RESUMEN

OBJECTIVES: To synthesize casein enzymatic hydrolysate (CEH)-laden gelatin methacryloyl (GelMA) fibrous scaffolds and evaluate the cytocompatibility and anti-inflammatory effects on dental pulp stem cells (DPSCs). MATERIALS AND METHODS: GelMA fibrous scaffolds with 10%, 20%, and 30% CEH (w/w) and without CEH (control) were obtained via electrospinning. Chemo-morphological, degradation, and mechanical analyses were conducted to evaluate the morphology and composition of the fibers, mass loss, and mechanical properties, respectively. Adhesion/spreading and viability of DPSCs seeded on the scaffolds were also assessed. The anti-inflammatory potential on DPSCs was tested after the chronic challenge of cells with lipopolysaccharides (LPS), followed by treatment with extracts obtained after immersing the scaffolds in α-MEM. The synthesis of the pro-inflammatory cytokines IL-6, IL-1α, and TNF-α was measured by ELISA. Data were analyzed by ANOVA/post-hoc tests (α = 5%). RESULTS: CEH-laden electrospun fibers had a larger diameter than pure GelMA (p ≤ 0.036). GelMA scaffolds laden with 20% and 30% CEH had a greater mass loss. Tensile strength was reduced for the 10% CEH fibers (p = 0.0052), whereas no difference was observed for the 20% and 30% fibers (p ≥ 0.6736) compared to the control. Young's modulus decreased with CEH (p < 0.0001). Elongation at break increased for the 20% and 30% CEH scaffolds (p ≤ 0.0038). Over time, DPSCs viability increased across all groups, indicating cytocompatibility, with CEH-laden scaffolds exhibiting greater cell viability after seven days (p ≤ 0.0166). Also, 10% CEH-GelMA scaffolds decreased the IL-6, IL-1α, and TNF-α synthesis (p ≤ 0.035). CONCLUSION: CEH-laden GelMA scaffolds facilitated both adhesion and proliferation of DPSCs, and 10% CEH provided anti-inflammatory potential after chronic LPS challenge. CLINICAL RELEVANCE: CEH incorporated in GelMA fibrous scaffolds demonstrated the potential to be used as a cytocompatible and anti-inflammatory biomaterial for vital pulp therapy.

Asunto(s)

RESUMEN

Preserving vital pulp in cases of dental pulpitis is desired but remains challenging. Previous research has shown that bioactive glass (BG) possesses notable capabilities for odontogenic differentiation. However, the immunoregulatory potential of BG for inflamed pulp is still controversial, which is essential for preserving vital pulp in the context of pulpitis. This study introduces a novel approach utilizing polydopamine-coated BG (BG-PDA) which demonstrates the ability to alleviate inflammation and promote odontogenesis for vital pulp therapy. In vitro, BG-PDA has the potential to induce M2 polarization of macrophages, resulting in decreased intracellular reactive oxygen species levels, inhibition of pro-inflammatory factor, and enhancement of anti-inflammatory factor expression. Furthermore, BG-PDA can strengthen the mitochondrial function in macrophages and facilitate odontogenic differentiation of human dental pulp cells. In a rat model of pulpitis, BG-PDA exhibits the capacity to promote M2 polarization of macrophages, alleviate inflammation, and facilitate dentin bridge formation. This study highlights the notable immunomodulatory and odontogenesis-inducing properties of BG-PDA for treating dental pulpitis, as evidenced by both in vitro and in vivo experiments. These results imply that BG-PDA could serve as a promising biomaterial for vital pulp therapy.

