The preparation of materials with structures composed of multiple metal cations that occupy specific sites is challenging owing to the difficulty of simultaneously addressing the incorporation of different elements at desired precise positions. We report how it is possible to use a metal-organic framework (MOF) built with a rod-shaped inorganic secondary building unit (SBU) to combine multiple metal elements at specific positions in a manner that is controllable at atomic and mesoscopic scales. Through the combination of four different metal elements at judiciously selected molar ratios, 20 MOFs of different compositions and the same topology have been prepared and characterized. The use of diffraction techniques, supported by density functional theory calculations, has led us to determine various possible atomic arrangements of the metal cations within the SBUs. In addition, seven of the compounds combine multiple types of atomic arrangements, which are mesoscopically distributed along the crystals. Given the large diversity and importance of rod-based MOFs, we believe that these findings offer a new general strategy to produce complex materials with required compositions and controllable arrangements of the metal cations for desired applications.
RESUMEN
Substitution of La(3+) by Sr(2+) in the double perovskite La(2)CoTiO(6) yields materials of the La(2-x)Sr(x)CoTiO(6) series showing a significant amount of trivalent cobalt ions when prepared at ambient atmosphere. The as-prepared compounds can be reduced in severe conditions retaining the perovskite structure while inducing the formation of a large amount of oxygen vacancies. The limit of aliovalent substitution in this series was found to extend up to x = 1. For substitution of La(3+) up to 15% cobalt and titanium are ordered, though the order is progressively lost as x increases; for x≥ 0.30 no ordering is observed as evidenced by magnetic measurements. The ability of these materials to present either cobalt ions in a mixed oxidation state or large amounts of anion vacancies depending on the atmosphere makes them interesting to be further investigated regarding their electrical and electrochemical properties, and hence, their usefulness in some electrochemical devices.