methylene blue (P = 0.001) and the control groups (P < 0.001). However, no significant differences were observed in the total-etch mode. (P = 0.54). CONCLUSIONS: The etching mode played a more significant role in the bond strength when using the universal adhesive alongside PDT with methylene blue and indocyanine green. Employing two photosensitizers in PDT during the self-etch mode significantly increased the bond strength values.

Asunto(s)

RESUMEN

Objective: This study aimed to evaluate the bond strength of a universal adhesive to dentin (µTBS) using different time periods of airborne particle abrasion (APA) and two types of acid etching. Methods: Seventy-two human third molars were divided into 9 groups (n=8) according to dentin pretreatment: APA duration (0, 5, or 10s) and acid etching (no acid - NA, 37% phosphoric acid - PhoA, or 1% phytic acid - PhyA). APA was performed at a 0.5 cm distance and air pressure of 60 psi using 50 µm aluminum oxide particles. Afterwards, two coats of Single Bond Universal adhesive (3M) were applied to the dentin surface. Composite blocks were built using the incremental technique, sectioned into 1×1 mm slices and subjected to microtensile bond strength (µTBS) testing. Fracture patterns and surface topography of each dentinal pretreatment were evaluated using a Scanning electron microscope (SEM). Bond strength data were analyzed using two-way ANOVA and Bonferroni post-hoc tests. Results: The group that received pretreatment with 5s APA and PhoA presented higher µTBS values among all groups, which was statistically different when compared with the PhoA, 10APA+PhoA, and 5APA+PhyA groups. PhyA did not significantly influence the bond strength of the air-abraded groups. Finally, adhesive failure was considered the predominant failure in all groups. Conclusion: Dentin pretreated by airborne particle abrasion using aluminum oxide demonstrated an increase in bond strength when abraded for 5 seconds and conditioned with phosphoric acid in a universal adhesive system.

RESUMEN

This study evaluated the effect of simulated pulpal pressure (SPP) conditions and storage time on contemporary adhesive systems' microtensile bond strength (µTBS) to dentin. Extracted human molars were prepared and randomly divided into four groups according to the adhesives: Clearfil Megabond 2 (CSE), Beautibond Xtreme Universal (BXU), G2-Bond (G2B), and Scotchbond Universal Plus (SBP). Each adhesive group was further divided following the SPP conditions: control with no simulation (SPP-CTR), SPP with distilled water (SPP-DTW), and SPP with fetal bovine serum (SPP-FBS). Resin composite build-ups were prepared, and teeth were stored in water (37 °C) for 24 h (24 h) and 3 months (3 m). Then, teeth were sectioned to obtain resin-dentin bonded beams and tested to determine the µTBS. Data were analyzed using three-way ANOVA, Tukey post hoc tests (=0.05), and Weibull failure analysis. Failure mode was observed using scanning electron microscopy. The µTBS response was affected by adhesive systems, simulated pulpal pressure conditions, and storage time. SPP-CTR groups presented a higher overall bond strength than SPP-DTW and SPP-FBS, which were not significantly different from each other. Only for SBP, the SPP-FBS group showed higher µTBS than the SPP-DTW group. The Weibull analysis showed that the bonding reliability and durability under SPP-DTW and SPP-FBS were inferior to SPP-CTR, and the 24 h bonding quality of adhesives to dentin was superior to that of 3 m. SPP drastically reduced the µTBS of all adhesives to dentin regardless of solution (distilled water or fetal bovine serum). Storage after 3 m also decreased µTBS despite the SPP condition.

RESUMEN

AIM: The aim of this study was to compare the microtensile bond strength (µTBS) and failure mode of 4 different universal adhesive systems (UAs) on human dentin. MATERIALS AND METHODS: The study sectioned the occlusal thirds of 32 human third molars and divided them into 4 groups based on the adhesive system used. Group A: Palfique Universal Bond, Group B: Single Bond Universal, Group C: All-Bond Universal, and Group D: One Coat 7 Universal. The specimens underwent a 10,000-cycle thermocycling ageing process prior to testing (n = 32). Afterwards, 8 beams were obtained per group and subjected to µTBS testing using a digital universal testing machine at a speed of 1 mm/min. The microtensile bond strength values were analysed in Megapascals (MPa), and the failure mode was evaluated using a stereomicroscope. Welch's parametric ANOVA with robust variance and the Games-Howell post hoc test were used for µTBS comparisons, and Fisher's exact test was used to determine the association between adhesive type and failure mode. The significance level was set at P < .05. RESULTS: Group D showed a significantly higher µTBS than groups A (P < .001) and B (P < .001), but no significant difference was observed with group C (P= .075). Furthermore, groups B and C showed significantly higher µTBS than group A (P< .001 and P < .001, respectively), but there was no significant difference between groups B and C (P = .132). Additionally, group A exhibited a significant association with an adhesive failure mode (P < .05), whereas groups B, C, and D were significantly associated with a mixed failure mode (P < .05). CONCLUSION: The One Coat 7 Universal adhesive system showed higher microtensile bond strength values and higher chemical interaction with dentin compared to Palfique Universal Bond and Single Bond Universal. However, no significant differences were observed compared to All-Bond Universal.