RESUMEN

AIM: The European Society of Endodontology outlines best practices for the management of deep caries and the pulp. Despite evidence supporting vital pulp treatments (VPTs) as predictable alternatives to conventional endodontic treatment, studies have shown they are not widely adopted in the UK. This study aimed to explore the barriers to implementation of VPTs by primary care general dental practitioners (GDPs). METHODOLOGY: Qualitative one-to-one semi-structured online interviews were conducted with purposively sampled UK GDPs. Interview transcripts were analysed using reflexive thematic analysis. Recurring themes were iteratively refined as additional transcripts were reviewed. RESULTS: Eleven participants were interviewed. A range of barriers to the provision of VPTs were identified, which aligned with two core themes: 'Motivational barriers to service provision' and 'Educational access & opportunities'. Sub-themes included lack of access to materials and equipment, deficiencies in knowledge of treatment (including protocols, outcomes and prognosis), lack of confidence (in treatment efficacy and clinical ability), time constraints and public dental service funding and remuneration. CONCLUSIONS: This study identifies barriers to the widespread adoption of VPTs among primary care GDPs in public and private settings. Economic constraints, practitioner confidence, time limitations and educational gaps are key challenges. Addressing these may require systemic changes such as policy interventions, education and improved resource allocation.

RESUMEN

Aim: To assess clinically and histologically the efficacy of TheraCal LC and Biodentine as Direct Pulp Capping agents. Materials and Method: Sixty caries-free maxillary first premolar teeth which were scheduled for orthodontic extraction were selected for the study and were divided equally into Group 1 (Theracal LC) and Group 2 (Biodentine). Thermal and electric pulp testing was performed on the teeth to assess pulp vitality followed by tooth preparation to expose pulp horns under local anesthesia. After achieving hemostasis, the direct pulp capping agent was placed and composite restoration was done. All the teeth were evaluated and compared in terms of clinical and histological findings after 6 weeks. The statistical analysis used was the Kruskal-Wallis test. Results: Teeth with Theracal LC showed no sensitivity to heat, cold, or percussion, whereas sensitivity to heat, cold, or percussion was noted with Biodentine. Histological evaluation revealed that TheraCal LC has higher efficiency in complete dentin bridge formation, had maximum dentin thickness, and showed minimal or no pulpal disorganization and pulpal inflammation as compared to Biodentine. Conclusion: TheraCal LC proves to be a promising future as a direct pulp capping agent.

RESUMEN

Aim: The aim of this study was to identify and analyze the most cited articles on vital pulp therapies. Methodology: Bibliographical data related to the abstract, citations, keywords, and other relevant information was extracted using different combinations of keywords. Further evaluation and visualization of the selected data were performed with the help of various tools, including MS Excel, Microsoft Word, Google open refine, BibExcel, and VOS viewer. An initial search revealed 91 documents, of which 40 were chosen for further analysis. We used the Kolmogorov-Smirnov test and Spearman correlation coefficient test, and our adopted significance level was p < 0.05. Results: In total, the articles received 1,905 citations, with six of them receiving at least 100 citations. Among the top 40 articles, the United States of America (10 articles) and Ireland (6 articles) were the countries with the highest number of cited articles. The journals "Journal of Endodontics" (14 articles; 650 citations) and "International Endodontic Journal" (13 articles; 577 citations) published most of the articles among the 50 most cited ones. Duncan H. was the author with the highest number of works cited (11 articles; 339 citations). Of the articles, systematic reviews accounted for 32%, literature reviews for 14%, in vitro experimental studies for 12%, clinical trials for 8%. Among the biomaterials used in vital pulp therapies, mineral trioxide aggregate (MTA) was discussed in 37 articles (74%), followed by calcium hydroxide, mentioned in 30 studies (60%). Interestingly, the publication year did not demonstrate a significant impact on citation count. Conclusion: The present study provided a detailed list of the top 50 most cited and classic articles on vital pulp therapies. This will help researchers, students, and clinicians in the field of endodontics with an impressive source of information.

