RESUMEN
This study aims to optimize the performance of CrN coatings deposited on WC cutting tools for machining Ti6Al4V alloy, where the formation of built-up edge (BUE) is a prevalent and critical issue. In-house CrN coatings were developed using the PVD (Physical Vapor Deposition) process, with variations in deposition parameters including nitrogen gas pressure, bias voltage, and coating thickness. A comprehensive experimental approach encompassing deposition, characterization, and machining performance evaluation was employed to identify the optimal deposition conditions. The results indicated that CrN coatings deposited at a nitrogen gas pressure of 4 Pa, a bias voltage of -50 V, and a thickness of 1.81 µm exhibited superior performance, significantly reducing BUE formation and tool wear. These optimized coatings demonstrated enhanced properties, such as a higher elastic modulus and a lower coefficient of friction, which contributed to improved tool life and machining performance. Comparative studies with commercial CrN coatings revealed that the in-house developed coatings outperformed the commercial variants by approximately 65% in tool life, owing to their superior mechanical properties and reduced friction. This research highlights the potential of tailored CrN coatings for advanced machining applications and emphasizes the importance of optimizing deposition parameters to achieve high-performance tool coatings.
RESUMEN
The machining of Ti6Al4V alloy, especially at low cutting speeds, is associated with strong Built-Up Edge (BUE) formation. The PVD coatings applied on cutting tools to machine such materials must have the necessary combination of properties to address such an underlying wear mechanism. The present work investigates and shows that TiB2 PVD coating can be designed to have certain mechanical properties and tribological characteristics that improve machining in cases where BUE formation is observed. Three TiB2 coatings were studied: one low hardness coating and two high hardness coatings with varied coating thicknesses. Wear performances for the various TiB2 coated carbide tools were evaluated while rough turning Ti6Al4V. Tool wear characteristics were evaluated using tool life studies and the 3D wear volume measurements of the worn surface. Chip morphology analyses were done to assess the in-situ tribological performance of the coatings. The micro-mechanical properties of the coatings were also studied in detail to co-relate with the coatings' performances. The results obtained show that during the rough turning of Ti6Al4V alloy with intensive BUE formation, the harder TiB2 coatings performed worse, with coating delamination on the rake surface under operation, whereas the softer version of the coating exhibited significantly better tool life without significant coating failure.
RESUMEN
During machining of stainless steels at low cutting -speeds, workpiece material tends to adhere to the cutting tool at the tool-chip interface, forming built-up edge (BUE). BUE has a great importance in machining processes; it can significantly modify the phenomenon in the cutting zone, directly affecting the workpiece surface integrity, cutting tool forces, and chip formation. The American Iron and Steel Institute (AISI) 304 stainless steel has a high tendency to form an unstable BUE, leading to deterioration of the surface quality. Therefore, it is necessary to understand the nature of the surface integrity induced during machining operations. Although many reports have been published on the effect of tool wear during machining of AISI 304 stainless steel on surface integrity, studies on the influence of the BUE phenomenon in the stable state of wear have not been investigated so far. The main goal of the present work is to investigate the close link between the BUE formation, surface integrity and cutting forces in the stable sate of wear for uncoated cutting tool during the cutting tests of AISI 304 stainless steel. The cutting parameters were chosen to induce BUE formation during machining. X-ray diffraction (XRD) method was used for measuring superficial residual stresses of the machined surface through the stable state of wear in the cutting and feed directions. In addition, surface roughness of the machined surface was investigated using the Alicona microscope and Scanning Electron Microscopy (SEM) was used to reveal the surface distortions created during the cutting process, combined with chip undersurface analyses. The investigated BUE formation during the stable state of wear showed that the BUE can cause a significant improvement in the surface integrity and cutting forces. Moreover, it can be used to compensate for tool wear through changing the tool geometry, leading to the protection of the cutting tool from wear.