RESUMEN
SiGeSn nanocrystals (NCs) in oxides are of considerable interest for photo-effect applications due to the fine-tuning of the optical bandgap by quantum confinement in NCs. We present a detailed study regarding the silicon germanium tin (SiGeSn) NCs embedded in a nanocrystalline hafnium oxide (HfO2) matrix fabricated by using magnetron co-sputtering deposition at room temperature and rapid thermal annealing (RTA). The NCs were formed at temperatures in the range of 500-800 °C. RTA was performed to obtain SiGeSn NCs with surfaces passivated by the embedding HfO2 matrix. The formation of NCs and ß-Sn segregation were discussed in relation to the deposition and processing conditions by employing HRTEM, XRD and Raman spectroscopy studies. The spectral photosensitivity exhibited up to 2000 nm in short-wavelength infrared (SWIR) depending on the Sn composition was obtained. Comparing to similar results on GeSn NCs in SiO2 matrix, the addition of Si offers a better thermal stability of SiGeSn NCs, while the use of HfO2 matrix results in better passivation of NCs increasing the SWIR photosensitivity at room temperature. These results suggest that SiGeSn NCs embedded in an HfO2 matrix are a promising material for SWIR optoelectronic devices.
RESUMEN
In this paper the opto-electrical nature of hydrogenated group IV alloys with optical bandgap energies ranging from 1.0 eV up to 2.3 eV are studied. The fundamental physical principles that determine the relation between the bandgap and the structural characteristics such as material density, elemental composition, void fraction and crystalline phase fraction are revealed. Next, the fundamental physical principles that determine the relation between the bandgap and electrical properties such as the dark conductivity, activation energy, and photoresponse are discussed. The unique wide range of IV valence alloys helps to understand the nature of amorphous (a-) and nanocrystalline (nc-) hydrogenated (:H) germanium films with respect to the intrinsicity, chemical stability, and photoresponse. These insights resulted in the discovery of i) a processing window that results in chemically stable Ge:H films with the lowest reported dark conductivity values down to 4.6·10-4 (Ω ·cm)-1 for chemical vapor deposited Ge:H films, and ii) O, C and Sn alloying approaches to improve the photoresponse and chemical stability of the a/nc-Ge:H alloys.