RESUMEN

(1) Background: Cementation of glass fiber posts to root canals has been associated with various failures, especially debonding. This narrative review aims to present the contemporary concepts concerning the adhesive cementation of glass fiber post and to discuss the optimal management of these factors. (2) Methods: Electronic search was performed in MEDLINE/Pub Med and Google Scholar using selected keywords examining the parameters post length, surface treatment of glass fiber posts, post space preparation and dentin pretreatment, resin cement selection, adhesive systems and hybrid layer formation, and clinical techniques. (3) Results: The search led to the selection of 44 articles. Epoxy resin-based endodontic sealers are recommended and the use of temporary cement in the root canal should be avoided. The minimum length of a glass fiber post adhesively cemented to a root canal is 5 mm. Irrigating the root canals with chlorhexidine, MTAD, or EDTA (alone or in combination with NaOCl) after post space preparation seems to enhance the bond strength. Silane application on the surface of the post seems to be beneficial. Concerning resin cements and adhesive systems, the results were rather inconclusive. Finally, resin cement should be applied inside the root canal with an elongation tip and photoactivation should be delayed. (4) Conclusions: Contemporary concepts of adhesive cementation of glass fiber posts can indeed improve the bond between glass fiber posts, resin cement, and root canal dentin, however, evidence coming from long-term randomized prospective clinical trials is needed in order to obtain safer conclusions.

RESUMEN

Objective: This systematic review aims to compare the clinical longevity of metallic and fiberglass intraradicular posts in teeth with severely compromised crowns, utilizing randomized clinical trials and case reports published in the last eleven years. Material and Methods: The research was conducted on PubMed, Medline, Lilacs, and BBO databases using the first search strategy with the descriptors 'dental posts,' 'longevity,' 'fiberglass-reinforced posts' or 'metallic posts.' The second search strategy involved analyzing the references of articles identified by the first search. Both studies were carried out with stringent inclusion and exclusion criteria. Results: No statistically significant and clinically relevant differences in longevity were observed between metallic and fiberglass posts. Conclusion: The clinical success and durability of the restorative procedure using intraradicular posts primarily depend on the remaining amount around the post (ferrule), the type and position of the tooth in the arch (impacting the masticatory forces exerted on the restored tooth), and the correct application of the cementation technique. It is noteworthy that fiberglass posts offer substantial advantages by presenting a modulus of elasticity similar to dental structure, ensuring a more homogeneous distribution of masticatory forces and reducing the risk of fractures. These findings have practical implications for material selection in restorative procedures involving intraradicular posts.(AU)

Objetivo: Esta revisão sistemática visa comparar a longevidade clínica de pinos intrarradiculares metálicos e de fibra de vidro em dentes com coroas severamente comprometidas, através de estudos clínicos randomizados e relatos de casos, publicados nos últimos onze anos. Material e Métodos: A pesquisa foi conduzida nas bases de dados PubMed, Medline, Lilacs e BBO, utilizando a primeira estratégia de busca com os s 'pinos dentais' e 'longevidade' e 'pinos reforçados com fibra de vidro' ou 'pinos metálicos'. A segunda estratégia de busca consistiu na análise das referências dos artigos identificados pela primeira estratégia. Ambos os estudos foram delineados com critérios rigorosos de inclusão e exclusão. Resultados: Não se constataram diferenças estatisticamente significativas e clinicamente relevantes na longevidade entre pinos metálicos e de fibra de vidro. Conclusão: O êxito clínico e a durabilidade do procedimento restaurador empregando pinos intrarradiculares dependem primordialmente da quantidade de remanescente ao redor do pino (férula), do tipo e posição do dente na arcada (o que impacta nas forças mastigatórias exercidas sobre o dente restaurado) e da aplicação correta da técnica de cimentação.Destaca-se que o pino de fibra de vidro oferece vantagens substanciais ao apresentar módulo de elasticidade similar à estrutura dentária, assegurando uma distribuição mais homogênea das forças mastigatórias e reduzindo o risco de fraturas (AU)

