RESUMEN

We report on the superconducting properties and intermediate resistive steps (IRS) observed in the current-voltage characteristics (IVC) of tungsten meander (MW) structures fabricated using focused ion beam (FIB) technique. Three number of MWs were studied with individual wire widths of 240 nm, 640 nm and 850 nm with superconducting transition temperatures (TC) of 4.5 K, 4.55 K and 4.60 K respectively. The measured normal state resistance values at 8 K for these wires are of ∼182 kΩ, ∼49 kΩ and ∼32 kΩ, respectively as a function of increasing wire widths; are higher than the quantum of resistance (h/4e2=6.45kΩ,his a Planck constant andeis electronic charge) indicating extreme disorder nature of the fabricated samples. The variation of resistance with respect to temperature (forT