RESUMEN

PURPOSE: The objective of this study was to determine the effect of the color of a background substructure on the overall color of a zirconia-based all-ceramic crown. MATERIALS AND METHODS: Twenty one posterior zirconia crowns were made for twenty subjects. Seven premolar crowns and six molar crowns were cemented onto abutments with metal post and core in the first and second group. In the third group, eight molar crowns were cemented onto abutments with a prefabricated post and composite core build-up. The color measurements of all-ceramic crowns were made before try-in, before and after cementation. A repeated measure ANOVA was used for a statistical analysis of a color change of all-ceramic crowns at α=.05. Twenty four zirconia specimens, with different core thicknesses (0.4-1 mm) were also prepared to obtain the contrast ratio of zirconia materials after veneering. RESULTS: L(*) , a(*) , and b(*) values of all-ceramic crowns cemented either on a metal cast post and core or on a prefabricated post did not show significant changes (P>.05). However, the slight color changes of zirconia crowns were detected and represented by ΔE(*) ab values, ranging from 1.2 to 3.1. The contrast ratios of zirconia specimens were 0.92-0.95 after veneering. CONCLUSION: No significant differences were observed between the L(*) , a(*) , and b(*) values of zirconia crowns cemented either on a metal cast post and core or a prefabricated post and composite core. However, the color of a background substructure could affect the overall color of posterior zirconia restorations with clinically recommended core thickness according to ΔE(*) ab values.

RESUMEN

PURPOSE: Zirconia has been used in clinical dentistry for approximately a decade, and there have been several reports regarding the clinical performance and survival rates of zirconia-based restorations. The aim of this article was to review the literatures published from 2000 to 2010 regarding the clinical performance and the causes of failure of zirconia fixed partial dentures (FPDs). MATERIALS AND METHODS: An electronic search of English peer-reviewed dental literatures was performed through PubMed to obtain all the clinical studies focused on the performance of the zirconia FPDs. The electronic search was supplemented by manual searching through the references of the selected articles for possible inclusion of some articles. Randomized controlled clinical trials, longitudinal prospective and retrospective cohort studies were the focuses of this review. Articles that did not focus on the restoration of teeth using zirconia-based restorations were excluded from this review. RESULTS: There have been three studies for the study of zirconia single crowns. The clinical outcome was satisfactory (acceptable) according to the CDA evaluation. There have been 14 studies for the study of zirconia FPDs. The survival rates of zirconia anterior and posterior FPDs ranged between 73.9% - 100% after 2 - 5 years. The causes of failure were veneer fracture, ceramic core fracture, abutment tooth fracture, secondary caries, and restoration dislodgment. CONCLUSION: The overall performance of zirconia FPDs was satisfactory according to either USPHS criteria or CDA evaluations. Fracture resistance of core and veneering ceramics, bonding between core and veneering materials, and marginal discrepancy of zirconia-based restorations were discussed as the causes of failure. Because of its repeated occurrence in many studies, future researches are essentially required to clarify this problem and to reduce the fracture incident.

RESUMEN

OBJECTIVES: The objectives of this study were to characterize the clinical performance and wear characteristics of lithia-disilicate-based ceramic crowns. METHODS: Thirty posterior crowns were made using the heat-pressing technique and lithia-disilicate-based core ceramic. Subjects were recalled annually. The quality of crowns and adjacent gingival tissues were examined using nine criteria for acceptability. All crowns were examined and ranked from 4 (Excellent) to 1 (Unacceptable) for each criterion. Impressions were made for replica models at each appointment. Wear characteristics of dental ceramic and enamel were obtained by comparing the surface of the original model with the follow-up model using a laser scanner. RESULTS: Twenty-nine subjects returned for the 1-year recall examination. The maximum clenching force for the 30 subjects ranged from 125 to 815 N. All clinical criteria were ranked good to excellent at the 1-year recall exam and no fractures were observed. The mean occlusal wear volumes for the ceramic crowns after 1 year were 0.19 (0.065)mm3 for premolar sites and 0.34 (0.08)mm3 for molar sites. The mean occlusal wear volumes of opposing enamel after 1 year were 0.21 (0.06)mm3 for premolar teeth and 0.50 (0.22)mm3 for molar teeth. The mean occlusal wear volume of ceramic molar crowns was significantly lower than the volume of enamel wear of the opposing teeth (p

Asunto(s)

Coronas , Porcelana Dental/química , Alisadura de la Restauración Dental , Coronas con Frente Estético , Adulto , Diente Premolar/patología , Fuerza de la Mordida , Coronas/normas , Esmalte Dental/patología , Diseño de Prótesis Dental , Femenino , Estudios de Seguimiento , Encía/patología , Humanos , Masculino , Microscopía Confocal , Persona de Mediana Edad , Diente Molar/patología , Técnica de Perno Muñón , Técnicas de Réplica , Atrición Dental/patología