RESUMEN
Conjugated polymer (CP)-based organic field-effect transistors (OFETs) have been considered a potential sensor platform for detecting gas molecules because they can amplify sensing signals by controlling the gate voltage. However, these sensors exhibit significantly poorer oxidizing gas sensing performance than their inorganic counterparts. This paper presents a high-performance nitric oxide (NO) OFET sensor consisting of a poly(3-hexylthiophene) (P3HT) film with an ultrathin nanoporous structure. The ultrathin nonporous structure of the P3HT film was created via deposition through the shear-coating-assisted phase separation of polymer blends and selective solvent etching. The ultrathin nonporous structure of the P3HT film enhanced NO gas diffusion, adsorption, and desorption, resulting in the ultrathin nanoporous P3HT-film-based OFET gas sensor exhibiting significantly better sensing performance than pristine P3HT-film-based OFET sensors. Additionally, upon exposure to 10 ppm NO at room temperature, the nanoporous P3HT-film-based OFET gas sensor exhibited significantly better sensing performance (i.e., responsivity ≈ 42%, sensitivity ≈ 4.7% ppm-1, limit of detection ≈ 0.5 ppm, and response/recovery times ≈ 6.6/8.0 min) than the pristine P3HT-film-based OFET sensors.
Asunto(s)
Nanoporos , Óxido Nítrico , Adsorción , Poli A , PolímerosRESUMEN
Organic field-effect transistor (OFET) gas sensors based on conjugated polymer films have recently attracted considerable attention for use in environmental monitoring applications. However, the existing devices are limited by their poor sensing performance for gas analytes. This drawback is attributed to the low charge transport in and the limited charge-analyte interaction of the conjugated polymers. Herein, we demonstrate that the incorporation of graphitic carbon nitride (g-C3N4) into the conjugated polymer matrix can improve the sensing performance of OFET gas sensors. Moreover, the effect of graphitic carbon nitride (g-C3N4) on the gas sensing properties of OFET sensors based on poly(3-hexylthiophene) (P3HT), a conjugated polymer, was systematically investigated by changing the concentration of the g-C3N4 in the P3HT/g-C3N4 composite films. The obtained films were applied in OFET to detect NO gas at room temperature. In terms of the results, first, the P3HT/g-C3N4 composite films containing 10 wt.% g-C3N4 exhibited a maximum charge carrier mobility of ~1.1 × 10-1 cm2 V-1 S-1, which was approximately five times higher than that of pristine P3HT films. The fabricated P3HT/g-C3N4 composite film based OFET sensors presented significantly enhanced NO gas sensing characteristics compared to those of the bare P3HT sensor. In particular, the sensors based on the P3HT/g-C3N4 (90/10) composite films exhibited the best sensing performance relative to that of the bare P3HT sensor when exposed to 10 ppm NO gas: responsivity = 40.6 vs. 18.1%, response time = 129 vs. 142 s, and recovery time = 148 vs. 162 s. These results demonstrate the enormous promise of g-C3N4 as a gas sensing material that can be hybridized with conjugated polymers to efficiently detect gas analytes.