Asunto(s)

RESUMEN

This paper investigates the influence of cavity configuration and post-endodontic restoration on the fracture resistance, failure mode and stress distribution of premolars by using a method of fracture failure test and finite elements analysis (FEA) coupled to Weibull analysis (WA). One hundred premolars were divided into one control group (Gcontr) (n = 10) and three experimental groups, according to the post-endodontic restoration (n = 30), G1, restored using composite, G2, restored using single fiber post and G3, restored using multifilament fiberglass posts (m-FGP) without post-space preparation. Each experimental group was divided into three subgroups according to the type of coronal cavity configuration (n = 10): G1O, G2O, and G3O with occlusal (O) cavity configuration; G1MO, G2MO, and G3MO with mesio-occlusal (MO); and G1MOD, G2MOD, and G3MOD with mesio-occluso-distal (MOD). After thermomechanical aging, all the specimens were tested under compression load, and failure mode was determined. FEA and WA supplemented destructive tests. Data were statistically analyzed. Irrespective of residual tooth substance, G1 and G2 exhibited lower fracture resistance than Gcontr (p < 0.05), whereas G3 showed no difference compared to Gcontr (p > 0.05). Regarding the type of restoration, no difference was highlighted between G1O and G2O, G1MO and G2MO, or G1MOD and G2MOD (p > 0.05), whereas G3O, G3MO, and G3MOD exhibit higher fracture resistance (p < 0.05) than G1O and G2O, G1MO and G2MO, and G1MOD and G2MOD, respectively. Regarding cavity configuration: in G1 and G2, G1O and G2O exhibited higher fracture resistance than G1MOD and G2MOD, respectively (p < 0.05). In G3, there was no difference among G3O, G3MO and G3MOD (p > 0.05). No difference was found among the different groups and subgroups regarding the failure mode. After aging, premolars restored with multifilament fiberglass posts demonstrated fracture resistance values comparable to those of an intact tooth, irrespective of the different type of cavity configuration.

RESUMEN

The purpose of this study was to investigate whether the root perforation repair with mineral aggregate-based cements affects the retention of customized fiberglass posts to bovine intraradicular dentin. Sixty-four bovine mandibular incisors had their root canals endodontically treated and prepared for fiberglass posts luting. Teeth were randomly distributed into four groups (n = 16), according to the cement used for the perforations repair (MTA HP; calcium aluminate cement-CAC; and CAC + calcium carbonate nanoparticles-nano-CaCO3) and control group (no perforation). The groups were redistributed according to the fiberglass posts luting protocol (n = 8): total-etching (TE) (MTA HP/TE; CAC/TE; CAC + CaCO3/TE and control/TE) and self-etching (SE) (MTA HP/SE; CAC/SE; CAC + CaCO3/SE and control/SE). Roots were sectioned into 1.3 mm-thick dentin slices obtaining samples that were submitted to the push-out test in Universal Testing Machine (Instron, Model 4444-0.5 mm/min). The fractured samples were analyzed under stereomicroscope and Scanning Electron Microscope (SEM). CAC/TE and CAC/SE groups had significant difference between the cervical and middle thirds (p < 0.05). When the root thirds were not considered, CAC/SE had the lowest bond strength and differed statistically from CAC/TE and CAC + CaCO3/TE groups, which had the highest mean bond strength values (p < 0.05). The root perforations repair did not affect the bond strength of resin cement/customized fiberglass posts to bovine dentin. The increase in bond strength is luting protocol dependent.

Asunto(s)

RESUMEN

Studies of endodontic outcomes suggest that fracture of the tooth after endodontic therapy may be a greater problem than endodontic reinfection. Immediate full coverage with or without a post and core is the best way to prevent fracture. Unfortunately, in many population areas, due predominantly to cost, this restoration is often delayed, leading to fracture of the tooth. Reviews of several in vitro studies suggest that a composite restoration reinforced with glass fibers, particularly with fiberglass posts laid horizontally in a buccolingual direction, significantly increased the resistance to fracture. This case report describes in detail the placement of horizontal posts in an endodontically treated molar to reinforce the coronal structure. In the discussion, we outlined the agreement of most of the authors on the increase in fracture resistance and the lack of consensus on what constitutes a catastrophic fracture.

