RESUMEN
Pt2Ca nanoparticles with a mean size diameter of 6 nm can be prepared by heating K2PtCl6, CaH2, carbon black and KCl at 400-500 °C. A mechanism study suggests that the formation of the Pt2Ca phase at moderate temperature is enabled by the fast ion transport via the vacancies in the KCl-CaH2 solid solution. The Pt2Ca nanoparticles exhibit high performance for the oxygen reduction reaction in acid due to optimal adsorption energy of the oxygen intermediate.
RESUMEN
As a most promising material for hydrogen generation by hydrolysis, magnesium hydride (MgH2) is also trapped by its yielded byproduct Mg(OH)2 whose dense passivated layers prevent the further contact of intimal MgH2 with water. In this work, LiH, as a destroyer, has been added to promote the hydrogen properties of MgH2. The results demonstrate that even 3 wt % LiH was added into MgH2-G, the hydrogen generation yield can increase about 72% compared to the hydrogen generation yield of MgH2-G. The possible mechanism is that Mg2+ from the hydrolysis of MgH2 preferentially bound with OH- ions from the hydrolysis of LiH to form Mg(OH)2 precipitation, which is dispersed in water rather than coated on the surface of MgH2. Moreover, adding MgCl2 into hydrolysis solution, using ball milling technology, and increasing the hydrolysis temperature can make the hydrolysis rate higher and reaction process more complete. It is noted that a too high weight ratio of LiH with too high of a hydrolysis temperature will make the reaction too violent to be safe in the experiment. We determinate the best experimental condition is that the LiH ratio added into MgH2 is 3 wt %, the hydrolysis temperature is 60 °C, and the concentration of MgCl2 hydrating solution is 1 M. MgH2-LiH composite hydrogen generation technology can meet the needs of various types of hydrogen supply and has broad application prospects.