RESUMEN

Aim: Long-term clinical success on indirect restorations is largely determined by bonding efficiency of the luting agent, with adhesion to dentin being the main challenge. Therefore, aim of this study was to assess the microtensile bond strength when using flowable resin composite, preheated resin composite and dual self-adhesive resin cement as dentin luting agents. Materials and Methods: Occlusal thirds of molar teeth were cut and randomly divided into 3 groups to be cemented: RelyX™U200, Filtek™ Z250 XT- preheated to 70° and Filtek Flow™ Z350XT. They were then thermocycled 5000 times between 5+/-2°C and 55+/-2°C. Subsequently, 10 microbars per group were prepared. The 30 samples were placed in saline solution for 24 hours at room temperature prior to microtensile test. This was performed with a digital universal testing machine at a crosshead speed of 0.5 mm/min. The bond strength values obtained were analyzed in Megapascals (MPa). Measures of central tendency such mean and measures of dispersion such standard deviation were used. In addition, the Kruskall Wallis non-parametric test with Bonferroni post hoc test was applied, considering a significance value of 5% (P < 0.05), with type I error. Results: The dentin microtensile bond strengths of preheated resin composite, flowable resin composite and dual self-adhesive cement were 6.08 ± 0.66 Mpa, 5.25 ± 2.60Mpa and 2.82 ± 1.26Mpa, respectively. In addition, the preheated resin composite exhibited significantly higher microtensile bond strength compared to the dual self-adhesive cement (P < 0.001). While the flowable resin composite showed no significant difference with the dual self-adhesive cement (P = 0.054) and the preheated resin composite (P = 0.329). Conclusions: The microtensile bond strength in dentin was significantly higher when using a preheated resin composite at 70°C as a luting agent compared to dual self-adhesive cement. However, the preheated resin composite showed similar microtensile bond strength compared to the flowable resin composite.

RESUMEN

OBJECTIVES: In-office and lab milled prostheses are the staple for indirect restorations. It is therefore critical to determine their long-term bonding durability. METHODS: CAD/ CAM blocks of two classes of restorative materials: 1) a nano-ceramic reinforced polymer matrix (NCPM) and, 2) a polymer-infiltrated ceramic network (PICN) were bonded using four different universal adhesives (UA) and silane systems. A lithium disilicate glassceramic (LDS) was used as a reference. The blocks were bisected and bonded with different UA/resin-cement pairs. Bonded blocks were then cut into 1.0x1.0x12.0 mm bar specimens for microtensile bond testing. Half the bars were subjected to bond strength testing immediately and the other half after aging by 50,000 thermal cycles between 5°C and 55°C. ANOVA and post-hoc tests were used to compare mean bond strength among groups. RESULTS: NCPM presented consistently high bond strength regardless of bonding techniques, while the bond strength of PICN and LDS were lower when bonded with UA relative to traditional silanes. The more hydrophilic UA produced higher bond strengths. DISCUSSION: Glass-ceramics exhibited lower bond strength with UA than the conventional etch-rinse-silane techniques. However, UAs preserved bonding interface in the long-term. SIGNIFICANCE: NCPM displayed superior bond strength relative to PICN and LDS regardless of the type of adhesives and bonding techniques.