Asunto(s)

RESUMEN

AIM: The aim of this study is to assess three protocols for removing a eugenol-based filling endodontic sealer from root dentin and the bond strength of fiberglass posts luted with resin cement. MATERIALS AND METHODS: Sixty single-rooted bovine teeth were prepared and filled with the Endofill endodontic sealer and gutta-percha cones. After 7 days, 9 mm of the filling was removed and divided into five groups (n = 12) according to the cleaning protocol: G1 (negative control), unfilled; G2 (positive control), saline solution; G3, 95% alcohol; G4, amyl acetate; and G5, Largo bur. The canals were hybridized and fiberglass posts were luted with resin cement. They were cross-sectioned in slices of 1 mm and subjected to the push-out test. The other samples were sectioned longitudinally and visualized in a scanning electron microscope (SEM), and the existing chemical elements were quantified by energy dispersive spectroscopy (EDS). The statistical analysis used variance analysis (ANOVA)-one way and Fisher's test, at a 5% significance level. RESULTS: The 95% alcohol was more effective for cleaning the canal, resulting in a clean dentinal surface and bond strength statistically similar to the negative control. The Largo bur was also statistically similar to the negative control, with only a few debris impregnated on the wall. Amyl acetate showed more sealer residues on the canal walls, with a consequent lower bond strength value than the other groups, only higher than the positive control. CONCLUSION: The 95% alcohol and Largo burs may be used after removing the canal filling, so that the bond strength is improved when using the eugenol-based sealer.

Asunto(s)

RESUMEN

Introducción: El uso de postes de fibra de vidrio es el método actual más utilizado para la reconstrucción postendodóncica. Sin embargo, su adhesión sigue siendo impredecible debido al control limitado de su técnica de cementación. Las resinas bulk-fill revelan valores de fuerza flexural similares a la dentina y su empleo en la reconstrucción postendodóncica podría ser una alternativa viable y conservadora. Objetivo: Comparar tres técnicas de reconstrucción postendodóncica al medir su resistencia a fuerzas de desalojo, clasificar el tipo de fractura y falla adhesiva, evaluar su costo y tiempo de trabajo. Material y métodos: Se realizan 18 muestras divididas en tres grupos: grupo 1: poste más cemento de un paso, grupo 2: poste más cemento de tres pasos y grupo 3: reconstrucción postendodóncica con resina bulk-fill. Resultados: En la evaluación de la fuerza al desalojo no se encontró diferencia estadísticamente significativa en los tres grupos. Respecto al comportamiento y falla adhesiva, se encontró una diferencia significativa p < 0.001, favoreciendo a los grupos 2 y 3, por su adhesión en la porción radicular. El tipo de fractura fue restaurable para los tres grupos. Respecto al tiempo y costo, fueron significativamente menores para el grupo 3. Conclusión: En nuestro estudio no existió diferencia significativa en la fuerza al desalojo en los tres grupos; sin embargo, la hubo en el comportamiento, falla adhesiva, costo y tiempo, favoreciendo mayormente al grupo 3. La técnica de reconstrucción con resina puede ser una técnica predecible, suficientemente resistente, conservadora, rápida y de menor costo

