RESUMEN
Fiber-reinforced plywood is a composite material that combines the natural strength and rigidity of plywood with the added durability and resilience provided by reinforcing fibers. This type of plywood is designed to offer improved characteristics over standard plywood, including enhanced strength, stiffness, resistance to impact and moisture, and environmental degradation. By integrating reinforcing fibers, such as glass, carbon, or natural fibers (like flax, bamboo, or hemp) into or onto plywood, manufacturers can create a material that is better suited for applications where traditional plywood might fall short or when a decrease in product weight or savings in wood raw material are necessary. This report reviews the current progress in fiber-reinforced plywood in the context of plywood as a construction material to better understand the potential gains in plywood applications, mechanical parameters, and material savings. It is found that a simple and cost-effective procedure of fiber reinforcement allows for substantial improvements in plywood's mechanical properties, typically to the extent of 10-40%. It is suggested that the wider adoption of fiber-reinforced plywood, especially in load- and impact-bearing applications, would greatly contribute to enhanced durability and longevity of the material while also allowing for more sustainable use of raw wood material.
RESUMEN
The reinforcement of plywood is demonstrated by laminating pretensioned basalt fibers between veneer sheets, to fabricate so-called prestressed plywood. Belt type basalt fibers bearing a specific adhesion promoting silane sizing were aligned between veneer sheets with 20 mm spacing and were pretensioned at 150 N. Three-layer plywood samples were prepared and tested for tensile strength at room temperature and at 150 °C. The room temperature tensile tests revealed a 35% increase in tensile strength for prestressed plywood compared to that of the conventional specimen. The reinforcement effect deteriorated at 150 °C but was restored upon cooling to room temperature. The deterioration is attributed to the weakening of bonding between the basalt fibers and phenolic resin matrix at elevated temperatures due to the softening of the resin.