We present a novel sample preparation method that allows correlative 3D X-ray Computed Nano-Tomography (CNT) and Focused Ion Beam Time-Of-Flight Secondary Ion Mass Spectrometry (FIB-TOF-SIMS) tomography to be performed on the same sample. In addition, our invention ensures that samples stay unmodified structurally and chemically between the subsequent experiments. The main principle is based on modifying the topography of the X-ray CNT experimental setup before FIB-TOF-SIMS measurements by incorporating a square washer around the sample. This affects the distribution of extraction field lines and therefore influences the trajectories of secondary ions that are now guided more efficiently towards the detector. As the result, secondary ion detection is significantly improved and higher, i.e. statistically better, signals are obtained.
RESUMEN
This paper shows how X-ray computed nanotomography (CNT) can be correlated with focused ion beam time-of-flight secondary ion mass spectrometry (FIB-TOF-SIMS) tomography on the same sample to investigate both the morphological and elemental structure. This methodology is applicable to relatively large specimens with dimensions of several tens of microns whilst maintaining a high spatial resolution of the order of 100 nm. However, combining X-ray CNT and FIB-TOF-SIMS tomography requires innovative sample preparation protocols to allow both experiments to be conducted on exactly the same sample without chemically or structurally modifying the sample between measurements. Moreover, dedicated algorithms have been developed for effective data fusion that is biased with nine degrees of freedom. This methodology has been tested using a porous and heterogeneous solid oxide fuel cell (SOFC) that has features varying in size by three orders of magnitude - from hundreds of nanometre large pores and grains to tens of micron wide functional layers.