Asunto(s)

RESUMEN

This study aimed to evaluate the effects of different resin-coating technique strategies and dual-cure resin luting materials on proximal marginal adaptation and the microtensile bond strengths (µTBSs) of CAD/CAM hybrid ceramic inlays. Extracted human molars were classified into four groups, depending on the coating technique: No coating (None), single coating (1-coating), double coating (2-coating), and flowable resin-coating (Combination). The inlays were bonded with one of the three materials: Panavia V5 (V5), Rely X Ultimate (RXU), and Calibra Ceram (CC). The differences with regard to adaptation were not significant. In the case of µTBS data for V5, no significant differences were observed, whereas for RXU, µTBS values for Combination statistically exceeded those for None and 1-coating. For CC, µTBS values for Combination statistically exceeded those for None, 1-coating, and 2-coating. The coating techniques did not influence the adaptation but influenced the bond strength, and Combination performed the best.

Asunto(s)

RESUMEN

BACKGROUND: The stability of resin-dentin interfaces is still highly questionable. The aim of this study was to evaluate the effect of Salvadora persica on resin-dentin bond durability. MATERIALS AND METHODS: Extracted human third molars were used to provide mid-coronal dentin, which was treated with 20% Salvadora persica extract for 1 min after acid-etching. Microtensile bond strength and interfacial nanoleakage were evaluated after 24 h and 6 months. A three-point flexure test was used to measure the stiffness of completely demineralized dentin sticks before and after treatment with Salvadora persica extract. The hydroxyproline release test was also used to measure collagen degradation by endogenous dentin proteases. Statistical analysis was performed using two-way ANOVA followed by post hoc Bonferroni test and unpaired t-test. P-values < 0.05 were considered statistically significant. RESULTS: The use of Salvadora persica as an additional primer with etch-and-rinse adhesive did not affect the immediate bond strengths and nanoleakage (p > 0.05). After 6 months, the bond strength of the control group decreased (p = 0.007), and nanoleakage increased (p = 0.006), while Salvadora persica group showed no significant difference in bond strength and nanoleakage compared to their 24 h groups (p > 0.05). Salvadora persica increased dentin stiffness and decreased collagen degradation (p < 0.001) compared to their controls. CONCLUSION: Salvadora persica extract pretreatment of acid-etched dentin preserved resin-dentin bonded interface for 6 months. CLINICAL SIGNIFICANCE: Durability of resin-dentin bonded interfaces is still highly questionable. Endogenous dentinal matrix metalloproteinases play an important role in degradation of dentinal collagen within such interfaces. Salvadora persica may preserve resin-dentin interfaces for longer periods of time contributing to greater clinical success and longevity of resin composite restorations.

Asunto(s)

RESUMEN

This study evaluated the bonding performance of coronal dentin disks, designed for biological restoration, and CAD/CAM resin composite disks when bonded to flat dentin surfaces using dual-cure resin cements, with and without a resin-coating (RC) technique. Three distinct groups were established within the non-RC group, each using one of the two types of resin cements in a self-adhesive mode: one-step self-etch adhesive (1-SEA) without light-cure, 1-SEA with light-cure, and a separate group using an alternate cement. Within the RC group, a subgroup was established for each cement. The microtensile bond strength (µTBS) of the disk-dentin beam was tested after 0 and 10,000 thermocycles in a 5°C/55°C. No significant µTBS difference was observed among the non-RC groups. However, when using RC, the µTBSs of coronal dentin disks significantly exceeded those of CAD/CAM resin composite disks. Thermocycle aging did not affect µTBS in any of the bonding methods, except in self-adhesive mode.

Asunto(s)

RESUMEN

PURPOSE: This study aimed to investigate the effects of the age and sex of tooth donors on dentin bond strength. METHODS: A total of 38 extracted teeth (12 male and 26 female donors; age range: 17-82 years) were used in this study. In addition to donor age and sex, four other microtensile bond strength (µTBS) test specimen factors were evaluated: dentin position, bonding area, presence of voids at the interface, and computed tomography (CT) values of dentin. The µTBS was measured immediately (24 h) and 6 months after storage in water. After the µTBS testing, linear mixed and nonlinear regression models were used to analyze the effects of these factors on the µTBS data. RESULTS: The results from the linear mixed model revealed that the bonding area (P = 0.02), presence of voids at the interface (P = 0.04), and storage time (P < 0.001) significantly affected bond strength. In contrast, no correlation was observed between the µ TBS and dentin position (P = 0.08) or sex (P = 0.07). The results of the nonlinear regression model with robust variance-covariance estimators revealed that age significantly affected bond strength (P < 0.001). In addition, a significant positive correlation was found between µTBS and age (P < 0.001), with nonlinearity (P = 0.002). However, no correlation was observed between the µTBS and CT values (P = 0.69) without nonlinearity (P = 0.39). CONCLUSIONS: These findings suggest that bond strength increases with age until 60 years but not afterward.

