RESUMEN
The change in the corrosion activities of SS304 and the carbon steel A36 were studied during their exposure for 30 days to hybrid pumice-Portland cement extract (CE), to simulate the concrete-pore environment. The ionic composition and the initial pH (12.99) of the CE were influenced by the reduction of Portland cement (PC) content, volcanic pumice oxides and alkaline activators. Because of the air CO2 dissolution, the pH decreased and maintained a constant value ≈ 9.10 (established dynamic ionic equilibrium). The CE promoted the passivation of both steels and their free corrosion potential (OCP) reached positive values. On the surfaces, Fe and Cr oxides were formed, according to the nature of the steel. Over the time of exposure, the presence of chloride ions in the pumice caused a localized pitting attack, and for carbon steel, this fact may indicate an intermediate risk of corrosion. The chloride effect was retarded by the accumulation of SO42- ions at the steel surfaces. Based on electrochemical impedance (EIS), the polarization resistance (Rp) and the thickness of the passive layers were calculated. Their values were compared with those previously reported for the steels exposed to CEs of Portland and supersulfated cements, and the hybrid cement was considered as a PC "green" alternative.
RESUMEN
Stainless steel SS430 and carbon steel B450C were exposed for 30 days to the aqueous extract of sodium silicate-modified limestone-Portland cement as an alternative for the partial replacement of the Portland cement clinker. The initial pH of 12.60 was lowered and maintained at an average of 9.60, associated with air CO2 dissolution and acidification. As a result, the carbon steel lost its passive state, and the corrosion potential (OCP) reached a negative value of up to 296 mV, forming the corrosion layer of FeO, and FeOOH. In the meaning time, on the stainless steel SS430 surface, a passive layer of Cr2O3 grew in the presence of FeO, Fe2O3 and Cr(OH)3 corrosion products; thus, the OCP shifted to more positive values of +150 mV. It is suggested that a self-repassivation process took place on the SS430 surface due to the accumulation of alkaline sulfates on the interface. Because of the chloride attack, SS430 presented isolated pits, while on B450C, their area was extended. The quantitative analysis of EIS Nyquist and Bode diagrams revealed that the Rp of the corrosion process for SS430 was 2500 kΩcm2, ≈32 times lower in magnitude than on B450C, for which the passive layer tended to disappear, while that on SS430 was ≈0.82 nm.
RESUMEN
Carbon steel B450C and low-chromium stainless steel SS430 were exposed for 30 days to supersulfated "SS1" cement extract solution, considered as a "green" alternative for partial replacement of the Portland cement clinker. The initial pH of 12.38 dropped since the first day to 7.84, accompanied by a displacement to more negative values of the free corrosion potential (OCP) of the carbon steel up to ≈-480.74 mV, giving the formation of γ-FeOOH, α-FeOOH and Fe2O3, as suggested by XRD and XPS analysis. In the meantime, the OCP of the SS430 tended towards more positive values (+182.50 mV), although at lower pH, and XPS analysis revealed the presence of Cr(OH)3 and FeO as corrosion products, as well the crystals of CaCO3, NaCl and KCl. On both surfaces, a localized corrosion attack was observed in the vicinity of local cathodes (Cu, Mn-carbides, Cr-nitrides, among others), influenced by the presence of Cl- ions in the "SS1" extract solution, originating from the pumice. Two equivalent circuits were proposed for the quantitative analysis of EIS Nyquist and Bode diagrams, whose data were correlated with the OCP values and pH change in time of the "SS1" extract solution. The thickness of the corrosion layer formed on the SS430 surface was ≈0.8 nm, while that on the B450C layer was ≈0.3 nm.