RESUMEN

This study aimed to develop gelatin methacryloyl (GelMA)-injectable hydrogels incorporated with 58S bioactive glass/BG-doped with strontium for vital pulp therapy applications. GelMA hydrogels containing 0% (control), 5%, 10%, and 20% BG (w/v) were prepared. Their morphological and chemical properties were evaluated by scanning electron microscopy/SEM, energy dispersive spectroscopy/EDS, and Fourier transform infrared spectroscopy/FTIR (n = 3). Their swelling capacity and degradation ratio were also measured (n = 4). Cell viability (n = 8), mineralized matrix formation, cell adhesion, and spreading (n = 6) on DPSCs were evaluated. Data were analyzed using ANOVA/post hoc tests (α = 5%). SEM and EDS characterization confirmed the incorporation of BG particles into the hydrogel matrix, showing GelMA's (C, O) and BG's (Si, Cl, Na, Sr) chemical elements. FTIR revealed the main chemical groups of GelMA and BG, as ~1000 cm-1 corresponds to Si-O and ~1440 cm-1 to C-H. All the formulations were degraded by day 12, with a lower degradation ratio observed for GelMA+BG20%. Increasing the concentration of BG resulted in a lower mass swelling ratio. Biologically, all the groups were compatible with cells (p > 0.6196), and cell adhesion increased over time, irrespective of BG concentration, indicating great biocompatibility. GelMA+BG5% demonstrated a higher deposition of mineral nodules over 21 days (p < 0.0001), evidencing the osteogenic potential of hydrogels. GelMA hydrogels incorporated with BG present great cytocompatibility, support cell adhesion, and have a clinically relevant degradation profile and suitable mineralization potential, supporting their therapeutic potential as promising biomaterials for pulp capping.

RESUMEN

The main purpose of vital pulp therapy (VPT) is to preserve the integrity and function of the pulp. A wide variety of materials and techniques have been proposed to improve treatment outcomes, and among them, the utilization of lasers has gained significant attention. The application of lasers in different stages of VPT has witnessed remarkable growth in recent years, surpassing previous approaches.This study aimed to review the applications of lasers in different steps of VPT and evaluate associated clinical and radiographic outcomes. An electronic search using Scopus, MEDLINE, Web of Science and Google Scholar databases from 2000 to 2023 was carried out by two independent researchers. The focus was on human studies that examined the clinical and/or radiographic effects of different laser types in VPT. A total of 4243 studies were included in this narrative review article. Based on the compiled data, it can be concluded that although current literature suggests laser may be proposed as an adjunct modality for some procedural steps in VPT, more research with standardized methodologies and criteria is needed to obtain more reliable and conclusive results.

Asunto(s)

RESUMEN

AIM: Conventional root resection in periodontally compromised furcation-involved maxillary molars requires preceding endodontic treatment and is therefore associated with loss of tooth vitality, higher invasiveness, treatment time and costs, and the risk of endodontic complications. Vital root resection (VRR) could overcome these disadvantages while establishing stable periodontal and endodontic conditions. This case series aimed to introduce the concept of one-stage VRR with radicular retrograde partial pulpotomy (VRRretro). SUMMARY: Seven vital maxillary molars with residual probing pocket depths (PPD) ≥ 6 mm and furcation ≥ class 2 of five patients with stage III/IV periodontitis were treated with VRRretro using mineral trioxide aggregate. Teeth with residual through-and-through furcations were additionally tunnelled. Follow-up up to 2.5 years postoperatively during supportive periodontal care included full periodontal status, percussion and thermal sensitivity testing. Periapical radiographs were obtained to rule out possible periradicular radiolucencies. All seven treated molars were in-situ at an average of 26.84 ± 5.37 months postoperatively and were clinically and radiographically inconspicuous independent of tooth position, the resected root, the need for tunnelling and the restorative status. The mean PPD on the seven treated molars was 4.02 ± 0.85 mm (6-10 mm) preoperatively and 2.62 ± 0.42 mm (3-4 mm) at the last follow-up. Clinical attachment level and bleeding on probing could also be decreased. The teeth showed no mobility over time and furcations class 2 were reduced to class 1 while the tunnelled furcations were accessible with interdental brushes. All molars reacted negatively to percussion and positively to thermal sensitivity testing. KEY LEARNING POINTS: In carefully selected cases considering patient- and tooth-related factors, VRRretro could be a promising treatment option to establish stable periodontal and endodontic conditions in furcation-involved maxillary molars while preserving tooth vitality.

