This study focuses on the fabrication of fiber membranes containing different concentrations of AgNO3 via the electrospinning technique. The AgNO3 present in the fibers is subsequently reduced to silver nanoparticles (Ag NPs) through UV irradiation. The resulting nanofiber film is characterized using scanning electron microscopy, X-ray diffraction, and evaluations of its anti-UV and anti-electromagnetic radiation properties. Experimental results demonstrate that increasing the AgNO3 content initially decreases and then increases the fiber diameter and fiber diameter deviation. Under UV light, the nanofibers fuse and bond, leading to an increase in the fiber diameter. AgNO3 is effectively reduced to Ag NPs after UV irradiation for more than 60 min, as confirmed by the characteristic diffraction peaks of Ag NPs in the XRD spectrum of the irradiated AgNO3/PVB fibers. The nanofiber film containing AgNO3 exhibits superior anti-UV performance compared to the film containing AgNO3-derived Ag NPs. The anti-electromagnetic radiation performances of the nanofiber films containing AgNO3 and AgNO3-derived Ag NPs are similar, but the nanofiber film containing AgNO3-derived Ag NPs exhibits higher performance at approximately 2.5 GHZ frequency. Additionally, at an AgNO3 concentration of less than 0.5 wt%, the anti-electromagnetic radiation performance is poor, and the shielding effect of the nanofiber film on medium- and low-frequency electromagnetic waves surpasses that on high-frequency waves. This study provides guidance for the preparation of polyvinyl butyral nanofibers, Ag NPs, and functional materials with anti-ultraviolet and anti-electromagnetic radiation properties.
RESUMEN
To analyze the feasibility of electrospinning nanofiber yarn using a wrapping yarn forming device, electrospun nanofiber-wrapped yarns and multiscale yarns were prepared by self-made equipment. The relationship between the surface morphology and properties of yarn and its preparation process was studied. The process parameters were adjusted, and it was found that some nanofibers formed Z-twisted yarns, while others showed exposed cores. To analyze the forming mechanism of electrospun nanofiber-wrapped yarn, the concept of winding displacement difference in the twisted yarn core A was introduced. The formation of nanofiber-wrapped structural yarns was discussed using three values of A. The starting point of each twist was the same position when A = 0 with a constant corner angle ß. However, the oriented nanofiber broke or was pulled out from the gripping point when it was twisted, and it appeared disordered. The forming process of electrospun nanofiber-wrapped yarn displayed some unique phenomena, including the emission of directional nanofibers during collection, fiber non-continuity, and twist angle non-uniformity. The conclusions of this research have theoretical and practical value to guide the industrial preparation of nanofiber yarns and their wrapped yarns.