Co(x)Ni(1-x) alloy nanowires with varying Co content (0 ≤ x ≤ 0.95), having a diameter of 130 nm and length of around 20 µm, are synthesized by template-assisted electrodeposition into the nanopores of SiO(2) conformal coated hard-anodic aluminum oxide membranes. The magneto-structural properties of both single isolated nanowires and hexagonally ordered nanowire arrays of Co-Ni alloys are systematically studied by means of magneto-optical Kerr effect magnetometry and vibrating sample magnetometry, respectively, allowing us to compare different alloy compositions and to distinguish between the magnetostatic and magnetocrystalline contributions to the effective magnetic anisotropy for each system. The excellent tunable soft magnetic properties and magnetic bistability exhibited by low Co content Co-Ni nanowires indicate that they might become the material of choice for the development of nanostructured magnetic systems and devices as an alternative to Fe-Ni alloy based systems, being chemically more robust. Furthermore, Co contents higher than 51 at.% allow us to modify the magnetic behavior of Co-rich nanowires by developing well controlled magnetocrystalline anisotropy, which is desirable for data storage applications.
RESUMEN
The magneto-optical properties of Au-Co(x)Fe(3 - x)O(4) core-shell nanowires embedded in porous alumina membranes are studied. The structures were obtained by depositing Co(x)Fe(3 - x)O(4) on the pore walls of alumina membranes by atomic layer deposition and filling the resulting nanotube with gold by electrodeposition. The effect of plasmon resonance excitation on the magneto-optical activity is clearly observed as a modification of the spectral line shape of the Kerr rotation signal.