Introduction: The use of fiberglass posts is the current method most used for post-endodontic reconstruction. However, its adhesion remains unpredictable due to the limited control of its cementing technique. Bulkfill resins reveal values of flexural strength similar to dentin and their use in post-endodontic reconstruction could be a viable and conservative alternative. Objective: Compare three post-endodontic reconstruction techniques by measuring their resistance to eviction forces, classifying the type of fracture and adhesive failure, evaluating their cost and time of work. Material and methods: 18 samples are divided into 3 groups: group 1: post plus cement of 1 step, group 2: post plus cement of 3 steps and group 3: post-endodontic reconstruction with bulk-fill resin. Results: In the evaluation of the force to the eviction, no statistically significant difference was found in the 3 groups. Regarding the behavior and adhesive failure, a significant difference was found p < 0.001, favoring groups 2 and 3, due to its adhesion in the root portion. The type of fracture was restorable for the 3 groups. Regarding time and cost, they were significantly lower for group 3. Conclusion: In our study there was no significant difference in the force to the eviction in the three groups, however there was in the behavior, adhesive failure, cost and time, favoring mainly the group 3. The technique of reconstruction with resin can be a predictable technique, Sufficiently resistant, conservative, fast and of lower cost (AU)

Asunto(s)

RESUMEN

Introducción: durante el proceso de identificación forense de cadáveres y restos humanos quemados, carbonizados o incinerados, el análisis de los materiales empleados en los diferentes tratamientos odontológicos se constituye en un marcador fehaciente para lograr una identificación positiva. El objetivo de este trabajo fue describir los cambios radiográficos de postes de titanio y de fibra de vidrio cementados, en premolares humanos sometidos a altas temperaturas con fines forenses. Métodos: estudio pseudo-experimental in vitro que observó los cambios radiográficos de los tejidos dentales (esmalte, dentina y cemento), de los materiales de uso endodóncico gutapercha (Wave One® de Dentsply Maillefer®), material de obturación (Top Seal® de Dentsply Maillefer®), material de cementación de los postes (Relyx TM ARC de 3M ESPE®) y de los postes de titanio (Tenax® Endodontic Post System de Coltene®) y fibra de vidrio (Tenax® Fiber Trans de Coltene®) en 30 dientes humanos, sometidos a cinco rangos de temperatura 200, 400, 600, 800 y 1000ºC. Resultados: los tejidos y los materiales dentales estudiados presentan gran resistencia a las altas temperaturas, sin variar considerablemente su macro-estructura (fisuras, grietas, fracturas y fragmentación), de tal manera que los cambios físicos pueden identificarse a través de radiografía convencional, y asociarse a cada rango de temperatura específico. Conclusiones: los postes cementados en premolares humanos presentan gran resistencia a la acción de altas temperaturas, razón por la cual pueden ser visualizados a través de radiografía convencional, contribuyendo con el proceso de identificación y documentación de la necropsia médico-legal de un cadáver o restos humanos que hayan resultado quemados, incinerados o carbonizados

IIntroduction: during the process of forensic identification of corpses and burnt, carbonized, or incinerated human remains, the analysis of materials used in dental treatments is a reliable marker for accurate identification. The objective of this study was to describe the radiographic changes of titanium and fiberglass posts cemented in human premolars subjected to high temperatures for forensic purposes. Methods: this was a pseudo-experimental in vitro study to observe the radiographic changes of dental tissues (enamel, dentin, and cement) and the following endodontic materials: gutta-percha (Wave One® by Dentsply Maillefer®), obturation material (Top Seal® by Dentsply Maillefer®), post cementation material (Relyx TM ARC by 3M ESPE®), titanium posts (Tenax® Endodontic Post System by Coltene®), and fiberglass posts (Tenax® Fiber Trans by Coltene®) in 30 human teeth subject to five temperature ranges: 200, 400, 600, 800, and 1000° C. Results: the studied dental tissues and materials are highly resistant to high temperatures without significantly changing their macrostructure (fissures, cracks, fractures, and fragmentation), in such a way that the physical changes can be identified through conventional radiography and associated with each specific temperature range. Conclusions: posts cemented in human premolars have great resistance to the action of high temperatures, so they can be observed through conventional radiography thus contributing to the process of identification and documentation of the medico-legal autopsy of a corpse or human remains that have been burned, incinerated, or carbonized

Asunto(s)

