RESUMEN
We report the results of a detailed examination of the occlusion of silver nitrate in silver zeolite A (AgA). The superlattice reported to occur in (AgNO3)9-AgA was found to melt at between 80 and 100 degrees C on heating and reappear when the sample was cooled down to 80 degrees C. Annealing in this temperature range and rigorous exclusion of water produced an enhancement of the superlattice peaks, which results from ordering of the contents of the zeolite cages. Peaks assigned to the superlattice were indexed with the tetragonal lattice parameters a = 17.440(5) and c = 12.398(4) A and proposed space group P4/nmm. The sharp peaks representing the lattice of the framework (a = 12.3711(5) A, Pm3m) remained largely unaffected by the guest in this compound, which was found to exhibit strong negative thermal expansion. The host and guest lattices are incommensurate with the tetragonal guest lattice being slightly larger than the cubic host in the c-direction and slightly smaller in the a- and b-directions.
RESUMEN
The effects of pH on the calcium phosphate phase, of Tris and of amino acids, such as aspartic acid, glutamic acid, and serine on hydroxyapatite formation and morphology, were studied in double diffusion experiments. In this system, hydroxyapatite was only formed when the pH was around 7.4 or higher for the duration of the reaction. A decrease in pH resulted in the transformation of hydroxyapatite to octacalcium phosphate. Amino acids and Tris or the buffering capacity of Tris have an effect on the morphology of the synthetic hydroxyapatite. The presence of the additive results in spheres consisting of needles, blades or plates depending on the reaction system.