RESUMEN

Lithium-ion solid-state batteries with spinel Li4Ti5O12 (LTO) electrodes have significant advantages, such as stability, long life, and good multiplication performance. In this work, the LTO electrode was obtained by the atmospheric plasma spraying method, and a composite solid electrolyte was prepared by in situ ultraviolet (UV) curing on the LTO electrode. The composite solid electrolyte was designed using a soft-hard combination strategy, and the electrolyte was prepared into a composite of a poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) flexible structure and high-conductivity Li1.3Al0.3Ti1.7(PO4)3 (LATP) hard particles. The composite electrolyte exhibited a good ionic conductivity up to 0.35 mS cm-1 at 30 °C and an electrochemical window above 4.0 V. In situ and ex situ electrolytes were assembled into LTO//electrolyte//Li solid-state batteries to investigate their impact on the electrochemical performance of the batteries. As a result, the assembled Li4Ti5O12//in situ electrolytes//Li batteries exhibited excellent rate of performance, and their capacity retention rate was 90% at 0.2 mA/cm2 after 300 cycles. This work provides a new method for the fabrication of novel advanced solid-state electrolytes and electrodes for applications in solid-state batteries.