RESUMEN
The increase in greenhouse gas emissions has led to seawater acidification, increasing the corrosion rate of metal structures in marine applications. This paper indicates that the spraying of four types of coatings, namely Zn, Al, Zn-Al, and Al-Mg, using the arc-spraying technique on steel substrate S235JR, creates effective protective coatings that interact differently with various pH solutions exposed to varying levels of seawater acidification. The study analyses the structural properties of the coating materials using SEM and XRD techniques. Electrochemical parameters are evaluated in solutions with different pH and salinity levels. The results demonstrate that alloy metallic coatings provide excellent resistance to corrosion in low-pH solutions.
RESUMEN
The present paper presents a study of the behaviour of Fe3Al intermetallic powders particles based on 86Fe-14Al, 86Fe-14(Fe5Mg), and 60.8Fe-39.2(Ti37.5Al) compositions obtained by mechanochemical synthesis at successive stages of the plasma spraying process: during transfer in the volume of the gas stream and deformation at the moment of impact on the substrate. The effect of the change in current on the size of powder particles during their transfer through the high-temperature stream and the degree of particle deformation upon impact with the substrate was determined. It was found that during transfer through the plasma jet, there was an increase in the average size of sputtering products by two-three times compared to the initial effects of mechanochemical synthesis due to the coagulation of some particles. In this case, an increase in current from 400 to 500 A led to a growth in average particle size by 14-47% due to the partial evaporation of fine particles with an increase in their heating degree. An increase in current also led to a 5-10% growth in particle deformation degree upon impact on the substrate due to the rising temperature and velocity of the plasma jet. Based on the research, the parameters of plasma spraying of mechanically synthesized Fe3Al intermetallic-based powders were determined, at which dense coatings with a thin-lamellar structure were formed.