RESUMEN

OBJECTIVES: This study aimed to evaluate the adhesive properties in dentine after the application of silver diamine fluoride (SDF) on carious dentine lesions immediately and after 2 years of water storage. METHODS: 96 human molars used were subjected to artificial dentine caries production, and then randomly divided into 12 experimental groups according to 1. application of an SDF solution (carious dentine lesion without SDF treatment [control], with 12 % silver diamine fluoride [SDF 12 %] or 38 % silver diamine fluoride [SDF 38 %]); 2. Universal adhesives (Clearfil Universal Bond Quick [CUQ] and Single Bond Universal [SBU]); 3. adhesive strategy (etch-and-rinse [ER] and self-etch [SE]). After restoration, the specimens were sectioned and submitted to the microtensile bond strength test (µTBS) and energy-dispersive X-ray spectrometry analysis (SEM/EDX). All tests were performed immediately and after 2 years of water storage. Data from the µTBS were analyzed using four-way ANOVA and Tukey's test (α = 0.05). RESULTS: Only the interaction of factors 'SDF' vs 'time' was significant (p = 0.03). After 2 years of storage, the groups where SDF was applied showed higher µTBS values compared to the control group. No significant decrease in µTBS values was observed for SBU when comparing immediate and 2-year results, but a significant reduction in µTBS values was observed after 2 years for CUQ. CONCLUSION: Independent of the adhesive strategy, the use of SDF may be a promising alternative to maintain the bonding of universal adhesives to carious dentinal lesions. CLINICAL SIGNIFICANCE: This study may clarify and support clinicians regarding the longevity of resin-based restoration in caries-affected dentine treated with silver diamine fluoride.

Asunto(s)

RESUMEN

PURPOSE: This study investigated and compared the bond strengths, microleakage, microgaps, and marginal adaptation of self-adhesive resin composites (SAC) to dentin with or without universal adhesives. MATERIALS AND METHODS: Dentin surfaces of 75 molars were prepared for shear and microtensile bond strength testing (SBS and µTBS). Silicon molds were used to build up direct restorations using the following materials to form 5 groups: 1. Surefil One; 2. Prime&Bond active Universal Adhesive + Surefil One; 3. Vertise Flow; 4. OptiBond Universal + Vertise Flow; 5. Scotchbond Universal + Filtek Z500 (control group). Bonded specimens were thermocycled 10,000x before being tested either for SBS or µTBS using a universal testing machine at a crosshead speed of 0.5 mm/min. Direct mesial and distal class-II cavities were created on 100 sound premolars, with the gingival margin of distal cavities placed below CEJ and restored according to the five groups. After thermocycling, microleakage scores were assessed following immersion of restored premolars in 2% methylene blue dye for 24 h, while marginal gaps and adaptation percentages were investigated on epoxy resin replicas under SEM at magnifications of 2000X and 200X, respectively. Results were statistically analyzed with parametric and non-parametric tests as applicable, with a level of significance set at α = 0.05. RESULTS: Bond strengths, microleakage scores, microgaps, and percent marginal adaptation of Surefil One and Vertise Flow were significantly (p < 0.001) inferior to the control group. Dentin preconditioning with universal adhesives significantly increased the study parameter outcomes of Surefil One and Vertise Flow, yet they were still significantly below the performance of the control group. CONCLUSION: Conventional resin composite outperformed the SAC whether applied solely or in conjunction with their corresponding universal adhesives.

Asunto(s)