Asunto(s)

RESUMEN

BACKGROUND: This systematic review aimed to investigate whether vital pulp therapy and root canal treatment (RCT) promote different postoperative pain. STUDIES REVIEWED: The authors searched PubMed, Cochrane Library, Embase, and Latin American and Caribbean Health Sciences Literature databases for studies published through June 30, 2022. The authors included randomized clinical trials if they reported on the assessment of postoperative pain after direct pulp capping, partial pulpotomy, pulpotomy, or single-visit RCT. The authors assessed the frequency of no, mild, moderate, and severe postoperative pain. They conducted meta-analyses to compare postoperative pain after full pulpotomy (PULP) and RCT. RESULTS: The qualitative synthesis included 57 studies, and the authors conducted meta-analysis of 3. PULP leads to more asymptomatic cases (relative risk [RR], 1.06; 95% CI, 1.01 to 1.11; P < .01; I2 = 67%) and to a lower occurrence of mild (RR, 0.89; 95% CI, 0.79 to 0.99; P < .04; I2 = 37%) and moderate (RR, 0.70; 95% CI, 0.51 to 0.95; P < .02; I2 = 57%) postoperative pain than RCT. The frequency of severe pain was very low for both vital pulp therapy and RCT. Moderate to severe postoperative pain was more common at 48 hours through 72 hours after RCT and up to 36 hours after PULP. Pain intensity after PULP was higher using calcium-enriched material compared with using mineral trioxide aggregate at 12, 18, and 36 hours (P < .001). PRACTICAL IMPLICATIONS: PULP showed a significantly higher incidence of no pain and a lower incidence of mild and moderate pain than single-visit RCT. Clinical decisions for RCT or PULP should not be based on differences in postoperative pain. When analgesia is indicated, it probably should be limited to a short time after PULP.

Asunto(s)

RESUMEN

BACKGROUND: The aim of the present study was to investigate the micro-shear bond strength (µSBS) of various restorative materials applied on two different fast-setting calcium silicate-based materials and to evaluate the effect of restoration time on µSBS. METHODS: A total of 180 acrylic blocks with a cavity in the center were randomly divided into 2 main groups according to the capping material to be used (Biodentine or RetroMTA). The specimens were also randomly divided into 3 groups according to the restoration time (3 min, 12 min, 24 h). After the specified waiting periods, glass hybrid material (EQUIA Forte HT), resin composite (Filtek Z550) and light-cured calcium silicate material (Theracal LC) were placed on the specimens with tygon tubes. The specimens were kept for 24 h and then subjected to µSBS test. Statistical analysis was performed by 3-way ANOVA followed by Tukey test for pairwise comparisons (α = 0.05). RESULTS: There is a statistically significant difference (p < 0.05) between the µSBS values obtained by applying resin composite on RetroMTA after different setting times (24 h > 12 min > 3 min). The µSBS obtained for the Biodentine-resin composite at the end of the 3 min setting time is significantly lower (p < 0.05) than the µSBS values at 12 min and 24 h. For both calcium silicate cements, at the end of all time periods, the µSBS obtained when resin composite was applied at the end was higher than the other materials (p < 0.05). CONCLUSIONS: For Biodentine-resin composite bonding, the manufacturer's recommendation of 12 min can be considered an appropriate time, whereas for RetroMTA-resin composite bonding, the µSBS increased as the waiting time increased. Regardless of the waiting time, it is recommended to prefer direct composite resin restoration over Biodentine and RetroMTA.

