RESUMEN
An effective-area photovoltaic efficiency of 1.27% in power conversion, excluding the grid metal contact area and under 1 sun, AM 1.5G conditions, has been obtained for the p-GaN/i-InGaN/n-GaN diode arrays epitaxially grown on (111)-Si. The short-circuit current density is 14.96 mA/cm2 and the open-circuit voltage is 0.28 V. Enhanced light trapping acquired via multiple reflections within the strain and defect free III-nitride nanorod array structures and the short-wavelength responses boosted by the wide bandgap III-nitride constituents are believed to contribute to the observed enhancements in device performance.
RESUMEN
The carrier transport characteristics of Sb2Se2Te topological insulators were investigated, after exposure to different levels of nitrogen gas. The magnetoresistance (MR) slope for the Sb2Se2Te crystal increased by approximately 100% at 10 K after 2-days of exposure. The Shubnikov-de Haas (SdH) oscillation amplitude increased by 30% while oscillation frequencies remained the same. MR slopes and the mobilities had the same dependency on temperature over a wide temperature range. All measured data conformed to a linear correlation between MR slope and mobility, supporting our hypothesis that the MR increase and the SdH oscillation enhancement might be caused by mobility enhancement induced by adsorbed N2 molecular.
RESUMEN
In this report, ferromagnetic interactions in modulation-doped GaMnN nanorods grown on Si (111) substrate by plasma-assisted molecular beam epitaxy are investigated with the prospect of achieving a room temperature ferromagnetic semiconductor. Our results indicate the thickness of GaN layer in each GaN/MnN pair, as well as Mn-doping levels, are essential for suppressing secondary phases as well as enhancing the magnetic moment. For these optimized samples, structural analysis by high-resolution X-ray diffractometry and Raman spectroscopy verifies single-crystalline modulation-doped GaMnN nanorods with Ga sites substituted by Mn atoms. Energy dispersive X-ray spectrometry shows that the average Mn concentration can be raised from 0.4 to 1.8% by increasing Mn fluxes without formation of secondary phases resulted in a notable enhancement of the saturation magnetization as well as coercive force in these nanorods.
RESUMEN
Gallium nitride [GaN] nanorods grown on a Si(111) substrate at 720°C via plasma-assisted molecular beam epitaxy were studied by field-emission electron microscopy and cathodoluminescence [CL]. The surface topography and optical properties of the GaN nanorod cluster and single GaN nanorod were measured and discussed. The defect-related CL spectra of GaN nanorods and their dependence on temperature were investigated. The CL spectra along the length of the individual GaN nanorod were also studied. The results reveal that the 3.2-eV peak comes from the structural defect at the interface between the GaN nanorod and Si substrate. The surface state emission of the single GaN nanorod is stronger as the diameter of the GaN nanorod becomes smaller due to an increased surface-to-volume ratio.