RESUMEN
In this article, the downsizing of functional Heusler alloys is discussed, focusing on the published results dealing with Heusler alloy nanowires. The theoretical information inspired the fabrication of novel nanowires that are presented in the results section of the article. Three novel nanowires were fabricated with the compositions of Ni66Fe21Ga13, Ni58Fe28In14, and Ni50Fe31Sn19. The Ni66Fe21Ga13 nanowires were fabricated, aiming to improve the stoichiometry of previous functional Ni-Fe-Ga Heusler nanomaterials with a functional behavior above room temperature. They exhibit a phase transition at the temperature of ≈375 K, which results in a magnetocaloric response of |ΔSM| ≈ 0.12 J·kg-1·K-1 at the magnetic field change of only µ0ΔH = 1 T. Novel Heusler alloy Ni58Fe28In14 nanowires, as well as Ni50Fe31Sn19 nanowires, are analyzed for the first time, and their magnetic properties are discussed, introducing a simple electrochemical approach for the fabrication of nanodimensional alloys from mutually immiscible metals.
RESUMEN
Three mechanically alloyed (MA) and spark plasma sintered (SPS) CoCrFeNiNbX (X = 5, 20, and 35 at.%) alloys with an addition of 5 at.% of SiC were investigated. The face-centered cubic (FCC) high-entropy solid solution, NbC carbides, and hexagonal Laves phase already developed during MA. In addition, the SPS compacting led to the formation of oxide particles in all alloys, and the Cr7C3 carbides in the Nb5 alloy. The fraction of the FCC solid solution decreased with increasing Nb concentration at the expense of the NbC carbide and the Laves phase. Long-term annealing at 800 °C led to the disappearance of the Cr7C3 carbide in the Nb5 alloy, and new oxides-Ni6Nb6O, Cr2O3, and CrNbO4-were formed. At laboratory temperature, the Nb5 alloy, containing only the FCC matrix and carbide particles, was relatively strong and very ductile. At a higher Nb content (Nb20 and Nb35), the alloys became brittle. After annealing for 100 h at 800 °C, the Nb5 alloy conserved its plasticity and the Nb20 and Nb35 alloys maintained or even increased their brittleness. When tested at 800 °C, the Nb5 and Nb20 alloys deformed almost identically (CYS ~450 MPa, UTS ~500 MPa, plasticity ~18%), whereas the Nb35 alloy was much stronger (CYS of 1695 MPa, UCS of 1817 MPa) and preserved comparable plasticity.
RESUMEN
Nanolayered metallic alloys are promising materials for nuclear applications thanks to their resistance to radiation damage. Here, we investigate the effect of ion (C, Si, and Cu) irradiation at room temperature with different fluences into sputtered Zr/Nb metallic multilayer films with periods 27 nm (thin) and 96 nm (thick). After irradiation, while a high strain in the entire thin nanoscale metallic multilayer (NMM) is observed, a quite small strain in the entire thick NMM is established. This difference is further analyzed by a semianalytical model, and the reasons behind it are revealed, which are also validated by local strain mapping. Both methods show that within a thick layer, two opposite distortions occur, making the overall strain small, whereas in a thin layer, all the atomic planes are affected by the interface and are subjected to only a single type of distortion (Nbâtension and Zrâcompression). In both thin and thick NMMs, with increasing damage, the strain around the interface increases, resulting in a release of the elastic energy at the interface (decrease in the lattice mismatch), and the radiation-induced transition of the Zr/Nb interfaces from incoherent to partially coherent occurs. Density functional theory simulations decipher that the inequality of point defect diffusion flux from the inner to the interface-affected region is responsible for the presence of opposite distortions within a layer. Technologically, based on this work, we estimated that Zr/Nb55 with thicknesses around Zr = 24 nm and Nb = 31 nm is the most promising multilayer system with the high radiation damage resistance and minimum swelling for nuclear applications.
RESUMEN
For the first time, the comprehensive characterization of the additively manufactured AlSi9Cu3Fe alloy is reported in this paper. Conventionally, the AlSi9Cu3(Fe) alloy is prepared by high-pressure die casting (HPDC), but this technology largely does not offer such opportunities as additive manufacturing (AM) does, especially in the design of new lightweight parts. In the present paper, testing samples were prepared by selective laser melting (SLM), one of the AM technologies, and characterized in terms of their microstructure (by means of light microscopy, scanning electron microscopy and transmission electron microscopy in combination with analytical techniques for evaluation of chemical and phase composition) and mechanical properties (static tension, compression, and hardness). All the characteristics were compared with the HPDC reference material. Our study showed an excellent improvement both in strength (374 ± 11 MPa compared to 257 ± 17 MPa) and plasticity (1.9 ± 0.2% compared to 1.2 ± 0.5%) of the material thanks to its very fine and distinctive microstructure.