RESUMEN
Tissue engineering has focused on the development of biomaterials that emulate the native extracellular matrix. Therefore, the purpose of this research was oriented to the development of nanofibrillar bilayer membranes composed of polycaprolactone with low and medium molecular weight chitosan, evaluating their physicochemical and biological properties. Two-bilayer membranes were developed by an electrospinning technique considering the effect of chitosan molecular weight and parameter changes in the technique. Subsequently, the membranes were evaluated by scanning electron microscopy, Fourier transform spectroscopy, stress tests, permeability, contact angle, hemolysis evaluation, and an MTT test. From the results, it was found that changes in the electrospinning parameters and the molecular weight of chitosan influence the formation, fiber orientation, and nanoarchitecture of the membranes. Likewise, it was evidenced that a higher molecular weight of chitosan in the bilayer membranes increases the stiffness and favors polar anchor points. This increased Young's modulus, wettability, and permeability, which, in turn, influenced the reduction in the percentage of cell viability and hemolysis. It is concluded that the development of biomimetic bilayer nanofibrillar membranes modulate the physicochemical properties and improve the hemolytic behavior so they can be used as a hemocompatible biomaterial.
RESUMEN
Membranes for guided bone regeneration represent valuable resources, preventing fibroblast infiltration and aiding anatomical bone reconstruction. Nonetheless, available membranes lack bone regenerative capacity, suitable mechanical behavior, or adequate degradation profile. Therefore, to overcome these limitations, this study developed bilayer membranes with a dense layer (dry phase inversion) of PLGA (poly(lactic-co-glycolic acid)):HAp (hydroxyapatite) - 95:05 (wt%) - and an electrospun layer of PLGA and HAp:ß-TCP (ß-tricalcium phosphate) with ratios of 60:40, 70:30 and 85:15 (wt%), evaluating its mechanical, morphological and in vitro properties. The bilayer membranes displayed adequate interlayer adhesion, dense layer pore size of 4.20 µm and electrospun layer with porosity degree of 38.2%, thus capable of preventing fibroblast infiltration while allowing osteoblast migration and nutrient permeation. They also showed Tg of 82 °C and higher storage modulus, which was constant up to 54.6 °C, characteristics important for membrane implantation and use with no mechanical compromise. In vitro degradation mass loss was only 10% after 60 days, a profile suitable for the application requirement. Membranes with calcium phosphates had better osteoblast attachment, proliferation and migration. Taken together, results indicate the great potential of PLGA/HAp/ß-TCP bilayer membranes on bone reconstruction with proper degradation profile, morphology, mechanical behavior and bone regenerative capacity.