RESUMEN

Graphene coating on the cobalt-chromium alloy was optimized and successfully carried out by a cold-wall chemical vapor deposition (CW-CVD) method. A uniform layer of graphene for a large area of the Co-Cr alloy (discs of 10 mm diameter) was confirmed by Raman mapping coated area and analyzing specific G and 2D bands; in particular, the intensity ratio and the number of layers were calculated. The effect of the CW-CVD process on the microstructure and the morphology of the Co-Cr surface was investigated by scanning X-ray photoelectron microscope (SPEM), atomic force microscopy (AFM), scanning electron microscopy (SEM), and energy dispersive X-ray spectroscopy (EDS). Nanoindentation and scratch tests were performed to determine mechanical properties of Co-Cr disks. The results of microbiological tests indicate that the studied Co-Cr alloys covered with a graphene layer did not show a pro-coagulant effect. The obtained results confirm the possibility of using the developed coating method in medical applications, in particular in the field of cardiovascular diseases.

Asunto(s)

RESUMEN

Cardiovascular diseases are the most distributed cause of death worldwide. Stenting of arteries as a percutaneous transluminal angioplasty procedure became a promising minimally invasive therapy based on re-opening narrowed arteries by stent insertion. In order to improve and optimize this method, many research groups are focusing on designing new or improving existent stents. Since the beginning of the stent development in 1986, starting with bare-metal stents (BMS), these devices have been continuously enhanced by applying new materials, developing stent coatings based on inorganic and organic compounds including drugs, nanoparticles or biological components such as genes and cells, as well as adapting stent designs with different fabrication technologies. Drug eluting stents (DES) have been developed to overcome the main shortcomings of BMS or coated stents. Coatings are mainly applied to control biocompatibility, degradation rate, protein adsorption, and allow adequate endothelialization in order to ensure better clinical outcome of BMS, reducing restenosis and thrombosis. As coating materials (i) organic polymers: polyurethanes, poly(ε-caprolactone), styrene-b-isobutylene-b-styrene, polyhydroxybutyrates, poly(lactide-co-glycolide), and phosphoryl choline; (ii) biological components: vascular endothelial growth factor (VEGF) and anti-CD34 antibody and (iii) inorganic coatings: noble metals, wide class of oxides, nitrides, silicide and carbide, hydroxyapatite, diamond-like carbon, and others are used. DES were developed to reduce the tissue hyperplasia and in-stent restenosis utilizing antiproliferative substances like paclitaxel, limus (siro-, zotaro-, evero-, bio-, amphi-, tacro-limus), ABT-578, tyrphostin AGL-2043, genes, etc. The innovative solutions aim at overcoming the main limitations of the stent technology, such as in-stent restenosis and stent thrombosis, while maintaining the prime requirements on biocompatibility, biodegradability, and mechanical behavior. This paper provides an overview of the existing stent types, their functionality, materials, and manufacturing conditions demonstrating the still huge potential for the development of promising stent solutions.

RESUMEN

Rapid endothelialization of cardiovascular stents is critical to prevent major clinical complications such as restenosis. Reconstruction of the native endothelium on the stent surface can be achieved by the capture of endothelial progenitor cells (EPCs) or neighboring endothelial cells (ECs) in vivo. In this study, stainless steel cardiovascular stents were functionalized with recombinant scFv antibody fragments specific for vascular endothelial growth factor receptor-2 (VEGFR2) that is expressed on EPCs and ECs. Anti-VEGFR2 scFvs were expressed in glycosylated form in Escherichia coli and covalently attached to amine-functionalized, titania-coated steel disks and stents. ScFv-coated surfaces exhibited no detectable cytotoxicity to human ECs or erythrocytes in vitro and bound 15 times more VEGFR2-positive human umbilical vein ECs than controls after as little as 3 min. Porcine coronary arteries were successfully stented with scFv-coated stents with no adverse clinical events after 30 days. Endovascular imaging and histology revealed coverage of the anti-VEGFR2 scFv-coated stent with a cell layer after 5 days and the presence of a neointima layer with a minimum thickness of 80 µm after 30 days. Biofunctionalization of cardiovascular stents with endothelial cell-capturing antibody fragments in this manner offers promise in accelerating stent endothelialization in vivo. © 2019 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 108B:213-224, 2020.

Asunto(s)

RESUMEN

Stents are important medical devices used to increase the quality and life expectancy of patients with heart diseases and stroke, leading causes of death, worldwide. In order to minimize the risk of restenosis, different coating on bare metal stents (BMS) such as polymer coatings; titanium dioxide, titanium nitride or titanium oxynitride coatings; carbon coatings and others are used. The aim of this work was to develop novel stents coated with titanium oxynitride (TiOxNy) with optimal chemical, mechanical and biological properties having possibly good coverage rate of inner and outer stent surfaces. The improvement should be achieved by optimization and development of a magnetron sputtering deposition technology. The goal of the study is understanding of the existing potential for improvement of the deposition technology and the coating quality itself. For this study, different O2/N2 ratios, meaning 1/2, 1/5 and 1/10 (the ratios of reagent gasses are given for the values of mass flows into the chamber) has been selected. Stability in simulated body fluids, surface morphology and protein adsorption as well as preliminary cytotoxic behaviour of the samples on HUVEC cells has been analysed. SEM experiments have shown the potential in the improvement of coating-stent adhesion by all samples. TiOxNy 1:5 samples were found to have the lowest adsorption, the smoothest surface morphology and the smallest rate of salt deposition from simulated body fluids (SBFs). This kind of surface has been recommended for further optimization and application.

Asunto(s)