RESUMEN

OBJECTIVES: The aim of this study was to compare the dentin adhesion of bulk-fill composites in high C-factor class I-cavities before and after thermocycling to a control group using incremental layering technique. METHODS: A standardized class I-cavity was prepared into 195 human molars, then different universal adhesives were applied either in self-etch or etch & rinse mode, and the cavity was filled according to each materials application protocol. The material combinations used were a conventional layered composite as control, the respective bulk-fill product, two other bulk-fill composites made by different manufacturers, with one of them being tested using two different polymerization times. Furthermore, one thermoviscous bulk-fill composite and one self-adhesive restorative were examined of which the latter can only be applied in self-etch mode. In each group the dentin adhesion to the cavity bottom was measured using microtensile bond strength test initially (24 h water storage) and after thermocycling. All results were statistically analyzed using STATA 17.0. RESULTS: The statistical analysis showed significant differences between the control and the experimental groups (p < 0.001). The highest mean bond strength before (14.8 ± 10.7 MPa) and after aging (14.2 ± 11.5 MPa) was measured for the etch & rinse-control group. Among the bulk-fill groups, the etch & rinse technique consistently showed higher bond strengths. Bond strength of groups with shortened polymerization did not exceed 2.1 MPa. The bond strength of the self-adhesive restoration material was low before and after thermocycling (2.7 MPa/ 0.0 MPa). Groups with low bond strength values showed a high number of pre-testing-failures. CONCLUSIONS: Bulk-fill materials used in high C-factor class I-cavities showed lower bond strength during self-etch application. The same applies for a shortened polymerization regime, which cannot be recommended for high C-factor cavities. CLINICAL SIGNIFICANCE: Today, a large variety of materials and application techniques can be used when placing an adhesive restoration. Whether new instead of established procedures should be applied in high C-factor cavities has to be critically assessed, as they are a demanding scenario for adhesive restorations.

Asunto(s)

RESUMEN

AIM: To evaluate the microtensile bond strength of self-etching adhesive systems in dentin treated with 2% chlorhexidine digluconate (CHX). MATERIALS AND METHODS: The occlusal surfaces of 20 human molars were removed and divided into eight groups: 1A, Clearfil SE adhesive (SE) with self-etching technique (TS); 1B, SE with TS and previous application of CHX; 2A, Scotchbond Universal (SBU) adhesive with TS; 2B, SBU adhesive with TS and previous application of CHX; 1C, SE with total-etching technique (TT); 1D, SE with TT and previous application of CHX; 2C, SBU with TT; 2D SBU with TT and previous application of CHX. Composite resin (5mm) was applied on the hybridized surface. Samples were subjected to microtensile test and evaluated on Scanning Electron Microscope (SEM) and with energy-dispersive X-ray (EDX). RESULTS: Low values of bond strength were observed in groups 1A (39,77±11,56) and 2A (40,84±12,49) comparing with 1B (22,86±5,18) and 2B (27,02±5,58). TS group presented adhesive type remover fracture while TT groups presented cohesive at the top of hybrid layer. EDX revealed the presence of CHX crystals for TS, which was not found in the TT. CONCLUSION: The previous application of chlorhexidine on dentin decreased the bond strength of adhesive systems on self-etching technique.

Asunto(s)

RESUMEN

Objective@#To explore the effect of Morinda citrifolia juice (MCJ) combined with ethylene diamine tetraacetic acid (EDTA) on premolar bonding strength and nanoleakage and compare the results with those of the most commonly used root canal irrigation solution, sodium hypochlorite (NaClO), to provide a reference for clinical application.@*Methods@#This study was approved by the ethics review committee. Sixty-three human premolars extracted for orthodontic treatment were randomly divided into a control group (distilled water group) and 6 experimental groups according to the different rinsing solutions used after the surface enamel was removed. The experimental groups included Group A (2.5% NaClO), Group B (5.25% NaClO), Group C (6% MCJ), Group D (2.5% NaClO-17% EDTA), Group E (5.25% NaClO-17% EDTA), and Group F (6% MCJ-17% EDTA) (n = 9). After soaking in the corresponding rinsing solution for 20 minutes, they were layered and stacked on their surfaces to form 4 mm × 4 mm × 3 mm Z350 resin blocks. Six samples from each group were cut into 1 mm × 1 mm × 8 mm specimen strips for microtensile bonding strength testing. The fracture type was determined under a stereomicroscope, and the remaining 3 samples from each group were aged and cut into 1 mm thick slices for interface nanoleakage testing and scanning electron microscopy observation of the resin dentin bonding interface.@*Results@#There were significant differences in the microtensile bonding strength among the groups (P<0.05), and the control group had the highest bonding strength. Among experimental groups, Group B had the lowest bonding strength, mainly bonding interface fracture, and Group F had the highest bonding strength, mainly mixed fracture. There were significant differences in nanoleakage among all groups (P<0.05), and the control group had the lowest nanoleakage value. Among experimental groups, Group B had the highest nanoleakage, with resin protrusions being unaltered, and Group F had the lowest nanoleakage value, with resin protrusions being thick and dense.@*Conclusion@#The higher the concentration of NaClO was, the worse the bonding strength and edge sealing of the crown dentin were. The effects of root canal irrigation with MCJ and EDTA on the adhesive strength and edge sealing of crown dentin were less pronounced than those of root canal irrigation with NaClO and EDTA.

