RESUMEN

BACKGROUND: The objective of this in vitro study was to evaluate the effect of the active application of self-etching ceramic primer (ME&P) on the bond strength of different dental CAD/CAM materials (Lithium Disilicate ceramic (LD), Leucite ceramic (LE), Zirconia reinforced lithium silicate ceramic (ZLS), and Hybrid ceramic (HC)) with thermocycling aging. MATERIAL AND METHODS: The samples were randomly divided into 16 groups (n = 20). Dual resin cement cylinders were made and light cured for 10 s (1.200 mW/cm2) for the shear bond strength test. 3-way ANOVA revealed that the factors were statistically significant (P< 0.05). RESULTS: The aging process had a negative impact on the bond strength for all groups except for Lithium Disilicate, with active application. ZLS and LE showed promising results with high bond strength values for the ME&P active application; however, after aging the bond strength value was significantly reduced. HC showed reduced bond strength values regardless the ME&P application. CONCLUSIONS: In order to obtain a durable bond strength, the recommended protocol of 20 s of active application followed by 40 s of sitting time in the self-etching ceramic primer should be followed when using reinforced-glass ceramics as restorative materials. Key words:Dentistry, dental materials, silane, shear strength, computer-aided design.

RESUMEN

BACKGROUND: The present review aimed to assess the impact of being a complier to supportive periodontal therapy (SPT), when compared to not being a complier, on tooth loss in patients with periodontitis. METHODS: Prospective and retrospective observational studies were included. MEDLINE, EMBASE, and LILACS databases were searched up to May 2019. The odds-ratio (OR) and standard error (SE) values of the studied groups (compliant or non-compliant) were converted to logOR, and the results of individual studies were grouped using a random effects model. RESULTS: From a total of 1815 articles initially searched, 13 retrospective studies and one prospective study comparing tooth loss of complier and non-complier individuals in SPT were included. Meta-analysis of eight studies showed that non-compliers in SPT have an increased risk of tooth loss when compared with compliers. Overall meta-analysis demonstrated that non-compliant patients in SPT have a 26% increased risk of tooth loss when compared with compliant patients (OR = 1.26; 95% CI = 1.06 to 1.51, Heterogeneity: I2 = 0%, p = 0.008). CONCLUSIONS: Patients with periodontitis who do not comply in SPT have a higher risk of tooth loss than compliant patients. Oral health professionals should implement measures to obtain optimal adherence by patients in SPT.

Asunto(s)

RESUMEN

BACKGROUND: In this study was assessed the degree of conversion (DC) of amine-free resin cements light cured through lithium disilicate-reinforced ceramics at different thicknesses and translucency. MATERIAL AND METHODS: Specimens were divided into 21 groups (n = 5) according to luting agent used: Variolink Esthetic LC (Light shade), RelyX Ultimate (A1 shade), and Filtek Z350 XT Flow (A1 shade); the ceramic translucency: low (LT) and high (HT); and the ceramic thickness: no ceramic (control), 0.5 mm, 1 mm, and 2 mm. A Teflon mold with (5 x 5 x 0.5 mm) was used to standardize the cement and over it the ceramic block from each group was placed. Set was cured using a polywave LED light (1200 mW/cm2 - Bluephase G2) for 40 s. FTIR spectra of uncured and cured materials was obtained and DC calculated from the height of the peaks 1610 and 1640 cm-1. Data were submitted to ANOVA followed by Tukey's test (α = 0.05). RESULTS: There was a significant difference for luting agents (p< 0.0001) and translucency (p = 0.025), but not for thickness (p = 0.73). Dual amine-free RelyX Ultimate showed the lowest DC values and higher translucency promoted higher DC. CONCLUSIONS: Dual amine-free cement showed the lowest monomer conversion and higher translucency ceramics promoted a higher DC. Key words:Ceramic, degree of conversion, resin cement, thickness, translucency.