Asunto(s)

RESUMEN

ABSTRACT Objective: To evaluate the clinical and radiographic response of pulp-dentin complex after selective caries removal with or without pulp lining in primary teeth. Material and Methods: Twenty-four primary molars with deep occlusal caries lesions and without pulpal alterations were selected from children, both genders, aged between 5 and 9 years old. After selective caries removal, the teeth were divided into three groups: without cavity liner (Group I), calcium hydroxide cement - CH (Group II), and Mineral trioxide aggregate - MTA (Group III). The final restoration was performed with resin-modified glass ionomer cement. Clinical and radiographic assessments were conducted at 6-month follow-up. The Kappa test determined intraexaminer reliability. Fisher's exact test evaluated intergroup comparisons (p<0.05). Results: All teeth showed clinical and radiographic success at the 6-month follow-up without statistically significant differences (p>0.05). Conclusion: Selective caries removal without cavity lining was acceptable for deep caries lesions in primary teeth.

Asunto(s)

RESUMEN

Abstract Several materials have been developed to preserve pulp vitality. They should have ideal cytocompatibility characteristics to promote the activity of stem cells of human exfoliated deciduous teeth (SHED) and thus heal pulp tissue. Objective To evaluate the cytotoxicity of different dilutions of bioceramic material extracts in SHED. Methodology SHED were immersed in αMEM + the material extract according to the following experimental groups: Group 1 (G1) -BBio membrane, Group 2 (G2) - Bio-C Repair, Group 3 (G3) - MTA Repair HP, Group 4 (G4) - TheraCal LC, and Group 5 (G5) - Biodentine. Positive and negative control groups were maintained respectively in αMEM + 10% FBS and Milli-Q Water. The methods to analyze cell viability and proliferation involved MTT and Alamar Blue assays at 24, 48, and 72H after the contact of the SHED with bioceramic extracts at 1:1 and 1:2 dilutions. Data were analyzed by the three-way ANOVA, followed by Tukey's test (p<0.05). Results At 1:1 dilution, SHED in contact with the MTA HP Repair extract showed statistically higher cell viability than the other experimental groups and the negative control (p<0.05), except for TheraCal LC (p> 0.05). At 1:2 dilution, BBio Membrane and Bio-C showed statistically higher values in intra- and intergroup comparisons (p<0.05). BBio Membrane, Bio-C Repair, and Biodentine extracts at 1:1 dilution showed greater cytotoxicity than 1:2 dilution in all periods (p<0.05). Conclusion MTA HP Repair showed the lowest cytotoxicity even at a 1:1 dilution. At a 1:2 dilution, the SHED in contact with the BBio membrane extract showed high cell viability. Thus, the BBio membrane would be a new non-cytotoxic biomaterial for SHED. Results offer possibilities of biomaterials that can be indicated for use in clinical regenerative procedures of the dentin-pulp complex.

RESUMEN

OBJECTIVES: To assess the effect of Tideglusib and CHIR99021 small molecules on the odontogenic differentiation potential of human dental pulp stem cells (hDPSCs) via Wnt/ß-catenin pathway activation. METHODOLOGY: hDPSCs were isolated from impacted third molars indicated for extraction and were characterized by flow cytometry. hDPSCs were then induced to differentiate into odontogenic lineage in the presence of Tideglusib and CHIR99021. Odontogenic differentiation was evaluated using Alizarin Red stain and RT-PCR for expression of odontogenic specific differentiation markers: DSPP, DMP1, ALP, OPN, and RUNX2 in relation to undifferentiated cells. RT-PCR was also conducted to assess the expression of Wnt/ß-catenin pathway activation marker (AXIN2). One-way ANOVA Kruskal-Wallis test was used for statistical analysis. RESULTS: Wnt/ß-catenin pathway was successfully activated by Tideglusib and CHIR99021 in hDPSCs where AXIN2 was significantly upregulated. Successful odontogenic differentiation was confirmed by Alizarin Red staining of calcified nodules. RT-PCR for odontogenic differentiation markers DSPP, DMP1, and RUNX expression by hDPSCs induced by CHIR99021 was higher than that expressed by hDPSCs induced by Tideglusib, whereas expression of OPN and ALP was higher in Tideglusib-induced cells than in CHIR99021-induced cells. CONCLUSIONS: Both small molecules successfully induced odontogenic differentiation of hDPSCs through Wnt/ß-catenin pathway activation. CLINICAL RELEVANCE: These findings suggest that Tideglusib and CHIR99021 can be applied clinically in pulp regeneration to improve strategies for vital pulp regeneration and to promote dentine repair.

