RESUMEN
In this report, we introduce a novel idea to prepare a redox additive in a gel polymer electrolyte system of PVA-ZnSO4-H2SO4 based on zinc-carbon battery recycling. Here, zinc cans from spent zinc-carbon batteries are dissolved completely in 1 M H2SO4 to obtain a redox additive in an aqueous electrolyte of ZnSO4-H2SO4. Moreover, carbon nanoparticles and graphene nanosheets were synthesized from carbon rod and carbon powder from spent zinc-carbon batteries by only one step of washing and electrochemical exfoliation, respectively, which have good electrochemical capability. The three-electrode system using a ZnSO4-H2SO4 electrolyte with carbon nanoparticles and graphene nanosheets as working electrodes shows high electrochemical adaptability, which points out its promising application in supercapacitor devices. Thus, the symmetrical solid-state supercapacitor devices based on the sandwich structure of graphene nanosheets/PVA-ZnSO4-H2SO4/graphene nanosheets illustrated the highest energy density of 39.17 W h kg-1 at a power density of 1700 W kg-1. While symmetrical devices based on carbon nanoparticles/PVA-ZnSO4-H2SO4/carbon nanoparticles exhibited a maximum energy density of 35.65 W h kg-1 at a power density of 1700 W kg-1. Moreover, these devices illustrate strong durability after 5000 cycles, with approximately 90.2% and 73.1% remaining, respectively. These results provide a promising strategy for almost completely recycling zinc-carbon batteries, one of the most popular dry batteries.
RESUMEN
In this paper, carbon materials, including graphene nanosheets and carbon nanoparticles, were prepared from spent zinc-carbon batteries by the following two simple methods: electrochemical exfoliation and ultrasonication. Here, graphene nanosheets were synthesized by electrochemical exfoliation in 0.5 M H2SO4 by using a direct current power supply with two carbon rods from spent zinc-carbon batteries. Carbon nanoparticles were prepared by fast ultrasonication in a low-cost, green solution of DI water and ethanol. Graphene nanosheets in this study have high quality, large scale, and good electrochemical ability, while carbon nanoparticles have a unique nanosize and a good specific surface area. These carbon materials were applied for electrochemical measurements for supercapacitor studies and showed excellent stability at different temperatures. Moreover, electric double-layer capacitor devices based on graphene nanosheets and carbon nanoparticles were also used in electrochemical studies with strong stability and good electrochemical capability.