RESUMEN
OBJECTIVES: The aim of this study was to evaluate the tooth crown discoloration induced by commonly used and new-generation endodontic sealers after 1 month and 1 and 3 years. MATERIALS AND METHODS: The crowns of 60 extracted incisors were cut and the pulp chambers were cleaned. The specimens were divided randomly into four groups (n = 15 each). Pulp chambers were filled with Pulpispad in group 1, AH26 in group 2, MTA Fillapex in group 3, and EndoREZ in group 4. Specimen color was measured with a spectrophotometer before and after sealer placement. Commission International de L'Eclairage's (CIE's) lighteness (L*), red-green (a*), yellow-blue (b*) color system values and color difference (ΔE) were recorded at 1 month and 1 and 3 years. Data were analyzed using repeated-measures analysis of variance and Tukey's honestly significant difference test (α = 0.05). RESULTS: All sealers caused discoloration. At 1 month, ΔE values were significantly higher in groups 1 and 2 than in groups 3 and 4 (p < 0.05). At 1 year, ΔE values were significantly lower in group 3 than in the other groups (p < 0.05). At 3 years, ΔE values were significantly higher in group 1 than in the other groups (p < 0.05). CONCLUSIONS: All tested sealers induced varying chromatic alterations. After root canal obturation, thorough debridement of sealers from the pulp chamber is essential for the prevention of sealer-induced discoloration. CLINICAL RELEVANCE: Tooth discoloration induced by endodontic materials is a problem for clinicians and patients and may impair the esthetic of endodontically treated teeth. Therefore, evaluation of long-term discoloration effects commonly used, and new-generation endodontic sealers were purposed in this study.
Asunto(s)
Materiales de Obturación del Conducto Radicular/efectos adversos , Corona del Diente/patología , Decoloración de Dientes/inducido químicamente , Resinas Compuestas/efectos adversos , Estética Dental , Humanos , Distribución Aleatoria , Cemento de Óxido de Zinc-Eugenol/efectos adversosRESUMEN
Crown discoloration can be induced by root canal sealer remnants following root canal treatment. Objective: The aim of this study was to evaluate chromatic alterations in human tooth crowns induced by a Mineral Trioxide Aggregate-based sealer (MTA Fillapex®) and a commonly used ZnOE-based sealer (Roth-811). The tested null hypothesis was that the application of the materials did not induce clinically perceptible crown discoloration (Ho: CIE color difference ΔE<3.7). Material and Methods: Forty five fully developed, intact, mandibular third molars were sectioned 1 mm below the cemento-enamel junction. The pulp chambers were chemomechanically debrided via the cervical access. The specimens were randomly assigned into three groups Group 1: MTA Fillapex, Group 2: Roth 811, Group 3: Negative control (unfilled) and immersed in individually marked vials containing distilled water up to the cervix (37±1°C). The spectral reflectance lines were recorded by utilizing a UV-VIS spectrophotometer equipped with integration sphere in the visual spectrum at baseline, 1 week, 1 and 3 months after material placement. Data were transformed into values of the CIE L*a*b* color system and the corresponding ΔE values were calculated. Statistical analysis was performed using two-way mixed ANOVA models, at p=0.05 level of significance. Results: A statistically significant increase in a* and b* chromatic parameters of the MTA Fillapex Group was measured. However, ΔE values did not exceed the human eye perceptibility threshold (set at ΔE<3.7) during the experimental period (ΔEt3=2.88). In Roth-811 Group, a statistically significant decrease in L* and a statistically significant increase in a* and b* chromatic parameters was measured, during all observation periods. Resultant ΔE values exceeded the human eye perceptibility threshold after 1 week (ΔEt1=5.65). Conclusions: Application of MTA Fillapex in tooth crowns resulted in minimal color alterations, while Roth 811 induced severe discoloration, in vitro. It could be suggested that, in terms of aesthetics, the use of MTA Fillapex appears to be favorable.