Asunto(s)

RESUMEN

In recent years, alternative pulpal therapies targeting dentinogenesis signaling pathways using different peptides have been investigated. The aim of this study was to verify the effectiveness of poly(aspartic acid), pAsp, in dentin regeneration using an animal model. METHODS: Mechanical pulp exposure was performed in the upper molars of 56 Wistar rats, randomly divided as follows (n = 14): control (no treatment); MTA group-pulp capping with mineral trioxide aggregate (MTA Angelus); pAsp group-application of 20 µL of pAsp solution (25 mg·mL-1); MTA+pAsp group-application of MTA mixed with pAsp (5:1 by mass). Animals were euthanized after 7 or 21 days. Histological sections were submitted to hematoxylin-eosin and Brown and Brenn staining and immunohistochemical analysis for osteopontin (OPN) and dentin matrix protein 1 (DMP 1). RESULTS: At 7 days, an acute inflammatory infiltrate and the presence of disorganized mineralized tissue were observed in all groups. At 21 days, the quality and thickness of the reparative dentin in treated groups were superior to the control, and bacterial contamination was observed in two MTA-pAsp specimens. While all treated groups showed intense immunostaining for OPN at 21 days, only the pAsp group expressed DMP 1, indicating the presence of fully differentiated odontoblast-like cells. CONCLUSION: Poly(aspartic) acid promoted dentin regeneration in rat molars in the absence of an additional calcium source and may be an alternative to MTA as a pulp-capping agent.

RESUMEN

BACKGROUND: Minimally invasive endodontics is recommended for young, immature teeth to preserve healthy pulp and dentin tissue. OBJECTIVES: The aim of the study was to examine the cold sensitivity of immature teeth that received photobiomodulation (PBM) after vital pulp therapy (VPT). MATERIAL AND METHODS: The study followed the STROBE guidelines and included 123 healthy patients aged 8-13. The immature teeth (incisors, premolars and molars) that qualified for VPT received the bioceramic material - Biodentine. In this experiment, teeth were treated immediately and at 24 h post-VPT with a 635-nm diode laser using a power of 100 mW, a power density of 200 mW/cm2 and a total energy of 4 J (PBM group, n = 43), while those not treated were the control group (n = 43). The tooth sensitivity to cold was measured using a visual analogue scale (VAS) before and at 6 h, 1 day, 7, 30, and 90 days after treatment. The predictor variable was PBM skills regarding the ability to decrease cold sensitivity after VPT. The primary endpoint was the time to reverse hypersensitivity to cold, and the secondary endpoint was the occurrence of possible side effects. The Mann-Whitney U test, Friedman test along with Dunn's post hoc test, and the χ2 test were used to investigate tooth sensitivity. RESULTS: Eighty-six immature permanent teeth of 86 children were included in the study. It was shown that the difference was significant for sensitivity to a cold stimulus between the groups at 6 h, 24 h, 7 days, and 30 days, but no difference was found preoperatively and at 90 days (6 h, 24 h, 7 days, and 30 days, p < 0.001, and 90 days, p = 0.079). However, patients in both groups reported a decrease in discomfort provoked by cold stimuli throughout the follow-up period. CONCLUSIONS: Photobiomodulation decreased postoperative sensitivity and was more acceptable for patients. Further randomized clinical studies with placebo-controlled groups are needed.