RESUMEN

This study evaluated the influence of the surface treatments of fiberglass posts on bond strength to root dentin using push-out test. Forty bovine incisor roots were endodontically treated. The surface of the fiberglass posts (Exacto #2, Angelus) were treated using 4 different protocols (n=10): Control - 70% ethanol for 1 min; 37% phosphoric acid for 1 min; 10% hydrofluoric acid for 1 min; and 24% hydrogen peroxide for 1 min. After a silane coupling agent was applied for 1 min and all posts were cemented using self-adhesive resin cement (RelyX Unicem, 3M-ESPE). The roots were sectioned and two 1-mm-thick slices were obtained from each third: cervical, middle and apical. The specimens were subjected to the push-out test with a crosshead speed of 0.5 mm/min. Data were analyzed by repeated measures ANOVA followed by Tukey's HSD tests (=0.05). The surface treatment (p<0.001) and root third region (p=0.007) factors were significant. The retention to root canal was affected by surface treatment type. The post surface treatment with 24% hydrogen peroxide for 1 min yielded significantly higher bond strength when the fiberglass posts were cemented with RelyX Unicem.

Este estudo avaliou a influência de tratamentos de superfície de pinos de fibra de vidro na resistência de união à dentina radicular por meio do teste de push-out. Quarenta raízes de incisivos bovinos foram submetidas a tratamento endodôntico. A superfície dos pinos de fibra de vidro (Exacto #2, Angelus) foram tratadas com 4 protocolos diferentes (n=10): Controle - 70 % de etanol durante 1 min; 37 % de ácido fosfórico durante 1 min, 10% de ácido fluorídrico durante 1 min e 24 % de peróxido de hidrogênio durante 1 min. Depois foi aplicado agente de união silano por 1 min e todos os pinos foram cimentados com cimento resinoso auto-adesivo (RelyX Unicem, 3M- ESPE). As raízes foram seccionadas e foram obtidas duas fatias de 1 mm de espessura em cada terço: cervical, médio e apical. Os espécimes foram submetidos ao teste de push-out com uma velocidade de 0.5 mm/min. Os dados foram analisados pelo teste ANOVA com medidas repetidas, seguido pelo teste de Tukey HSD (=0,05). Os fatores tratamento de superfície (p<0,001) e região do terço radicular (p=0,007) foram significantes; no entanto, a interação entre os dois fatores não foi significante (p=0,827). A retenção ao canal radicular foi afetada pelo tipo de tratamento de superfície. O tratamento de superfície com 24% de peróxido de hidrogênio por 1 min rendeu significativamente maior resistência de união quando os pinos de fibra de vidro foram cimentados com RelyX Unicem.

Asunto(s)

RESUMEN

Este trabalho teve como objetivo avaliar a microdureza de dois cimentos resinosos de polimerização dual (RelyX U100®, 3M-ESPE e Panavia F 2.0®, Kuraray), empregados na cimentação de pinos de fibra de vidro (Fibrekor-Jeneric® Pentron) variando o modo de polimerização em químico, fotoativação imediata ou tardia após 5min através de luz halógena, avaliando também o efeito do armazenamento em água deionizada por três meses. Este trabalho testou as seguintes hipóteses nulas: não há diferença nos valores de microdureza entre os cimentos, modo de polimerização, efeito do armazenamento e entre os terços radiculares. Sessenta raízes de incisivos bovinos, com 16mm de comprimento cérvico-apical, tiveram seus condutos obturados e, posteriormente, preparados para cimentação do pino intracanal. Os espécimes foram divididos em 6 grupos (n = 10), cada um subdividido em 2 subgrupos com 5 espécimes para cada cimento. Os pinos foram cimentados de acordo com o protocolo descrito por cada fabricante. No grupo A1, os espécimes foram mantidos em ambiente à prova de luz para que ocorresse apenas a polimerização química. No grupo B1, os espécimes foram cimentados e submetidos à fotoativação imediata, e, no grupo C1, realizou-se a fotoativação após 5 minutos. As raízes foram seccionadas longitudinalmente, para que a linha de cimento pudesse ser exposta e os testes de microdureza realizados. Após 7 dias, as médias de microdureza (± desvio padrão) foram obtidas, para os terços cervical, médio e apical, respectivamente: A1 (Panavia) - 41,25 ±3,38 / 38,17±1,74 / 35,63±1,73; A1 (U100) - 59,43±4,32 / 52,14±3,00 / 50,27±4,13; B1 (Panavia) - 75,29±4,84 / 60,36±6,76 / 48,97±3,33; B1 (U100) 62,41±6,83 / 53,99±4,74 / 49,04±2,20; C1 (Panavia) - 70,22±93 / 61,00±4,48 / 56,46±7,51; C1 (U100) - 62,40±6,66 / 53,69±2,00 / 51,54±2,18.

