RESUMEN
Cryogenics is the science and technology of very low temperatures, typically below 120 K. The most common applications are liquified natural gas carriers, ground-based tanks, and propellant tanks for space launchers. A crucial aspect of cryogenic technology is effective insulation to minimise boil-off from storage tanks and prevent frost build-up. Rigid closed-cell foams are prominent in various applications, including cryogenic insulation, due to their balance between thermal and mechanical properties. Polyurethane (PU) foam is widely used for internal insulation in cryogenic tanks, providing durability under thermal shocks and operational loads. External insulation, used in liquified natural gas carriers and ground-based tanks, generally demands less compressive strength and can utilise lower-density foams. The evolution of cryogenic insulation materials has seen the incorporation of environmentally friendly blowing agents and bio-based polyols to enhance sustainability. Fourth-generation physical blowing agents, such as HFO-1233zd(E) and HFO-1336mzz(Z), offer low global warming potential and improved thermal conductivity. Additionally, bio-based polyols from renewable resources like different natural oils and recycled polyethylene terephthalate (PET) are being integrated into rigid PU foams, showing promising properties for cryogenic applications. Research continues to optimise these materials for better mechanical performance and environmental impact.
RESUMEN
Rigid polyurethane (PUR) foams have been the most effective insulation material used in space launchers since the beginning of cryogenic fuel use, due to their outstanding thermal and mechanical properties. In this study, spray-applied PUR foams using different ratios of amine-based catalysts were produced. Due to climate change, several restrictions have been made regarding the usage of blowing agents used for PUR foam production. Lately, hydrofluoroolefins (HFOs) have been suggested as an alternative for PUR foam production due to their low global warming potential (GWP) and ozone depletion potential (ODP), replacing the hydrofluorocarbons (HFCs) so far used. This change in blowing agents naturally altered the usage of catalysts. Reactive amine-based catalysts are less hazardous because of their low volatility and ability to react successfully with isocyanate or polyols. Spray-applied PUR foams with a potential application for cryogenic insulation were produced and tested for long-term storage, analyzing parameters such as the pH value of polyol composition, foaming kinetics (trise, tcream), etc. Athermal analysis (TG, DSC) was also applied to developed materials, as well as artificial ageing by exposing samples to UV light. It was discovered that PUR foams obtained using reactive amine-based catalysts, such as Polycat 203 and 218, have a higher integral heat capacity, but polyol mixtures containing these catalysts cannot exceed a storage time of more than 4 months. It was also observed from artificial ageing tests of PUR cryogenic insulation by exposure to UV light that the thickness of the degraded layer reached 0.8 mm (after 1000 h), but no significant destruction of cellular structure deeper in the material was observed.
RESUMEN
Rigid polyurethane (PUR) foams have outstanding properties, and some of them are successfully used even today as cryogenic insulation. The fourth-generation blowing agent Solstice® LBA and commercial polyols were used for the production of a low-density cryogenic PUR foam composition. A lab-scale pouring method for PUR foam preparation and up-scaling of the processes using an industrial spraying machine are described in this article. For the determination of the foam properties at cryogenic temperature, original methods, devices, and appliances were used. The properties at room and cryogenic temperatures of the developed PUR foams using a low-toxicity, bismuth-based, and low-emission amine catalyst were compared with a reference foam with a conventional tin-based additive amine catalyst. It was found that the values of important cryogenic characteristics such as adhesion strength after cryoshock and the safety coefficient of the PUR foams formed with new reactive-type amine-based catalysts and with the blowing agent Solstice® LBA were higher than those of the foam with conventional catalysts.