RESUMEN

Vital pulp therapy (VPT) is primarily intended to preserve the vitality of pulp tissues, which have been exposed for any reason. Various materials and techniques have been proposed to improve treatment outcomes, including the use of lasers. This study aimed to review the histological results of different dental lasers including low-level lasers, carbon dioxide (CO2), erbium-doped yttrium aluminum garnet laser (Er:YAG), neodymium-doped yttrium aluminum garnet (Nd:YAG), erbium, chromium:yttrium-scandium-gallium-garnet (Er,Cr:YSGG) lasers, and diode lasers for VPT. This focused review included a comprehensive electronic search of Scopus, MEDLINE, Web of Science, and Google Scholar databases from 2000 to 2022 by two independent investigators. Different combinations of keywords were used, and reference mining of related papers was done. The review included studies related to histologic evaluation of laser-assisted vital pulp therapy that stated the laser parameters that were used. Articles with radiographic or clinical assessments or articles lacking necessary data were excluded. Non-English articles were excluded unless their abstract was in English and encompassed the necessary data. Most studies indicated the efficacy of lasers for reduction of inflammation, acceleration of healing, and increasing the thickness of dentinal bridge. According to the evidence, lasers used in combination with pulp capping agents are beneficial to enhance the success rate of VPT.

Asunto(s)

RESUMEN

OBJECTIVES: This study aims to formulate metronidazole liquid nanocapsules (MTZLNC) and evaluate their effect on the physicochemical and biological properties of calcium silicate-based bioactive endodontic cements, in vitro. METHODS: A MTZLNC suspension was formulated by deposition of the preformed polymer and characterized by laser diffraction and high-performance liquid chromatography (HPLC). Calcium silicate (CS) was mixed with a radiopaque agent (calcium tungstate - CaWO4), at 10 wt%, to produce the cement powder. Cements liquids were used with two concentrations of MTZLNC suspension: 0.3 mg/ml and 0.15 mg/ml. Cements prepared with distilled water were used as the control. The radiopacity, setting time, and flow were evaluated following ISO 6876:2012. The compressive strength analysis was conducted according to ISO 9917:2007. pH and mineral deposition were evaluated after immersion in simulated body fluid (SBF). Cell behavior was evaluated by the viability of pre-osteoblastic cells and pulp fibroblasts by SRB and MTT and the antibacterial activity against Enterococcus faecalis was analyzed immediately and after nine months of water storage. RESULTS: MTZLNCs were formulated with a median diameter of 148 nm and 83.44 % load efficiency. Increased flow and reduced strength were observed for both MTZLNCs concentrations. The incorporation of MTZLNCs maintained the ability of cements to increase pH media and promote mineral deposition over the samples, without promoting cytotoxicity. A 2 log10 reduction in E. faecalis CFU was observed immediately and after nine months in water storage. CONCLUSION: The formulation of MTZLNCs allowed the development of antibacterial calcium silicate-based-cements with suitable physicochemical properties and bioactivity, with a reduction in mechanical strength. The 0.3 mg/ml concentration in cements liquid promoted effective and sustainable antibacterial activity.

Asunto(s)