RESUMEN

OBJECTIVES: Tideglusib has shown great performance in terms of dentin regenerative properties. This study aims to evaluate bonding ability, of demineralized dentin infiltrated with polymeric nanoparticles (NPs) doped with tideglusib (TG) (TG-NPs). METHODS: Dentin conditioned surfaces were infiltrated with NPs and TG-NPs. Bonded interfaces were created and stored for 24 h and then submitted to mechanical, chemical and thermal challenging. The resin-dentin interface was evaluated through a doubled dye fluorescent technique and a calcium chelator fluorophore under a confocal laser scanning microscopy, and by field emission scanning electron microscopy. RESULTS: Dentin surfaces treated with TG-NPs and load cycled produced higher bond strength than the rest of the groups. Immersion of dentin specimens treated with undoped-NPs in collagenase solution attained the lowest microtensile bond strength (MTBS) values. Both porosity and nanoleakage decreased when dentin was infiltrated with TG-NPs, that revealed strong signals of xylenol orange stain at both hybrid layer and dentinal tubules. The presence of NPs, in general, inducted the presence of mineralized interfaces after mechanical loading and thermocycling. CONCLUSIONS: Nanoparticles doped with tideglusib promoted the highest dentin bonding efficacy among groups, as they facilitated the maximum bond strength values with creation of mineral deposits at the hybrid layer and dentinal walls. Tideglusib enabled scarce porosity, nanoleakage and advanced sealing among dentin groups. SIGNIFICANCE: Doping hydrophilic polymeric NPs with tideglusib, infiltrated in etched dentin represents a reproducible technique to create reparative dentin at the resin-dentin interface, by inducing therapeutic bioactivity.

Asunto(s)

RESUMEN

One of the major goals of adhesive dentistry is to improve the interaction of the already-existing adhesives with different substrates by using different application techniques. Thus, the objective of the present in vitro study was to assess the bond performance of four adhesive systems, Prime&Bond Universal (PBU), Clearfil SE Bond (CSE), OptiBond Universal (OBU), and OptiBond FL (OBFL), to dentin using various application modes: passive application (PA), active application (AA), Compo-Vibes modified application (CVM), and Compo-Vibes application (CV). Eighty extracted human molars were allocated into four groups based on the application modalities tested. The micro-tensile bond strength as well as fracture mode were tested in accordance with ISO/TS 11.405 after 24 h and 6 months of aging. Adhesive contact angle (CA) and scanning electron microscope analysis were also performed (n = 3). Statistical tests were performed with α = 0.05. After 24 h, a significant difference with a higher bond strength value was found for PBU in the AA modality and for CSE in the CVM modality (p < 0.05). However, no significant difference was shown between the techniques used among the other adhesives (OBFL and OBU). Moreover, at 24 h, only the PA demonstrated significant differences between the tested materials (p < 0.05). After 6 months, CSE, PBU, and OBU demonstrated significant differences between the techniques (p < 0.05), with a higher bond strength for CSE in AA and CVM modalities, for PBU in AA modality, and for OBU in AA and PA modalities. No significant differences were found between the techniques used among the OBFL (p > 0.05). In addition, only the CVM technique demonstrated significant differences between the tested materials after 6 months. CV and CVM showed a decreased value after aging for CSE and PBU, respectively. However, all the modalities decreased for OBU and OBFL after aging. All the adhesives showed marked resin infiltration into dentinal tubules in AA among all the modalities tested. Both universal adhesive systems (OBU and PBU) demonstrated statistically lower CA when compared to the other systems (CSE and OBFL) (p < 0.05) when applied in the PA mode. Concerning the AA mode, only CSE and OBFL were tested. The AA demonstrated lower CA values compared to the same adhesives in PA (p < 0.05). It could be concluded that the bond strength could be influenced by both materials and application techniques. It seems that the AA technique could be recommended as a gold standard for the application of an adhesive system to dentin. Plus, the CV and CVM modalities after 6 months of aging were considered stable for PBU and CSE, respectively. Consequently, the performance of these adhesive systems might vary when applied to other modalities. Future studies are needed to test this hypothesis.