Para os grupos armazenados em água, os valores médios de microdureza (± desvio padrão) obtidos nos 3 grupos, químico (grupo A2), fotoativado imediatamente (grupo B2) e fotoativado tardiamente (grupo C2), nos terços cervical, médio e apical, respectivamente, foram: A2 (Panavia) - 37,17±1,38 / 35,01±0,74 / 34,10±2,37; A2 (U100) - 52,39±2,00 / 52,13±3,01 / 51,06±1,48; B2 (Panavia) - 63,01±2,17 / 55,94±2,10 / 48,55±1,62; B2 (U100) - 58,81±2,34 / 55,19±1,42 / 55,71±3,17; C2 (Panavia) - 56,99±1,21 / 51,29±1,81 / 48,29±3,00; C2 (U100) - 59,02±2,04 / 57,05±2,04 / 54,95±1,05. Os resultados foram submetidos ao teste ANOVA a 4 critérios (cimento, modo de polimerização, armazenamento e terços), que detectou diferenças estatísticas entre os grupos, e o teste de Tukey foi aplicado para comparações individuais. Os resultados mostraram que: a fotoativação com luz halógena promoveu um aumento significativo nos valores de microdureza para o cimento Panavia; o armaz namento em água por três meses reduziu os valores de microdureza para a maioria dos grupos, sendo que o cimento o U100 apresentou menor variação de dureza quando comparado ao Panavia; os terços que receberam maior intensidade de luz halógena tiveram maior aumento de microdureza para ambos os cimentos, especialmente para o cimento Panavia. Conclui-se, portanto, que as hipóteses de nulidade propostas foram rejeitadas.

The objective of this study was to evaluate the microhardness of two dual cure resin cements (RelyX - U100®, 3M-ESPE and Panavia F 2.0®, Kuraray), used for fiberglass posts (Fibrekor ® - Jeneric Pentron) cementation. Chemical cure and a halogen immediate and late light cure source were compared, and the effect of storage in deionized water for three months was also evaluated. This study tested the following null hypotheses: there is no difference between the microhardness values for each dual cure resin cement, cure source type, storage time, or root thirds. Sixty bovine incisor roots 16mm long had their roots restored and then prepared for post cementation. The specimens were divided into 6 groups (n = 10), and each group was subdivided into 2 subgroups with 5 specimens for each cement. The posts were cemented according to manufacturers instructions. In group A1, the specimens were kept in a light-proof environment to ensure only a chemical cure. In group B1, the specimens were restored and subjected to immediate light curing, and in group C1, light curing was performed after 5 minutes. The roots were longitudinally sectioned to expose the cement line and perform microhardness tests. After 7 days, the average microhardness (± standard deviation) values were obtained for the cervical, medium and apical thirds, respectively: A1 (Panavia ) - 41,25±3,38 / 38,17±1,74 / 35,63±1,73; A1 (U100) - 59,43±4,32 / 52,14±3,00 / 50,27±4,13; B1 (Panavia) - 75,29±4,84 / 60,36±6,76 / 48,97±3,33; B1 (U100) - 62,41±6,83 / 53,99±4,74 / 49,04±2,20; C1 (Panavia) - 70,22±1,93 / 61,00±4,48 / 56,46±7,51; C1 (U100) - 62,40±6,66 / 53,69±2,00 / 51,54±2,18...

Asunto(s)