RESUMEN

This article reports findings on screen-printed electrodes employed in microfluidic diagnostic devices. The research described includes developing a series of graphene- and other carbon form-based printing pastes compared to their rheological parameters, such as viscosity in static and shear-thinning conditions, yield stress, and shear rate required for thinning. In addition, the morphology, electrical conductivity, and electrochemical properties of the electrodes, printed with the examined pastes, were investigated. Correlation analysis was performed between all measured parameters for six electrode materials, yielding highly significant (p-value between 0.002 and 0.017) correlations between electron transfer resistance (Ret), redox peak separation, and static viscosity and thinning shear-rate threshold. The observed more electrochemically accessible surface was explained according to the fluid mechanics of heterophase suspensions. Under changing shear stress, the agglomeration enhanced by the graphene nanoplatelets' interparticle affinity led to phase separation. Less viscous pastes were thinned to a lesser degree, allowing non-permanent clusters to de-agglomerate. Thus, the breaking of temporary agglomerates yielded an unblocked electrode surface. Since the mechanism of phase ordering through agglomeration and de-agglomeration is affected by the pastes' rheology and stress during the printing process and requires no further treatment, it can be appropriately labeled as a self-assembling electrode material.

Asunto(s)

RESUMEN

Rapid growth of personal electronics with concurrent research into telerehabilitation solutions discovers opportunities to redefine the future of orthopedic rehabilitation. After joint injury or operation, convalescence includes free active range of movement exercises, such as joints bending and straightening under medical supervision. Flexion detection through wearable textile sensors provides numerous potential benefits such as: (1) reduced cost; (2) continuous monitoring; (3) remote telerehabilitation; (4) gamification; and (5) detection of risk-inducing activities in daily routine. To address this issue, novel piezoresistive multi-walled carbon nanotubes/graphite/styrene-butadiene-styrene copolymer (CNT/Gr/SBS) fiber was developed. The extrusion process allowed adjustable diameter fiber production, while being a scalable, industrially adapted method of manufacturing textile electronics. Composite fibers were highly stretchable, withstanding strains up to 285%, and exhibited exceptional piezoresistive parameters with a gauge factor of 91.64 for 0-100% strain range and 2955 for the full scope. Considering the composite's flexibility and sensitivity during a series of cyclic loading, it was concluded that developed Gr/CNT/SBS fibers were suitable for application in wearable piezoresistive sensors for telerehabilitation application.

Asunto(s)

RESUMEN

Wearable electronics are new structures with a wide range of possible applications. This study aims to analyze the effects of hot pressing in thermal transfer of different carbon-based composites as a new application method of screen-printed electronics on textiles. Flexible heaters were screen-printed on polyethylene terephthalate PET foil with composites based on graphene, carbon black, and graphite with different wt.%, measured and then hot pressed to measure and analyze differences. Research showed that the hot pressing process in thermal transfer resulted in decreased electrical resistance, increased power, and higher maximal temperatures. Best results were achieved with composites based on 12 wt.% graphene with sheet resistance lowered by about 40% and increased power by about 110%. This study shows promise for thermal transfer and screen-printing combination as an alternative for creating flexible electronics on textiles.

RESUMEN

Novel printable composites based on high aspect ratio graphene nanoplatelets (GNPs), fabricated without using solvents, and at room temperature, that can be employed for flexible, standalone conducting lines for wearable electronics are presented. The percolation threshold of examined composites was determined to be as low as 0.147 vol% content of GNPs. Obtained sheet resistance values were as low as 6.1 Ω/sq. Stretching and bending tests are presented, proving suitability of the composite for flexible applications as the composite retains its conductivity even after 180° folding and 13.5% elongation.