RESUMEN

INTRODUCTION: Tumor necrosis factor (TNF)-α is a pro-inflammatory cytokine that promotes biomineralization in vitro in dental pulp cells. However, the role of TNF-α-TNF receptor 1 (TNFR1) signaling in reparative dentin formation and related inflammatory pathways is not known. Therefore, the aim of this study was to evaluate the role of the TNF-α-TNFR1 axis in dental pulp repair following pulp capping in vivo. METHODS: Dental pulp repair response of genetically deficient TNF-α receptor-1 mice (TNFR1-/-; n = 20) was compared with that of C57Bl6 mice (wild type [WT]; n = 20). Pulp capping was performed with mineral trioxide aggregate on the mandibular first molars of mice. After 7 and 70 days, tissues were collected and stained with hematoxylin and eosin for histopathological and histometric evaluation, and assessed by the Brown and Brenn methods for histomicrobiological analysis and by immunohistochemistry to localize TNF-α, Runt-related transcription factor 2, Dentin Sialoprotein (DSP) and Osteopontin (OPN) expression. RESULTS: Compared with WT mice, TNFR1-/- mice showed significantly decreased reparative dentin formation with a lower mineralized tissue area (P < .0001). Unlike WT mice, TNFR1-/- mice also exhibited significant dental pulp necrosis, neutrophil recruitment, and apical periodontitis formation (P < .0001) without bacterial tissue invasion. TNFR1-/- animals further exhibited decreased TNF-α, DSP, and OPN expression (P < .0001), whereas Runt-related transcription factor 2 expression was unchanged (P > .05). CONCLUSION: The TNF-α-TNFR1 axis is involved in reparative dentin formation following dental pulp capping in vivo. Genetic ablation of TNFR1 modified the inflammatory process and inhibited the expression of the DSP and OPN mineralization proteins, which culminated in dental pulp necrosis and development of apical periodontitis.

Asunto(s)

RESUMEN

This mini-review was conducted to present an overview of the use of exosomes in regenerating the dentin-pulp complex (DPC). The PubMed and Scopus databases were searched for relevant articles published between January 1, 2013 and January 1, 2023. The findings of basic in vitro studies indicated that exosomes enhance the proliferation and migration of mesenchymal cells, as human dental pulp stem cells, via mitogen-activated protein kinases and Wingless-Int signaling pathways. In addition, they possess proangiogenic potential and contribute to neovascularization and capillary tube formation by promoting endothelial cell proliferation and migration of human umbilical vein endothelial cells. Likewise, they regulate the migration and differentiation of Schwann cells, facilitate the conversion of M1 pro-inflammatory macrophages to M2 anti-inflammatory phenotypes, and mediate immune suppression as they promote regulatory T cell conversion. Basic in vivo studies have indicated that exosomes triggered the regeneration of dentin-pulp-like tissue, and exosomes isolated under odontogenic circumstances are particularly strong inducers of tissue regeneration and stem cell differentiation. Exosomes are a promising regenerative tool for DPC in cases of small pulp exposure or for whole-pulp tissue regeneration.

RESUMEN

INTRODUCTION: Direct pulp capping (DPC) procedures require the placement of a bioactive material over an exposure site without selective pulp tissue removal. This web-based multicentered survey had 3 purposes: (1) to investigate the factors that affect clinicians' decisions in DPC cases, (2) to determine which method of caries removal is preferred, and (3) to evaluate the preferred capping material for DPC. METHODS: The questionnaire comprised 3 sections. The first part comprised questions regarding demographic features. The second part comprised questions on how treatment plans change according to factors such as nature, location, number and size of the pulp exposure, and patients' age. The third part composed of questions on the common materials and techniques used in DPC. To estimate the effect size, the risk ratio (RR) and 95% confidence interval (CI) were calculated using a meta-analysis software. RESULTS: A tendency toward more invasive treatment was observed for the clinical scenario with carious-exposed pulp (RR = 2.86, 95% CI: 2.46, 2.32; P < .001) as opposed to the clinical scenario with 2 pulp exposures (RR = 1.38, 95% CI: 1.24, 1.53; P < .001). Complete caries removal was significantly preferred to selective caries removal (RR = 4.59, 95% CI: 3.70, 5.69; P < .001). Among the capping materials, calcium silicate-based materials were preferred over calcium hydroxide-based materials (RR = 0.58, 95% CI: 0.44, 0.76; P < .05). CONCLUSIONS: While carious-exposed pulp is the most important factor in clinical decisions regarding DPC, the number of exposures has the least impact. Overall, complete caries removal was preferred over selective caries removal. In addition, the use of calcium silicate-based materials appears to have replaced calcium hydroxide-based materials.

Asunto(s)