RESUMEN
The large and rapidly growing family of 2D early transition metal carbides, nitrides, and carbonitrides (MXenes) raises significant interest in the materials science and chemistry of materials communities. Discovered a little more than a decade ago, MXenes have already demonstrated outstanding potential in various applications ranging from energy storage to biology and medicine. The past two years have witnessed increased experimental and theoretical efforts toward studying MXenes' mechanical and tribological properties when used as lubricant additives, reinforcement phases in composites, or solid lubricant coatings. Although research on the understanding of the friction and wear performance of MXenes under dry and lubricated conditions is still in its early stages, it has experienced rapid growth due to the excellent mechanical properties and chemical reactivities offered by MXenes that make them adaptable to being combined with other materials, thus boosting their tribological performance. In this perspective, the most promising results in the area of MXene tribology are summarized, future important problems to be pursued further are outlined, and methodological recommendations that could be useful for experts as well as newcomers to MXenes research, in particular, to the emerging area of MXene tribology, are provided.
RESUMEN
Two-dimensional (2D) MXene materials have recently been the focus of membrane research due to their unique properties, such as their single-atomic-layer thickness, flexibility, molecular filtration abilities and microstructural similarities with graphene, which is currently the most efficient precursor material for gas separation applications. In addition, the potential to process nanoscale channels has motivated investigations of parameters which can improve membrane permeability and selectivity. Interlayer spacing and defects, which are still challenging to control, are among the most crucial parameters for membrane performance. Herein, the effect of heat treatment on the d-spacing of MXene nanosheets and the surface functionalization of nanolayers was shown regarding its impact on the gas diffusion mechanism. The distance of the layers was reduced by a factor of over 10 from 0.345 nm to 0.024 nm, the defects were reduced, and the surface functionalization was maintained upon treatment of the Ti3C2 membrane at 500 °C under an Ar/H2 atmosphere as compared to 80 °C under vacuum. This led to a change from Knudsen diffusion to molecular sieving, as demonstrated by single-gas permeation tests at room temperature. Overall, this work shows a simple and promising way to improve H2/CO2 selectivity via temperature treatment under a controlled atmosphere.