RESUMEN
All-soluble all-iron redox flow batteries (AIRFBs) are an innovative energy storage technology that offer significant financial benefits. Stable and affordable redox-active materials are essential for the commercialization of AIRFBs, yet the battery stability must be significantly improved to achieve practical value. Herein, ferrous complexes combined with the triisopropanolamine (TIPA) ligand are identified as promising anolytes to extend battery life by reducing cross-contamination due to a pronounced steric hindrance effect. The coordination structure and failure mechanism of our Fe-TIPA complexes were determined by molecular dynamics simulation and spectroscopic experiments. By coupling with [Fe(CN)6]4 -/3- , Fe-TIPA/Fe-CN AIRFBs retained excellent stability exceeding 1831 cycles at 80 mA·cm -2 , yielding an energy efficiency of ~80% and maintaining a steady discharge capacity. Moreover, the all-soluble electrolyte was tested in an industrial-scale Fe-TIPA/Fe-CN AIRFB prototype energy storage system, where an energy efficiency of 81.3% was attained. Given the abundance of iron resources, we model the TIPA AIRFB electrolyte cost to be as low as 32.37 $/kWh, which is significantly cheaper than the current commercial level. This work demonstrates that steric hindrance is an effective measure to extended battery life, facilitating the commercial development of affordable flow batteries.
RESUMEN
At present, the all-iron redox flow batteries (RFBs) have greater application potential due to high accessibility of electrolytes compared to traditional RFBs. Meanwhile, although electroactive bacteria can accelerate the electrons transfer, their potential to improve the performance of RFBs has been overlooked. Previously, we had confirmed that ferrous-oxidizing bacteria (FeOB) could enhance the performance of an all-iron RFB, therefore we conducted several batch experiments and chronopotentiometry experiments by using the ferric-reducing bacteria (FeRB) or mixed culture (FeOB and FeRB) to demonstrate whether they have the same or stronger effects on Fe3+-DTPA/Na4[Fe(CN)6] RFB. The results showed that the experimental reactors could achieve higher charging current density and initial cathodic potential during constant voltage charging process. The electrochemical impedance spectroscopy data and cyclic voltammetry curves demonstrated that the polarization impedance increased slower and reduction peak potential of experimental groups also emerged a positive shift compared to CK. According to chronopotentiometry experiments results, the microbes could function at maximum 0.3 M, 12 mA/cm2, and also improved the charging specific capacity. Combined the SEM pictures and microbial composition analysis, the main functional electroactive FeRB were Alcaligenes, Corynebacterium and Bacillus, which indicated to have important potential in improving the performance of RFBs.